Analysis of [NOx]removal process in sintering flue gas |
ZHANG Hong-liang1,2,SHI Qi1,LONG Hong-ming1,3,LI Jia-xin1,CHUN Tie-jun1,GAO Zhi-fang1 |
(1. School of Metallurgical Engineering,Anhui University of Technology,Ma’anshan 243002,Anhui,China 2. Analysis and Testing Central Facility,Anhui University of Technology,Ma’anshan 243002,Anhui,China 3. Key Laboratory of Metallurgical Emission Reduction and Resources Recycling of Ministry of Education,Anhui University of Technology,Ma’anshan 243002,Anhui,China) |
|
|
Abstract With the government’s increasingly stringent emissions requirements of pollutants,the[NOx]removal from sintering flue gas becomes an important direction of pollution control in the steel industry. At present,[NOx]removal in sintering process is mainly achieved by the control of raw material and process,while the terminal control technology which is the key of denitration in the future is not mature. Therefore,this paper simply introduces the technology of raw material control and process control,and the problems and solutions of terminal control technology,especially selective catalytic reduction technology in sintering flue gas treatment are mainly introduced.
|
Received: 27 September 2016
Published: 04 May 2017
|
|
|
|
[1] |
Tang C, Zhang H, Dong L. Ceria-based catalysts for low-temperature selective catalytic reduction of NO with NH3 [J]. Catalysis Science & Technology. 2016, 6(5): 1248.
|
[1] |
Tang C, Zhang H, Dong L. Ceria-based catalysts for low-temperature selective catalytic reduction of NO with NH3 [J]. Catalysis Science & Technology. 2016, 6(5): 1248.
|
[2] |
闫晓淼,李玉然,朱廷钰,等. 钢铁烧结烟气多污染物排放及协同控制概述[J]. 环境工程技术学报. 2015,5(2) : 85.YAN Xiao-miao,LI Yu-ran,ZHU Ting-yu,et al. Review of emission and simultaneous control of multiple pollutants from iron-steel sintering flue gas [J]. Journal of Environmental Engineering Technology. 2015, 5(2) : 85.
|
[2] |
闫晓淼,李玉然,朱廷钰,等. 钢铁烧结烟气多污染物排放及协同控制概述[J]. 环境工程技术学报. 2015,5(2) : 85.YAN Xiao-miao,LI Yu-ran,ZHU Ting-yu,et al. Review of emission and simultaneous control of multiple pollutants from iron-steel sintering flue gas [J]. Journal of Environmental Engineering Technology. 2015, 5(2) : 85.
|
[3] |
苏玉栋,李咸伟,范晓慧. 烧结过程中NOx减排技术研究进展[J]. 烧结球团. 2013,38(6): 41.SU Yu-dong, LI Xian-wei, FAN Xiao-hui. Research progress of NOx reduction technology in sintering process [J]. Sintering and Pelletizing. 2013, 38(6): 41.
|
[3] |
苏玉栋,李咸伟,范晓慧. 烧结过程中NOx减排技术研究进展[J]. 烧结球团. 2013,38(6): 41.SU Yu-dong, LI Xian-wei, FAN Xiao-hui. Research progress of NOx reduction technology in sintering process [J]. Sintering and Pelletizing. 2013, 38(6): 41.
|
[4] |
赵利明,李咸伟,马洛文. 烧结过程NOx形成机理及减排措施探讨[J]. 烧结球团. 2015,40(5): 57.ZHAO Li-ming, LI Xian-wei, MA Luo-wen. Discussion on NOx formation mechanism in sintering process and its emission reduction measures [J]. Sintering and Pelletizing. 2015, 40(5): 57.
|
[4] |
赵利明,李咸伟,马洛文. 烧结过程NOx形成机理及减排措施探讨[J]. 烧结球团. 2015,40(5): 57.ZHAO Li-ming, LI Xian-wei, MA Luo-wen. Discussion on NOx formation mechanism in sintering process and its emission reduction measures [J]. Sintering and Pelletizing. 2015, 40(5): 57.
|
[5] |
邢芳芳,姜琪,张亚志,等. 钢铁工业烧结烟气多污染物协同控制技术分析[J]. 环境工程. 2014, 32(4): 75.XING Fang-fang, JIANG Qi, ZHANG Ya-zhi, et al. The analysis of multi-pollutant collaborative control technologies of sinter flue gas in iron and steel industry [J]. Environmental Engineering. 2014, 32(4): 75.
|
[5] |
邢芳芳,姜琪,张亚志,等. 钢铁工业烧结烟气多污染物协同控制技术分析[J]. 环境工程. 2014, 32(4): 75.XING Fang-fang, JIANG Qi, ZHANG Ya-zhi, et al. The analysis of multi-pollutant collaborative control technologies of sinter flue gas in iron and steel industry [J]. Environmental Engineering. 2014, 32(4): 75.
|
[6] |
刘福东,单文坡,石晓燕,等. 用于NH3选择性催化还原NOx的钒基催化剂[J]. 化学进展. 2012, 24(4): 445.LIU Fu-dong, SHAN Wen-po, SHI Xiao-yan, et al. Vanadium-Based Catalysts for the Selective Catalytic Reduction of NOx with NH3 [J]. Progress in Chemistry. 2012, 24(4): 445.
|
[6] |
刘福东,单文坡,石晓燕,等. 用于NH3选择性催化还原NOx的钒基催化剂[J]. 化学进展. 2012, 24(4): 445.LIU Fu-dong, SHAN Wen-po, SHI Xiao-yan, et al. Vanadium-Based Catalysts for the Selective Catalytic Reduction of NOx with NH3 [J]. Progress in Chemistry. 2012, 24(4): 445.
|
[7] |
Li J, Chang H, Ma L, et al. Low-temperature selective catalytic reduction of NOx with NH3 over metal oxide and zeolite catalysts-A review [J]. Catalysis Today. 2011, 175 (1): 147.
|
[7] |
Li J, Chang H, Ma L, et al. Low-temperature selective catalytic reduction of NOx with NH3 over metal oxide and zeolite catalysts-A review [J]. Catalysis Today. 2011, 175 (1): 147.
|
[8] |
Liu C, Shi J W, Gao C, et al. Manganese oxide-based catalysts for low-temperature selective catalytic reduction of NOx with NH3: A review [J]. Applied Catalysis A: General. 2016, 522: 54.
|
[8] |
Liu C, Shi J W, Gao C, et al. Manganese oxide-based catalysts for low-temperature selective catalytic reduction of NOx with NH3: A review [J]. Applied Catalysis A: General. 2016, 522: 54.
|
[9] |
Liu F, He H. Selective catalytic reduction of NO with NH3 over manganese substituted iron titanate catalyst: Reaction mechanism and H2O/SO2 inhibition mechanism study [J]. Catalysis Today. 2010, 153(3-4): 70.
|
[9] |
Liu F, He H. Selective catalytic reduction of NO with NH3 over manganese substituted iron titanate catalyst: Reaction mechanism and H2O/SO2 inhibition mechanism study [J]. Catalysis Today. 2010, 153(3-4): 70.
|
[10] |
Shan W, Liu F, He H, et al. The remarkable improvement of a Ce-Ti based catalyst for NOx abatement, prepared by a homogeneous precipitation method. ChemCatChem. 2011, 3(8): 1286.
|
[10] |
Shan W, Liu F, He H, et al. The remarkable improvement of a Ce-Ti based catalyst for NOx abatement, prepared by a homogeneous precipitation method. ChemCatChem. 2011, 3(8): 1286.
|
[11] |
Xu W, He H, Yu Y. Deactivation of a Ce/TiO2 catalyst by SO2 in the selective catalytic reduction of NO by NH3 [J]. The Journal of Physical Chemistry C. 2009, 113(11): 4426.
|
[11] |
Xu W, He H, Yu Y. Deactivation of a Ce/TiO2 catalyst by SO2 in the selective catalytic reduction of NO by NH3 [J]. The Journal of Physical Chemistry C. 2009, 113(11): 4426.
|
[12] |
Liu Z, Li J, Junaid A S M. Knowledge and know-how in improving the sulfur tolerance of deNOx catalysts [J]. Catalysis Today. 2010, 153(3-4): 95.
|
[12] |
Liu Z, Li J, Junaid A S M. Knowledge and know-how in improving the sulfur tolerance of deNOx catalysts [J]. Catalysis Today. 2010, 153(3-4): 95.
|
[13] |
Hou Y, Huang Z, Guo S. Effect of SO2 on V2O5/ACF catalysts for NO reduction with NH3 at low temperature [J]. Catalysis Communications. 2009, 10(11): 1538.
|
[13] |
Hou Y, Huang Z, Guo S. Effect of SO2 on V2O5/ACF catalysts for NO reduction with NH3 at low temperature [J]. Catalysis Communications. 2009, 10(11): 1538.
|
[14] |
Li K, Tang X L, Yi H H, et al. Low-temperature catalytic oxidation of NO over Mn-Co-Ce-Ox catalyst [J]. Chemical Engineering Journal. 2012, 192: 99.
|
[14] |
Li K, Tang X L, Yi H H, et al. Low-temperature catalytic oxidation of NO over Mn-Co-Ce-Ox catalyst [J]. Chemical Engineering Journal. 2012, 192: 99.
|
[15] |
Chang H Z, Chen X Y, Li J H, et al. Improvement of activity and SO2 tolerance of Sn-Modified MnOx-CeO2 catalysts for NH3-SCR at low temperatures [J]. Environmental Science &Technology. 2013, 47(10): 5294.
|
[15] |
Chang H Z, Chen X Y, Li J H, et al. Improvement of activity and SO2 tolerance of Sn-Modified MnOx-CeO2 catalysts for NH3-SCR at low temperatures [J]. Environmental Science &Technology. 2013, 47(10): 5294.
|
[16] |
Zhang Q L, Qiu C T, Xu H D, et al. Novel promoting effects of tungsten on the selective catalytic reduction of NO by NH3 over MnOx-CeO2 monolith catalyst [J]. Catalysis Communications. 2011, 16(1): 20.
|
[16] |
Zhang Q L, Qiu C T, Xu H D, et al. Novel promoting effects of tungsten on the selective catalytic reduction of NO by NH3 over MnOx-CeO2 monolith catalyst [J]. Catalysis Communications. 2011, 16(1): 20.
|
[17] |
Zhang D S, Zhang L, Shi L Y, et al. In situ supported MnOx-CeOx on carbon nanotubes for the low-temperature selective catalytic reduction of NO with NH3 [J]. Nanoscale. 2013, 5(3): 1127.
|
[17] |
Zhang D S, Zhang L, Shi L Y, et al. In situ supported MnOx-CeOx on carbon nanotubes for the low-temperature selective catalytic reduction of NO with NH3 [J]. Nanoscale. 2013, 5(3): 1127.
|
[18] |
Lu X N, Song C Y, Chang C C, et al. Manganese oxides supported on TiO2-Graphene nanocomposite catalysts for selective catalytic reduction of NOx with NH3 at low temperature [J]. Industrial & Engineering Chemistry Research. 2014, 53(29): 11601.
|
[18] |
Lu X N, Song C Y, Chang C C, et al. Manganese oxides supported on TiO2-Graphene nanocomposite catalysts for selective catalytic reduction of NOx with NH3 at low temperature [J]. Industrial & Engineering Chemistry Research. 2014, 53(29): 11601.
|
[19] |
Samojeden B, Motak M, Grzybek T. The influence of the modification of carbonaceous materials on their catalytic properties in SCR-NH3: A short review [J]. Comptes Rendus Chimie. 2015, 18(10): 1049.
|
[19] |
Samojeden B, Motak M, Grzybek T. The influence of the modification of carbonaceous materials on their catalytic properties in SCR-NH3: A short review [J]. Comptes Rendus Chimie. 2015, 18(10): 1049.
|
[20] |
Gao R H, Zhang D S, Maitarad P, et al. Morphology-dependent properties of MnOx/ZrO2-CeO2 nanostructures for the selective catalytic reduction of NO with NH3 [J]. The Journal of Physical Chemistry C. 2013, 117(20): 10502.
|
[20] |
Gao R H, Zhang D S, Maitarad P, et al. Morphology-dependent properties of MnOx/ZrO2-CeO2 nanostructures for the selective catalytic reduction of NO with NH3 [J]. The Journal of Physical Chemistry C. 2013, 117(20): 10502.
|
[21] |
孟庆立,李昭祥,杨其伟,等. 台湾中钢SCR触媒在烧结场脱硝与脱二噁英中的应用[J]. 武汉大学学报(工学版). 2012, 45(6): 751.MAN Chin-li, LEE Zhou-shiang, YOUNG Chyiwoeiz, et al. Application of SCR catalyst to sinter plant for NO/dioxins removal [J]. Engineering Journal of Wuhan University. 2012, 45(6): 751.
|
[21] |
孟庆立,李昭祥,杨其伟,等. 台湾中钢SCR触媒在烧结场脱硝与脱二噁英中的应用[J]. 武汉大学学报(工学版). 2012, 45(6): 751.MAN Chin-li, LEE Zhou-shiang, YOUNG Chyiwoeiz, et al. Application of SCR catalyst to sinter plant for NO/dioxins removal [J]. Engineering Journal of Wuhan University. 2012, 45(6): 751.
|
[22] |
Li H, Wu S, Li L, et al. CuO-CeO2/TiO2 catalyst for simultaneous NO reduction and Hg0 oxidation at low temperatures [J]. Catalysis Science & Technology. 2015, 5(12): 5129.
|
[22] |
Li H, Wu S, Li L, et al. CuO-CeO2/TiO2 catalyst for simultaneous NO reduction and Hg0 oxidation at low temperatures [J]. Catalysis Science & Technology. 2015, 5(12): 5129.
|
[23] |
杨飏. 氮氧化物减排技术与烟气脱硝工程[M]. 北京: 冶金工业出版社, 2007.YANG Yang. Nitrogen oxides emission reduction technology and flue gas denitrification Engineering [M]. Beijing: Metallurgical industry press, 2007.
|
[23] |
杨飏. 氮氧化物减排技术与烟气脱硝工程[M]. 北京: 冶金工业出版社, 2007.YANG Yang. Nitrogen oxides emission reduction technology and flue gas denitrification Engineering [M]. Beijing: Metallurgical industry press, 2007.
|
[1] |
ZHANG Wei-li, WU Sheng-li, HU Zhong-jie. Analysis of affecting factors of activated coke denitrationefficiency for sintering flue gas[J]. Iron and Steel, 2020, 55(5): 109-115. |
[2] |
ZHANG Wei-li1,WU Sheng-li1,HU Zhong-jie1,2. Statistical analysis of factors affecting desulfurization rate of activated coke for sintering flue gas[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 281-288. |
[3] |
WAN Jun-ying, CHEN Tie-jun, ZHOU Xian-lin, LUO Yan-hong, HUANG Kai-wei. Experimental study on NO reduction with catalysis of sinter[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(4): 354-360. |
[4] |
LIU Ding-ping,YUAN Dan-jue. Experimental research on sintering flue gas swirl atomization desulfurization and dust integration[J]. Iron and Steel, 2018, 53(8): 102-106. |
[5] |
WANG Qing-guo,,ZHU Tong,LI Yong. Sintering flue gas purifying process and equipment by use of activated coke in Baosteel[J]. Iron and Steel, 2018, 53(3): 87-95. |
[6] |
WANG Zheng,CUI Heng,. Saline-sodic soils amelioration with sintering flue gas desulfurization gypsum[J]. Iron and Steel, 2015, 50(12): 47-52. |
|
|
|
|