Origin analysis and improvement measures for striped color defects of 780 MPa grade dualphase steel |
ZHANG Liang-liang1,2,LI Yan1,2,YU Yang1,2,GAO Xiao-li1,2,SUN Chao-fan1,2,QI Da3 |
(1. Thin Strip Department, Shougang Research Institute of Technology, Beijing 100043, China 2. Beijing Key Laboratory of Green Recyclable Process for Iron and Steel Production Technology, Beijing 100043, China 3. Department of Cold Rolling Operation, Shougang Jingtang Iron and Steel Company,Tangshan 063200, Hebei, China) |
|
|
Abstract The microscopic characteristics of serious color defects on the surface of 780 MPa grade dual-phase steel strip were systematically investigated. The surface condition of defects were studied through SEM and EPMA analysis methods. The results show that the area with color defect was rough and the surface shows the broken topography and there was a positive correlation between the broken intensity and the severity of the color defects. EDS and EPMA proved the existence of slightly oxidization at the broken area. The surface enrichment of the defects was analyzed through GDOES analysis, and the severity of striped color defect was closely related to the depth of enrichment(mainly Si and Mn) peak from the surface. Combined with hot-rolled section analysis, the enrichment has already existed in the form of olivine and its macroscopic state was the red scale defect. The red scale defect was difficult to be wiped off after pickling, the broken intensity and the enrichment depth showed many differences on the surface in different areas after cold-rolling, which finally formed the striped color defects on the surface of annealing plate. Based on the origin analysis, the measurements for hot and cold rolling production have been proposed, which ultimately reduced or eliminated the formation of striped color defects.
|
Received: 16 May 2016
Published: 13 January 2017
|
|
|
|
[1] |
李远鹏,张启富, 江社明.双相钢中 含量对表面氧化物及抑制层形貌的影响[J].材料热处理学报, 2014, 35(1):152-156
|
[1] |
李远鹏,张启富, 江社明.双相钢中 含量对表面氧化物及抑制层形貌的影响[J].材料热处理学报, 2014, 35(1):152-156
|
[2] |
Murugaiyan A,Saha Podder A.Phase transformations in two C-Mn-Si-Cr dual phase steels[J].ISIJ International, 2006, 46(10):1489-1494
|
[2] |
Murugaiyan A,Saha Podder A.Phase transformations in two C-Mn-Si-Cr dual phase steels[J].ISIJ International, 2006, 46(10):1489-1494
|
[3] |
徐斌,吝章国,贾耿,伟谷凤龙.汽车用冷轧板表面色差缺陷的研究[A]. 见:河北省冶金学会编..河北省2010年炼钢-连铸-轧钢生产技术与学术交流会论文集[C]., 2010, :86-90
|
[3] |
徐斌,吝章国,贾耿,伟谷凤龙.汽车用冷轧板表面色差缺陷的研究[A]. 见:河北省冶金学会编..河北省2010年炼钢-连铸-轧钢生产技术与学术交流会论文集[C]., 2010, :86-90
|
[4] |
刘晓程,张向东,孙学玉.冷轧板表面色差缺陷控制[J].河北冶金, 2013, 215(11):60-62
|
[4] |
刘晓程,张向东,孙学玉.冷轧板表面色差缺陷控制[J].河北冶金, 2013, 215(11):60-62
|
[5] |
郭晓波,钟莉莉,刘跃华.冷轧板常见表面缺陷特征及成因分析[J].鞍钢技术, 2011, 372(6):37-42
|
[5] |
郭晓波,钟莉莉,刘跃华.冷轧板常见表面缺陷特征及成因分析[J].鞍钢技术, 2011, 372(6):37-42
|
[6] |
Shi M F, Thomas G H, Chen X M.Formability Performance Comparison Between Dual Phase and HSLA Steels. 43 MWSP CONF.PROC:ISS , [J].世界钢铁, .2001, 11(4):18-22
|
[6] |
Shi M F, Thomas G H, Chen X M.Formability Performance Comparison Between Dual Phase and HSLA Steels. 43 MWSP CONF.PROC:ISS , [J].世界钢铁, .2001, 11(4):18-22
|
[7] |
左军,常军,刘勇,张开华,杨金成,李卫平.热轧钢板红锈氧化铁皮形成机制及改进措施[J].钢铁, 2010, 45(10):84-87
|
[7] |
左军,常军,刘勇,张开华,杨金成,李卫平.热轧钢板红锈氧化铁皮形成机制及改进措施[J].钢铁, 2010, 45(10):84-87
|
[8] |
蒋柯,韩静涛.氧化铁皮成分和结构研究[J].塑性工程学报, 2000, 7(3):40-43
|
[8] |
蒋柯,韩静涛.氧化铁皮成分和结构研究[J].塑性工程学报, 2000, 7(3):40-43
|
[9] |
张清东,王文广,吴越,王慧.冷轧带钢板形和表面粗糙度协同控制[J].北京科技大学学报, 2005, 27(2):232-234
|
[9] |
张清东,王文广,吴越,王慧.冷轧带钢板形和表面粗糙度协同控制[J].北京科技大学学报, 2005, 27(2):232-234
|
[10] |
井玉安,臧晓明,商秋月,覃毅,李富强,刘英明.还原冷轧过程中带钢表面形貌演变规律[J].钢铁, 2014, 49(12):38-43
|
[10] |
井玉安,臧晓明,商秋月,覃毅,李富强,刘英明.还原冷轧过程中带钢表面形貌演变规律[J].钢铁, 2014, 49(12):38-43
|
[11] |
郭太雄,钟声,贾斌,方淑芳,李扬州.冷轧薄板表面条痕缺陷成因及预防[J].轧钢, 2000, 17(6):22-24
|
[11] |
郭太雄,钟声,贾斌,方淑芳,李扬州.冷轧薄板表面条痕缺陷成因及预防[J].轧钢, 2000, 17(6):22-24
|
[1] |
CAO Jing-hua1,PAN Hong-bo2,3,ZHANG Jing1,ZHANG Teng-fei2,LI Xu-dong2,LIU Wei-ming2,3. Continuous cooling transformation of NbTi microcarbon deep drawing dualphase steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 322-328. |
[2] |
SHI Jun-liang1,LI Shen-bao2,ZHENG Wei-wei2. Effect of bainite characteristics on room temperature mechanical properties of fine ferrite/bainite dual phase steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 166-174. |
[3] |
LI Song-fen. Fatigue crack growth behavior of DP780 dual phase steel subjected to single tensile overload[J]. Iron and Steel, 2019, 54(3): 82-86. |
[4] |
ZHOU Xiao- guang,LIU Xu- hui,,YANG Chun- yu,WU Hao- hong,LIU Zhen- yu,WANG Guo- dong. Microstructural evolution of hot- rolled thin- gauge DP600 dual- phase steel[J]. , 2019, 31(2): 221-226. |
[5] |
ZHU Rui-qi,SONG Xin-li,ZHENG Ai-qin,CHEN Rong-dong,JIA Juan,FAN Li-xia. Microstructure characteristic and mechanical properties of hot rolled DP600 steel[J]. Iron and Steel, 2018, 53(9): 57-62. |
[6] |
JIANG Guang-rui,,CHEN Ling-feng,WANG Hai-quan,,LIU Jin-sheng,LIU Li-bin,5. Influence of over-aging dew point on surface color difference of dual phase steel[J]. Iron and Steel, 2017, 52(8): 87-91. |
|
|
|
|