Analysis on delaminating of tensile fracture for 700 MPa beam steel |
LIU Hui1,2,3,WANG Yang1,2,3,SUN Qing4,ZHU Jing-tao4,FU Jian-xun1,2,3 |
(1. State Key Laboratory of Advanced Special Steel, Shanghai 200072, China 2. Shanghai Key Laboratory of Advanced Ferrometallurgy, Shanghai 200072, China 3. School of Materials Science and Engineering, Shanghai University, Shanghai 200072, China 4. Department of Steel Research Development, Rizhao Steel Holding Group Co., Ltd., Rizhao 276806, Shandong, China) |
|
|
Abstract The mechanical properties of the 700 MPa beam steel hot rolled plate were tested, confirming the phenomenon of delamination in the tensile fracture. Metallographic microscope, Scanning electron microscope with energy dispersive spectrometer (SEM-EDS), transmission electron microscope with energy dispersive (TEM-EDS) were used to investigate the layered fracture. The average yield strength and tensile strength of this steel were 766.9 and 839.0 MPa respectively with average elongation of 19.2%,which meets the requirement of the performance. The results of the study shows that the inclusions and precipitates were finely distributed in slab and rolled products, which, however, is not the main cause of the delamination phenomenon. The bainite and M-A island were zonal distributed along the middle of the thickness-direction of the hot rolled plate, resulting in the discrepancy of plastic property, which is the direct cause of delamination phenomenon. The delaminating of tensile fracture for 700 MPa beam steel were analyzed and the improvement direction of actual production was proposed.
|
Received: 06 June 2017
Published: 14 November 2017
|
|
|
|
[1] |
李光瀛, 马鸣图.我国汽车板生产现状及展望[J].轧钢, 2014, 31(4):22-32
|
[1] |
李光瀛, 马鸣图.我国汽车板生产现状及展望[J].轧钢, 2014, 31(4):22-32
|
[2] |
李光瀛, 马鸣图, 张宜生, 等.超高强塑性汽车构件的先进热成形处理深加工技术[J].轧钢, 2015, 32(3):1-8
|
[2] |
李光瀛, 马鸣图, 张宜生, 等.超高强塑性汽车构件的先进热成形处理深加工技术[J].轧钢, 2015, 32(3):1-8
|
[3] |
杜林秀, 张中平, 佘广夫, 等.低成本级汽车大梁钢板的工业试制[J].金属热处理, 2007, 32(12):42-44
|
[3] |
杜林秀, 张中平, 佘广夫, 等.低成本级汽车大梁钢板的工业试制[J].金属热处理, 2007, 32(12):42-44
|
[4] |
干勇, 李光瀛, 马鸣图, 等.先进短流程-深加工新技术与高强塑性汽车构件的开发[J].轧钢, 2015, 32(4):1-11
|
[4] |
干勇, 李光瀛, 马鸣图, 等.先进短流程-深加工新技术与高强塑性汽车构件的开发[J].轧钢, 2015, 32(4):1-11
|
[5] |
王欣, 康永林, 于浩, 等.FTSR工艺生产低C-Mn钢510L汽车大梁板的组织性能分析[J].汽车工艺与材料,2006,0(2):6-8
|
[5] |
王欣, 康永林, 于浩, 等.FTSR工艺生产低C-Mn钢510L汽车大梁板的组织性能分析[J].汽车工艺与材料,2006,0(2):6-8
|
[6] |
张继魁, 辛莹, 张曼曼, 等.汽车大梁用低合金高强度钢板的性能与发展[J].汽车工艺与材料,2004,0(6):42-50
|
[6] |
张继魁, 辛莹, 张曼曼, 等.汽车大梁用低合金高强度钢板的性能与发展[J].汽车工艺与材料,2004,0(6):42-50
|
[7] |
蔡宁, 鞠新华, 邢阳, 等.Ti微合金化700MPa级汽车大梁钢的研究[J].轧钢, 2013, 30(5):5-9
|
[7] |
蔡宁, 鞠新华, 邢阳, 等.Ti微合金化700MPa级汽车大梁钢的研究[J].轧钢, 2013, 30(5):5-9
|
[8] |
叶晓瑜, 张开华, 王羿, 等.高Ti微合金化热轧高强度汽车结构用钢的开发[J].轧钢, 2015, 32(3):29-31
|
[8] |
叶晓瑜, 张开华, 王羿, 等.高Ti微合金化热轧高强度汽车结构用钢的开发[J].轧钢, 2015, 32(3):29-31
|
[9] |
李云, 王华, 秦海山, 顾柏, 等.热轧高强船板拉力分层原因分析及措施[J].钢铁, 2012, 47(4):98-101
|
[9] |
李云, 王华, 秦海山, 顾柏, 等.热轧高强船板拉力分层原因分析及措施[J].钢铁, 2012, 47(4):98-101
|
[10] |
杨建勋, 杜显彬, 李广艳, 等.800MPa级低碳贝氏体高强钢板拉伸断口分层机理[J].金属热处理, 2012, 37(9):40-44
|
[10] |
杨建勋, 杜显彬, 李广艳, 等.800MPa级低碳贝氏体高强钢板拉伸断口分层机理[J].金属热处理, 2012, 37(9):40-44
|
[11] |
郑建平, 侯中华, 廖仕军, 等.拉伸时分层的Q690D钢板试样的显微组织研究[J].热处理, 2012, 27(5):30-33
|
[11] |
郑建平, 侯中华, 廖仕军, 等.拉伸时分层的Q690D钢板试样的显微组织研究[J].热处理, 2012, 27(5):30-33
|
[12] |
王芹, 彭其春, 王理猷, 等.珠光体偏析带与,Ti(C,N)对HG70C钢热轧板拉伸断后分层的影响[J].特殊钢, 2012, 33(5):65-68
|
[12] |
王芹, 彭其春, 王理猷, 等.珠光体偏析带与,Ti(C,N)对HG70C钢热轧板拉伸断后分层的影响[J].特殊钢, 2012, 33(5):65-68
|
[13] |
刘新生, 赵定国, 崔成业.冷轧薄板中分层现象的研究[J].钢铁, 2008, 43(5):40-43
|
[13] |
刘新生, 赵定国, 崔成业.冷轧薄板中分层现象的研究[J].钢铁, 2008, 43(5):40-43
|
[14] |
Bai D Q, Nelson T, Bodnar R, et al.Development of high-performance steels for bridge applications at SSAB north American[J].Iron Steel Technology, 2009, 6(10):65-74
|
[14] |
Bai D Q, Nelson T, Bodnar R, et al.Development of high-performance steels for bridge applications at SSAB north American[J].Iron Steel Technology, 2009, 6(10):65-74
|
[1] |
WEI Tong-yu, ZOU De-ning, ZHANG Ying-bo, CHEN Wan-wan. Effect of aluminum on microstructure and properties of high alumina ferritic heat resistant steel[J]. Iron and Steel, 2020, 55(6): 80-83. |
[2] |
ZHAO Yun-peng, YU Chao, XIAO Hong, WU Zong-he, XU Peng-peng, XIE Hong-biao. Effect of pure iron interlayer on mechanical properties of hot rolled stainless steel clad plate[J]. Iron and Steel, 2020, 55(5): 73-79. |
[3] |
SHAO Cheng-wei, WANG Jun-tao, ZHAO Xiao-li, HUI Wei-jun. Microstructure and mechanical properties of intercritically annealed Al-contain medium Mn steel[J]. Iron and Steel, 2020, 55(5): 87-93. |
[4] |
XING Xian-qiang, CAO Wen-quan, WANG Cun-yu. Bond structure of 55SiCr steel used for coil springs of automotive suspension system[J]. Iron and Steel, 2020, 55(3): 68-73. |
[5] |
WANG Ji-hong, ZHANG Li-na, CHEN De-li, QI Yue, CAO Li-hong. Discussion about heat treatment process of X20Cr13 blade steel for gas turbine[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 18-. |
[6] |
ZHANG Quan-xin,ZHU Bin,XU Hong-hao,CAO Zheng-kuan. Cause analysis of cracking of 40CrNiMo steel shaft[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(2): 32-. |
|
|
|
|