Optimization experiment of sinter basicity on low-grade complex ore |
WU Qiang1,ZHU Zi-zong1,ZENG Jian-hua1,XIONG Hao1,MENG Xian-tao2,ZHANG Shi-qiao2 |
1. College of Material Science and Engineering, Chongqing University, Chongqing 400044, China 2. Xinxing Ductle Iron Pipes Xinjiang Co., Ltd., Hejing 841300, Xinjiang, China |
|
|
Abstract In order to utilize the lean ore resources in Xinjiang rationally and optimize the?blast furnace charge structure, the optimizing experiments on sinter basicity were carried out. In view of the complex ore in Xinjiang,Seven groups of sintering pot tests were conducted. The basicity of all these tests changed among 1.65 and 2.00. Through analyzing the mechanical strength, metallurgical properties and mineral composition of sinter, it is concluded that when the alkalinity was between 1.80 to 1.85, an obvious increase of the SFCA content in sinter can be observed, the ISO drum strength of sinter was comparatively high and the yield can be as high as 78%, the reducibility and low temperature reduction desintegration index of sinter were also improved, and the soft melting range was the narrowest. So it is the optimal basicity range of sinter. However, when the basicity was among 1.65 and 1.75, the drum index declined and the property of molten drop became worse. It is the pulverization basicity interval of sinter, therefore considering the complexity of ore in Xinjiang area, this range should be avoided in sintering production.
|
Received: 06 January 2015
Published: 06 January 2016
|
|
|
|
|
[1] |
蒋大军,何木光,甘 勤,等. 高碱度对烧结矿性能与工艺参数的影响[J]. 钢铁,2009,44(2):99.
|
[1] |
蒋大军,何木光,甘 勤,等. 高碱度对烧结矿性能与工艺参数的影响[J]. 钢铁,2009,44(2):99.
|
[2] |
于素荣,周节旺,于淑娟,等. 碱度对鞍钢烧结矿产、质量的影响[J]. 烧结球团,2007,32(5):18.
|
[2] |
于素荣,周节旺,于淑娟,等. 碱度对鞍钢烧结矿产、质量的影响[J]. 烧结球团,2007,32(5):18.
|
[3] |
朱贺民. 烧结矿碱度、SiO2和MgO含量对烧结冶金性能的影响[J]. 钢铁研究,2006,34(4):17.
|
[3] |
朱贺民. 烧结矿碱度、SiO2和MgO含量对烧结冶金性能的影响[J]. 钢铁研究,2006,34(4):17.
|
[4] |
刘竹林,李永清,高泽平. 炼铁原料[M]. 北京:化学工业出版社,2007:145.
|
[4] |
刘竹林,李永清,高泽平. 炼铁原料[M]. 北京:化学工业出版社,2007:145.
|
[5] |
武 轶,金 俊,熊德怀. 低碱度高镁烧结矿性能的研究[J]. 钢铁研究,2013,41(3):9-10.
|
[5] |
武 轶,金 俊,熊德怀. 低碱度高镁烧结矿性能的研究[J]. 钢铁研究,2013,41(3):9-10.
|
[6] |
A. A. Panychev and D. R Ganin. Optimizing the MgO content of the charge in sintering and blast- furnace smelting [J]. Metallurgist,2012,55(5):876.
|
[6] |
A. A. Panychev and D. R Ganin. Optimizing the MgO content of the charge in sintering and blast- furnace smelting [J]. Metallurgist,2012,55(5):876.
|
[7] |
王海涛,李光辉,范晓慧,等. 几种高炉炉料冶金性能的对比研究[J]. 钢铁,2006,41 (1) :27.
|
[7] |
王海涛,李光辉,范晓慧,等. 几种高炉炉料冶金性能的对比研究[J]. 钢铁,2006,41 (1) :27.
|
[1] |
DU Liang, HAN Xiu-li, ZHANG Quan-sheng, ZHOU Xiang, YANG Hong-da, WANG Ying. Quantitative relation between mineralogical structure and metallurgical properties of sinter of import iron ore[J]. Iron and Steel, 2020, 55(6): 38-45. |
[2] |
SUN Jun-jie, ZHANG Yong-jie, XU Ji. Segregation of sinter particles in sinter shaft cooler[J]. Iron and Steel, 2020, 55(3): 16-22. |
[3] |
JIANG Da-jun. Influence of fuel structure on sintering character and comprehensive effect[J]. Iron and Steel, 2020, 55(2): 31-41. |
[4] |
HU Chang-qing,WANG Xiao-lei,SHI Xue-feng,WANG Zhi-xing,HAN Wei-gang. Effect of alkalinity and MgO content on mineral composition and microstructure of FeOx-SiO2-CaO-MgO-Al2O3 system[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 103-110. |
[5] |
NIU Lele,LIU Zhengjian,ZHANG Jianliang,ZHANG Zongwang, WANG Yaozu,DU Chengbo. Effect of mineral composition of iron ore on metallurgical properties of sinter[J]. Iron and Steel, 2019, 54(9): 27-32. |
[6] |
LIU Zhe,WANG Yi-ci,ZHAO Feng-guang,LUO Guo-ping,ZHAO Bin. Influence of binary basicity on physical properties of blast furnace slag of Baogang Group[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 696-701. |
|
|
|
|