Investigations on inclusion control of heat resistant steel 310S in EAF+AOD+LF process |
ZHAI Jun1,2,LIU Liu1 |
(1. Metallurgical Technology Research Institute,Central Iron and Steel Research Institute,Beijing 100081,China 2. Technical Center,Shanxi Taigang Stainless Steel Co.,Ltd.,Taiyuan 030003,Shanxi,China) |
|
|
Abstract For achieving preferable corrosion resistance,the cleanliness of 310S stainless steel needs to be improved further. The cleanliness of 310S heat resistant steel produced by EAF+AOD+LF process were studied by means of chemical analysis,metallographic observation as well as scanning electron microscope. Based on the results,the optimizing solutions were put forward. The results indicated that increasing AOD slag basicity to 2.0,adding Al in LF process to deep deoxidizing and prolonging the Ar blowing time to remove inclusions with large size were very effective. After optimizing,[w(T[O])] in steel slab decresed from 0.003 4%to 0.002 5%,and the amount of inclusions with the size of 1-7 μm increased by 15.5%,the amount of inclusions larger than 15 μm decreased by 5.8%,and large inclusions over 30 μm were approximately eliminated.
|
Received: 14 July 2016
Published: 04 May 2017
|
|
|
|
[1] |
高津刚,张虎平。关于0Cr25Ni20钢轧制开裂问题的研究[J].天津冶金。2000:21-22.
|
[1] |
高津刚,张虎平。关于0Cr25Ni20钢轧制开裂问题的研究[J].天津冶金。2000:21-22.
|
[2] |
Parda J M, Carvalho S S. Failure analysis of AISI 310S plate in an inert gas generator used in off-shore oil platform[J]. Engineering Failure Analysis,2011(18):1435-1444.
|
[2] |
Parda J M, Carvalho S S. Failure analysis of AISI 310S plate in an inert gas generator used in off-shore oil platform[J]. Engineering Failure Analysis,2011(18):1435-1444.
|
[3] |
李正邦.超洁净钢和零非金属夹杂钢[J].2004,25(4):24-25.
|
[3] |
李正邦.超洁净钢和零非金属夹杂钢[J].2004,25(4):24-25.
|
[4] |
Mizuno K,Todoroki H,Noda M,et a1.Effects ofA1 and Ca in Ferrosilicon Alloys for Deoxidation on Inclusion Composition in Type 304 Stainless Steel[J].Iron and Steelmaker,2001(8):93-101.
|
[4] |
Mizuno K,Todoroki H,Noda M,et a1.Effects ofA1 and Ca in Ferrosilicon Alloys for Deoxidation on Inclusion Composition in Type 304 Stainless Steel[J].Iron and Steelmaker,2001(8):93-101.
|
[5] |
陈家祥.炼钢常用图标数据手册[M].冶金工业出版社 768-781.
|
[5] |
陈家祥.炼钢常用图标数据手册[M].冶金工业出版社 768-781.
|
[6] |
张荣品. 150t椭圆型钢包吹氩精炼优化研究[J]. 梅山科技,2003,04:31-34.
|
[6] |
张荣品. 150t椭圆型钢包吹氩精炼优化研究[J]. 梅山科技,2003,04:31-34.
|
[7] |
李道明.不锈钢中非金属夹杂物的危害及去除[J].山西冶金,2008,31(4):24-26.
|
[7] |
李道明.不锈钢中非金属夹杂物的危害及去除[J].山西冶金,2008,31(4):24-26.
|
[1] |
HOU Xin-mei, LIU Yun-song, WANG En-hui. Effect of ladle-lining refractory on non-metallic inclusions in steel[J]. Iron and Steel, 2020, 55(6): 15-24. |
[2] |
YU Hui-xiang, PAN Ming, YANG De-xin. Behavior of inclusions in ultra-low carbon IF steel during deoxidation and alloying process[J]. Iron and Steel, 2020, 55(6): 46-53. |
[3] |
NIU Kai-jun, YANG Wen, ZHANG Li-feng, CHU Yan-ping, ZHANG Hong-qi, GUO Zi-qiang. Thermodynamics and industrial practice of formation of inclusions during solidification of tire cord steels[J]. Iron and Steel, 2020, 55(6): 61-67. |
[4] |
LI Lan-xin1,WANG Min1,JUAN Rong-fei1,BAO Yan-ping1,YANG Jin2. Distribution characteristics of oxides and sulfide inclusions in key areas of gear steel forgings[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 370-376. |
[5] |
QIN Zheng-feng, XUE Zheng-liang, LI Jin-bo, LI Bo-si. Origin of large spherical or bar-shaped inclusions in calcium treated steel[J]. Iron and Steel, 2020, 55(5): 31-38. |
[6] |
WANG Yi, ZHANG Li-feng, REN Ying, REN Qiang. Mechanism of inclusion evolution during refining process of 37Mn5 steel production[J]. Iron and Steel, 2020, 55(5): 39-44. |
|
|
|
|