Roasting mechanism of pellet made from PMC and Sijiaying |
Lü Qing1,TIAN Ye1,LIU Xiao-jie1,QIE Ya-na1,LI Jian-peng1,HUANG Hong-hu2 |
(1. College of Metallurgy and Energy,North China University of Science and Technology, Tangshan 063009,Hebei,China 2. Steelmaking Department,Handan Xinxing Ductile Iron Pipes Co.,Ltd., Handan 056300,Hebei,China) |
|
|
Abstract The effects of pre-heating temperature, pre-heating time, roasting temperature and roasting time on consolidation properties of the pellet were studied to utilize PMC. The pellet was composed of PMC and the PMC mineral to Sijiaying mineral powder was 7[∶]3. Results show that, when the preheating time is 10 min, the roasting time is 20 min, and the roasting temperature is 1 275 ℃, the compression strength of the pellet increases firstly and then decreases with the increase of pre-heating temperature. When the pre-heating temperature is 925 ℃, the compression strength of the pellet reaches the maximum, which is 2 765.75 N/per. When the pre-heating temperature is 925 ℃, the roasting time is 20 min and the roasting temperature is 1 275 ℃, the compression strength of the pellet increases from 2 646 N/per to 2 833.61N/per with the increase of pre-heating time. When the preheating time is 15 min, the roasting time is 10 min and the pre-heating temperature is 925 ℃, the compression strength of the pellet increases from 674.96 N/per to 2 503.83 N/per with the increase of roasting temperature. When the preheating time is 15 min, the pre-heating temperature is 925 ℃ and the roasting temperature is 1 300 ℃, the compression strength of the pellet increases from 2 503.83 N/per to 2 872.52 N/per with the increase of roasting time.
|
Received: 13 January 2016
Published: 26 July 2016
|
|
|
|
[1] |
孔令坛.中国炼铁原料技术的科技进步和展望[J].中国冶金,2003, (4):1-4.[J].中国炼铁原料技术的科技进步和展望, 2003, (4):1-4
|
[1] |
孔令坛.中国炼铁原料技术的科技进步和展望[J].中国冶金,2003, (4):1-4.[J].中国炼铁原料技术的科技进步和展望, 2003, (4):1-4
|
[2] |
亢立明,吕庆,孙丽芬,刘曙光.冀东磁铁精粉球团矿焙烧机理的研究. 钢铁研究,2008,1
|
[2] |
亢立明,吕庆,孙丽芬,刘曙光.冀东磁铁精粉球团矿焙烧机理的研究. 钢铁研究,2008,1
|
[3] |
吕庆,亢立明,孙丽芬,刘曙光.冀东磁铁精粉球团矿氧化机理的研究.钢铁研究学报,2007,8:7-10.
|
[4] |
刘成松, 李京社, 杨树峰, 等.邯邢地区磁精矿造球的实验和机理[J].钢铁, 2014, 49(10):7-17
|
[3] |
吕庆,亢立明,孙丽芬,刘曙光.冀东磁铁精粉球团矿氧化机理的研究.钢铁研究学报,2007,8:7-10.
|
[4] |
刘成松, 李京社, 杨树峰, 等.邯邢地区磁精矿造球的实验和机理[J].钢铁, 2014, 49(10):7-17
|
[5] |
刘曙光.冀东铁精矿粉造球、氧化及焙烧机理的研究[D]. 唐山: 河北理工大学, 2006.
|
[5] |
刘曙光.冀东铁精矿粉造球、氧化及焙烧机理的研究[D]. 唐山: 河北理工大学, 2006.
|
[6] |
赵威, 王翠轻, 邯邢磁铁矿精粉用作球团矿原料的试验研究[J].烧结球团,2008,33(6):11.
|
[6] |
赵威, 王翠轻, 邯邢磁铁矿精粉用作球团矿原料的试验研究[J].烧结球团,2008,33(6):11.
|
[7] |
周文涛, 复杂磁铁精矿球团制备的基础研究[D].长沙: 中南大学资源加工与生物工程学院, 2013.
|
[7] |
周文涛, 复杂磁铁精矿球团制备的基础研究[D].长沙: 中南大学资源加工与生物工程学院, 2013.
|
[8] |
傅菊英, 李云涛, 姜昌伟, 等.磁铁矿球团氧化动力学[J].中南大学学报: 自然科学版, 2004, 35(6):950-954
|
[8] |
傅菊英, 李云涛, 姜昌伟, 等.磁铁矿球团氧化动力学[J].中南大学学报: 自然科学版, 2004, 35(6):950-954
|
[9] |
黄柱成, 张元波, 朱尚朴, 等.以赤铁矿为主配加磁铁矿制备氧化球团的研究[J].钢铁, 2004, 39(4):9-13
|
[9] |
黄柱成, 张元波, 朱尚朴, 等.以赤铁矿为主配加磁铁矿制备氧化球团的研究[J].钢铁, 2004, 39(4):9-13
|
[10] |
黎前程, 朱德庆, 潘建.南非磁铁精矿球团试验[J].烧结球团, 2005, 30(3):1-4
|
[10] |
黎前程, 朱德庆, 潘建.南非磁铁精矿球团试验[J].烧结球团, 2005, 30(3):1-4
|
[1] |
CHENG Xiang-kui, ZHAO Ying-tao, ZHAO Xu, WANG Jun, HUANG Xiao-li, PU Chun-lei. Preparation of V-Ti magnetite ore basic pellet containing NaOH[J]. Iron and Steel, 2020, 55(6): 33-37. |
[2] |
WANG Xin, PAN Jian, ZHU De-qing, GUO Zheng-qi, TIAN Hong-yü. Process of pelletization of nickel laterite and chromite[J]. Iron and Steel, 2020, 55(3): 23-28. |
[3] |
WANG Xiao-lei1,SHI Xue-feng1,HU Chang-qing1,WANG Xin-dong2,HU Qi-chen2. Experimental study on spherication and cold performance of highsilica magnesium flux pellets[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(3): 212-219. |
[4] |
ZHANG Lin-lin, FU Gang-hua, GUO Yu-feng, CHEN Feng, ZHENG Fu-qiang . Effect of basicity on quality of green fluxed pellets[J]. Iron and Steel, 2019, 54(5): 14-18. |
[5] |
ZHANG Xue-song1,2, XU Meng1,2, WU Jian-long1,2, WANG Wei1,2. Sulfur analysis and measures for reducing sulfur in ironmaking process of Shougang Jingtang[J]. Iron and Steel, 2019, 54(3): 18-22. |
[6] |
WANG Xin-dong, LI Jian-xin, HU Qi-chen. Application practice of source and process sulfur-nitrate reduction technology based on optimization of blast furnace charge structure[J]. Iron and Steel, 2019, 54(12): 104-110. |
|
|
|
|