碳热还原转炉渣脱磷的试验

doi:10.13228/j.boyuan.issn0449-749x.20150311

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (0 KB) HTML (0 KB)
Export: BibTeX | EndNote (RIS)

Abstract The thermodynamic analysis of dephosphorization of BOF slag by carbothermal reduction was studied， and many experimental studies were carried out in the molybdenum disilicide high-temperature heat treatment resistance furnace and the 500 kg top and bottom combined blowing multifunctional furnace. The results indicated that reaction temperature and dynamic condition had significant effects on the dephosphorzition rate. In the high temperature heat treatment resistance furnace， 1 500 ℃ reaction temperature can be guaranteed and about 30% dephosphorzition rate can be reached under the condition of carbon equivalent 3.0 and 30 min holding time. In the top and bottom combined blowing multifunctional furnace， coke powder can be used as reduction material and heating-up material. Dephosphorization reaction processing under the high temperature can be guaranteed by the exothermal reaction between coke powder and oxygen. Meanwhile， the top-blowing oxygen agitated the molten slag layer， which benefit to increasing the dephosphorization rate more， dephosphorization rate reached 84% in the whole process， thereinto， dephosphorization rate in the molten pool was 75.85%， dephosphorization rate of evapouration was 8.15%. 10.8% sulphur carried by coke powder entered the molten steel and 6.25% entered the molten slag.

Received: 03 July 2015 Published: 26 April 2016

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	DIAO Cheng-Lin
	ZHANG Ning
	KANG Lei
	CAO Dong
	LI An-Bang

Cite this article:

DIAO Cheng-Lin,ZHANG Ning,KANG Lei等. Experiments on dephosphorization of BOF slag by carbothermal reduction[J]. Iron and Steel, 2016, 51(5): 41-44.

URL:

http://www.chinamet.cn/Jweb_gt/EN/10.13228/j.boyuan.issn0449-749x.20150311 OR http://www.chinamet.cn/Jweb_gt/EN/Y2016/V51/I5/41

[1]	李光强，张峰，张力，等.高温碳热还原进行转炉渣资源化的研究[J].材料与冶金学报，2003，2(3)：167-172.(LI Guang-qiang, ZHANG Feng, ZHANG Li. Recycle of Converter Slag by High Temperature Carbon Thermal Reduction[J]. Journal of Materials and Metallurgy, 2003, 2(3):167-172.)
[1]	李光强，张峰，张力，等.高温碳热还原进行转炉渣资源化的研究[J].材料与冶金学报，2003，2(3)：167-172.(LI Guang-qiang, ZHANG Feng, ZHANG Li. Recycle of Converter Slag by High Temperature Carbon Thermal Reduction[J]. Journal of Materials and Metallurgy, 2003, 2(3):167-172.)
[2]	李光辉，邬斌，张元波，等.转炉钢渣工艺矿物学及其综合利用技术[J].中南大学学报，2010，41(6)：2065-2071.(LI Guang-hui, WU Bin, ZHANG Yuan-bo. Mineralogical characteristics and comprehensive utilization of converter steel slag[J]. Journal of Central South University, 2010, 41(6): 2065-2071.)
[2]	李光辉，邬斌，张元波，等.转炉钢渣工艺矿物学及其综合利用技术[J].中南大学学报，2010，41(6)：2065-2071.(LI Guang-hui, WU Bin, ZHANG Yuan-bo. Mineralogical characteristics and comprehensive utilization of converter steel slag[J]. Journal of Central South University, 2010, 41(6): 2065-2071.)
[3]	吴明.转炉冶炼低碳钢留渣操作的生产实践[J].炼钢，2009，25(2)：16-18. (WU Ming. Low carbon steel production with BOF slag-remaining practice[J]. Steelmaking, 2009, 25(2): 16-18.)
[3]	吴明.转炉冶炼低碳钢留渣操作的生产实践[J].炼钢，2009，25(2)：16-18. (WU Ming. Low carbon steel production with BOF slag-remaining practice[J]. Steelmaking, 2009, 25(2): 16-18.)
[4]	武轶，金俊，夏征宇.配用转炉渣烧结生产实践[J].钢铁研究，2010，38(2)：21-23. (WU Yi, JIN Jun, XIA Zheng-yu. Sintering Production by proportioning of converter slag[J]. Research on iron and steel, 2010, 38(2): 21-23.)
[4]	武轶，金俊，夏征宇.配用转炉渣烧结生产实践[J].钢铁研究，2010，38(2)：21-23. (WU Yi, JIN Jun, XIA Zheng-yu. Sintering Production by proportioning of converter slag[J]. Research on iron and steel, 2010, 38(2): 21-23.)
[5]	吕岩，张锰，陈津，等.钢渣在微波场中还原脱磷的工艺[J].河北理工大学学报，2010，32(3)：38-42. (LV Yan, ZHANG Meng, CHEN Jin. Technologic Research of on Dephosphorization of converter slag bu microwave heating[J]. Journal of Hebei Polytechnic University, 2010, 32(3): 38-42.)
[5]	吕岩，张锰，陈津，等.钢渣在微波场中还原脱磷的工艺[J].河北理工大学学报，2010，32(3)：38-42. (LV Yan, ZHANG Meng, CHEN Jin. Technologic Research of on Dephosphorization of converter slag bu microwave heating[J]. Journal of Hebei Polytechnic University, 2010, 32(3): 38-42.)
[6]	艾立群，周朝刚，吕岩，等.微波加热钢渣脱磷的升温特性[J].钢铁钒钛，2011，32(2)：29-32.(AI Li-qun, ZHOU Chao-gang, LV Yan. Temperature Characteristics of Dephosphorization of Steelmaking Slag in Microwave Heating Process[J]. Iron steel vanadium titanium, 2011, 32(2): 29-32.)
[6]	艾立群，周朝刚，吕岩，等.微波加热钢渣脱磷的升温特性[J].钢铁钒钛，2011，32(2)：29-32.(AI Li-qun, ZHOU Chao-gang, LV Yan. Temperature Characteristics of Dephosphorization of Steelmaking Slag in Microwave Heating Process[J]. Iron steel vanadium titanium, 2011, 32(2): 29-32.)
[7]	王书桓，吴艳青，刘新生，等.硅还原转炉熔渣气化脱磷实验研究[J].钢铁，2008，43(2)：31-34.(WANG Shu-huan, WU Yan-qing, LIU Xin-sheng. Experimental Study on Gasification Dephosphorization of Converter Slag With Reduction by Silicon[J]. Iron and steel, 2008, 43(2): 31-34.)
[7]	王书桓，吴艳青，刘新生，等.硅还原转炉熔渣气化脱磷实验研究[J].钢铁，2008，43(2)：31-34.(WANG Shu-huan, WU Yan-qing, LIU Xin-sheng. Experimental Study on Gasification Dephosphorization of Converter Slag With Reduction by Silicon[J]. Iron and steel, 2008, 43(2): 31-34.)
[8]	邓志豪，王钰，周云.转炉渣系矿物相研究[J].安徽工业大学学报，2011，28(3)：201-204.(DENG Zhi-hao, WANG Yu, ZHOU Yun. Study on the Mineral Phase of the Converter Slag System[J]. Journal of Anhui University of Technology, 2011, 28(3): 201-204.)
[8]	邓志豪，王钰，周云.转炉渣系矿物相研究[J].安徽工业大学学报，2011，28(3)：201-204.(DENG Zhi-hao, WANG Yu, ZHOU Yun. Study on the Mineral Phase of the Converter Slag System[J]. Journal of Anhui University of Technology, 2011, 28(3): 201-204.)
[9]	梁连科，车荫昌，杨怀，等.冶金热力学及动力学[M].沈阳：东北工学院出版社，1990:120. (Liang Lian-ke, Che Meng-chang, Yang huai, et a1. Metallurgic thermodynamics and kinetics[M]. Shenyang: Northeastern engineering college press , 1990:120.)
[10]	郑常乐，张建良，肖洪，等.唐钢3200m3高炉喷煤有效热的研究[J].钢铁，2013，48(10)：76-81.(ZHENG Chang-le, ZHANG Jian-liang, XIAO Hong. Research on 3200m3 BF,s PCI Effective Calorific Value of Tangshan Iron and Steel[J]. Iron and Steel, 2013, 48(10): 76-81)
[9]	梁连科，车荫昌，杨怀，等.冶金热力学及动力学[M].沈阳：东北工学院出版社，1990:120. (Liang Lian-ke, Che Meng-chang, Yang huai, et a1. Metallurgic thermodynamics and kinetics[M]. Shenyang: Northeastern engineering college press , 1990:120.)
[10]	郑常乐，张建良，肖洪，等.唐钢3200m3高炉喷煤有效热的研究[J].钢铁，2013，48(10)：76-81.(ZHENG Chang-le, ZHANG Jian-liang, XIAO Hong. Research on 3200m3 BF,s PCI Effective Calorific Value of Tangshan Iron and Steel[J]. Iron and Steel, 2013, 48(10): 76-81)