Control technology of oxide scale for thin gauge hot rolled strip in CSP process |
WANG Shui-ze,LIU Yang,SUN Yi-qiang,HU Kuan-hui |
(Wuhan Branch, Baosteel Cetral Reasearch Institute, Wuhan 430080, Hubei, China) |
|
|
Abstract In order to study the influence of the main process parameters on the oxide scale of hot rolled strip, the nidustry experiment was carried out on the basis of CSP production line. The results show that the thickness of the strip has an important influence on the thickness of the oxide scale,and the thickness of oxide scale is unevenly distributed along the width of the stripdue to the difference of oxygen supply. By adjusting the final rolling temperature and laminar cooling method,the thickness of oxide scale can be reduced,but the effect is not obvious. Decreasing the coiling temperature is beneficial to promote the occurrence of eutectoid reaction of FeO,increase the ratio of α-Fe+Fe3O4,and improve the adhesion of oxide scale at room temperature. The distribution of oxide scales in the width of strip is uneven,and the eutectoid reaction of FeO in the middle is more adequate.
|
Received: 09 June 2017
Published: 05 February 2018
|
|
|
|
[1] |
R. Y. Chen , W. Y. D. Yuen. Review of the High-Temperature Oxidation of Iron and Carbon Steels in Air or Oxygen[J] , Oxidation of Metals, 2003 , 59(5), 433-468.
|
[1] |
R. Y. Chen , W. Y. D. Yuen. Review of the High-Temperature Oxidation of Iron and Carbon Steels in Air or Oxygen[J] , Oxidation of Metals, 2003 , 59(5), 433-468.
|
[2] |
Huibin Qi, Yuhai Qian, Wei Wang, etal. “Quartus Scale” of Hot-rolled Strip Steels and Its Formation Mechanism [J]. Baosteel Technical Research, 2007, 1(1): 42-54.
|
[2] |
Huibin Qi, Yuhai Qian, Wei Wang, etal. “Quartus Scale” of Hot-rolled Strip Steels and Its Formation Mechanism [J]. Baosteel Technical Research, 2007, 1(1): 42-54.
|
[3] |
F. Friedel, H. Bolt, X. Cornet, et al. Investigation of the formation, constitution and properties of scale formed during the finishing rolling, cooling and coiling of thin hot strips [R], European Commission, 2004.
|
[3] |
F. Friedel, H. Bolt, X. Cornet, et al. Investigation of the formation, constitution and properties of scale formed during the finishing rolling, cooling and coiling of thin hot strips [R], European Commission, 2004.
|
[4] |
刘振宇,王国栋. 热轧钢材氧化铁皮控制技术的最新进展[J]. 鞍钢技术,2012(2):1-5.
|
[4] |
刘振宇,王国栋. 热轧钢材氧化铁皮控制技术的最新进展[J]. 鞍钢技术,2012(2):1-5.
|
[5] |
吴光亮,孟征兵,李一为,成小军. 薄板坯连铸连轧过程氧化铁皮变化规律研究[J]. 钢铁,2011,46(6):79-85.
|
[5] |
吴光亮,孟征兵,李一为,成小军. 薄板坯连铸连轧过程氧化铁皮变化规律研究[J]. 钢铁,2011,46(6):79-85.
|
[6] |
刘洋,韩斌,谭文,等.热轧带钢氧化铁皮控制技术的现状与发展趋势[J].轧钢,2012,29(4):34-37.
|
[6] |
刘洋,韩斌,谭文,等.热轧带钢氧化铁皮控制技术的现状与发展趋势[J].轧钢,2012,29(4):34-37.
|
[1] |
ZHOU Cong-rui, CHEN Xiao-long, ZHOU Ming-ke,FAN Lei, MEI Peng, BAO Si-qian. Cause analysis of surface blackening of SPHC hot rolled strip after pickling[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 41-. |
[2] |
zhong-peng. Analysis of the formation mechanism of surface skin on tinplate[J]. , 2020, 45(3): 0-0. |
[3] |
MA Wei1,LI Wei-gang1,2,ZHAO Yun-tao1,YAN Bao-kang1. Prediction of hot-rolled roll force based on deep learning[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(9): 805-815. |
[4] |
YANG Geng-wei,LU Jia-wei,SUN Hui,FANG Zi-wei,ZHOU Yi-liao,YAO Nan. Microstructure, mechanical properties and phase transformation behavior of TiV microalloyed highstrength hotstrip steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 726-732. |
[5] |
ZHANG Jian-jun1,2, MAO Xin-ping 2, WANG Chun-feng3, ZHU Wan-jun2. Development and expection on high-efficiency producing technology of steelmaking in TSCR line[J]. Iron and Steel, 2019, 54(5): 1-8. |
[6] |
KANG Yong-lin, TIAN Peng, ZHU Guo-ming. Progress and trend on hot wide strip endless rolling technology[J]. Iron and Steel, 2019, 54(3): 1-8. |
|
|
|
|