Hardenability bandwidth of Mn-Cr gear steel based on micro-segregation model |
WANG Xiao-ying1,2,YAN Hui-cheng2,QIU Sheng-tao2 |
(1. School of Materials and Metallurgy, Northeastern University, Shenyang 110819,Liaoning, China 2. National Engineering Research Center of Continuous Casting Technology, Central Iron and Steel Research Institute,Beijing 100081, China) |
|
|
Abstract The heat transfer model of the solidification process of billet in CCM was used to calculate the cooling rates in different stages of solidification, the classical BF micro-segregation model was modified, based on which a prediction model of hardenability bandwidth induced by the inhomogeneity of chemical compositions for Mn-Cr gear steel was established. The effect of secondary cooling intensity on the distribution of hardenability bandwidth of 20CrMnTi steel was also investigated. The calculated results shows that the hardenability bandwidth of 20CrMNTi continuous casting billet along jominy distance was parabolic. The hardenability bandwidth-Jominy distance curve firstly appeared up-trend within 15 mm and then down-trend, and the hardenability bandwidth reached maximal value at the point of Jominy distance of 15 mm. It indicated that Appropriate improvement of secondary cooling intensity can narrow the biggest hardenability bandwidth of casting billets.
|
Received: 12 April 2016
Published: 08 October 2016
|
|
|
|
[1] |
LI Lan-xin1,WANG Min1,JUAN Rong-fei1,BAO Yan-ping1,YANG Jin2. Distribution characteristics of oxides and sulfide inclusions in key areas of gear steel forgings[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 370-376. |
[2] |
WANG Xing-yu, HAN Yan-shen, LIU Qing, XIAO Dong,CHEN Jun, GUAN Min. Effect of F-EMS on inner quality of spring steel continuous casting billet[J]. Iron and Steel, 2020, 55(5): 59-67. |
[3] |
TIAN Yan1,2,ZHAO Ming-chun2. Segregation of Nb and its formation mechanism of high strength casing steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 335-343. |
[4] |
TIAN Yan1,2,ZHAO Ming-chun2. Segregation of Nb and its formation mechanism of high strength casing steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 344-350. |
[5] |
SUN Jun-jie, ZHANG Yong-jie, XU Ji. Segregation of sinter particles in sinter shaft cooler[J]. Iron and Steel, 2020, 55(3): 16-22. |
[6] |
CHEN Deng-fu, XU Pei, LONG Mu-jun, DUAN Hua-mei, YANG Jie, WU Shi-xin. Development and investigation of advanced process model for secondary cooling in continuous casting of molten steel[J]. Iron and Steel, 2020, 55(3): 40-49. |
|
|
|
|