Pilot practice of direct modification of molten blast furnace slag and preparation of mineral wool fiber |
LI Jun1,ZHANG Ling-ling2,ZHAO Gui-zhou1,CANG Da-qiang1 |
(1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083,China 2. School of Energy and Environmental Engineering, University of Science and Technology Beijing,Beijing 100083, China) |
|
|
Abstract Molten blast furnace slag flowed into electric furnace through the slag runner and siliceous additives as modification agent were simultaneously added into the electric furnace to remelt the slag. The modified slag was heated to 1 400-1 500 ℃ by electric furnace and then the molten slag with proper viscosity and fluidity was prepared into fireproof,thermal insulation and sound absorbing slag wool fiber through high-speed centrifugation method. Parameters of the slag wool fiber met the?national standards,with shot content of 4.7%,average diameter of 5.5 μm and water-absorption rate of 0.2%. Energy consumption and cost decreased by 40%-60% compared with traditional cupola furnace method. The new technology of preparing mineral wool fiber using direct modification provided a high value added method for the direct utilization of molten blast furnace slag.
|
Received: 09 March 2017
Published: 07 September 2017
|
|
|
|
[1] |
刘保瑶,张小兵.熔融高炉渣制造玄武岩棉的可行性分析[J].矿产综合利用, 2006, 1(1):44-47
|
[1] |
刘保瑶,张小兵.熔融高炉渣制造玄武岩棉的可行性分析[J].矿产综合利用, 2006, 1(1):44-47
|
[2] |
郭强,袁守谦,刘军,等.高炉渣改性作为矿渣棉原料的试验[J].中国冶金, 2011, 21(8):46-49
|
[2] |
郭强,袁守谦,刘军,等.高炉渣改性作为矿渣棉原料的试验[J].中国冶金, 2011, 21(8):46-49
|
[3] |
周扬民,杨志远,闫兆民,等.高炉熔渣离心法制取矿棉[J].中国稀土学报, 2010, 28(Spec issue):351-353
|
[3] |
周扬民,杨志远,闫兆民,等.高炉熔渣离心法制取矿棉[J].中国稀土学报, 2010, 28(Spec issue):351-353
|
[4] |
Xiao Y L, Liu Y, Li Y Q.Status and development of mineral wool made from molten blast furnace slag[J].Baosteel Technical Research, 2011, 5(2):3-8
|
[4] |
Xiao Y L, Liu Y, Li Y Q.Status and development of mineral wool made from molten blast furnace slag[J].Baosteel Technical Research, 2011, 5(2):3-8
|
[5] |
张耀明.玻璃纤维与矿物棉全书[J]., 2001, :-
|
[5] |
张耀明.玻璃纤维与矿物棉全书[J]., 2001, :-
|
[6] |
Cheng A, Lin W T, Huang R.Application of rock wool waste in cement-based composites[J].Materials & Design, 2011, 32(2):636-642
|
[7] |
杨铧.高效利用高炉熔渣显热的一步法矿棉生产技术[J].新型建筑材料, 2003, 3(2):54-55
|
[6] |
Cheng A, Lin W T, Huang R.Application of rock wool waste in cement-based composites[J].Materials & Design, 2011, 32(2):636-642
|
[7] |
杨铧.高效利用高炉熔渣显热的一步法矿棉生产技术[J].新型建筑材料, 2003, 3(2):54-55
|
[8] |
Yamada M, Yokoyama H, Tada T.Rock wool products manufactured from blast furnace slag as main raw material[J].JFE Technical Report, 2008, 2(2):38-42
|
[8] |
Yamada M, Yokoyama H, Tada T.Rock wool products manufactured from blast furnace slag as main raw material[J].JFE Technical Report, 2008, 2(2):38-42
|
[9] |
Marabini A M, Plescia P, Maccari D, et al.New materials from industrial and wastes: glass–ceramics and glass- and rock-wool fiber[J].Int J Miner Process, 1998, 53(1-2):121-134
|
[9] |
Marabini A M, Plescia P, Maccari D, et al.New materials from industrial and wastes: glass–ceramics and glass- and rock-wool fiber[J].Int J Miner Process, 1998, 53(1-2):121-134
|
[10] |
肖永力,李永谦,刘茵,等.高炉渣矿棉的研究现状及发展趋势[J].硅酸盐通报, 2014, 33(7):1689-1694
|
[10] |
肖永力,李永谦,刘茵,等.高炉渣矿棉的研究现状及发展趋势[J].硅酸盐通报, 2014, 33(7):1689-1694
|
[11] |
王旭,袁守谦,李海潮.矿渣棉生产发展现状的综述[J].中国冶金, 2014, 24(8):18-21
|
[11] |
王旭,袁守谦,李海潮.矿渣棉生产发展现状的综述[J].中国冶金, 2014, 24(8):18-21
|
[12] |
Bisio G.Energy recovery from molten slag and exploitation of recovered energy[J].Energy, 1997, 22(5):501-509
|
[12] |
Bisio G.Energy recovery from molten slag and exploitation of recovered energy[J].Energy, 1997, 22(5):501-509
|
[13] |
龙跃,杜培培,李智慧,等.高炉熔渣四辊离心法制取矿渣棉[J].环境工程学报, 2015, 12(9):6049-6053
|
[13] |
龙跃,杜培培,李智慧,等.高炉熔渣四辊离心法制取矿渣棉[J].环境工程学报, 2015, 12(9):6049-6053
|
[14] |
?irok B, Bizjan B, Orbani? A, et al.Mineral wool melt fiberization on a spinner wheel[J].Chemical Engineering Research and Design, 2014, 91(1):80-90
|
[14] |
?irok B, Bizjan B, Orbani? A, et al.Mineral wool melt fiberization on a spinner wheel[J].Chemical Engineering Research and Design, 2014, 91(1):80-90
|
|
|
|