CaO基含TiO2和Al2O3半钢渣系脱磷能力的热力学

doi:10.13228/j.boyuan.issn0449-749x.20170408

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (932 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract A dephosphorization thermodynamic model was established based on the coexistence theory and the principle of metallurgical dephosphorization. The thermodynamic study on the phosphorus distribution ratio and phosphate capacity of CaO-based steel slag which contained TiO2 and Al2O3 was carried out， and the thermodynamic model of phosphorus distribution ratio and phosphorus capacity of containing TiO2 and Al2O3 of CaO-based semi-steel slag were obtained. The calculated results indicate that the ability of dephosphorization would be reduced with the increase of[w((TiO2))]and [w((Al2O3))，]especially under the low temperature and low alkalinity conditions. The effect of TiO2 is greater than that of Al2O3 with the same content of the two oxides. The phosphorus distribution ratio and phosphate capacity increase first and then are almost invariant with the increase of alkalinity， increase first and then decreased as[w((FeO))]increasing， and decrease with the[w((MgO))]increasing. Semi-steel is smelted by semi-steel slag ball， and the[w((TiO2)＋(Al2O3))]and [w((FeO))]increase as semi-tempered slag ball isused， and[w((MgO))]decreases. On accounting of the synergistic action of FeO and MgO， the phosphorus distribution ratio and phosphate capacity increase. It is better for the increase of the phosphorus distribution ratio and phosphate capacity and weakening the influence of[w((TiO2)＋(Al2O3))]when the basicity of slag is about 4.0 and[w((FeO))≤20.0%，]and the proportion of semi-tempered slag ball is 15.0 %-20.0 % of total slag.

Received: 09 August 2017 Published: 16 March 2018

PACS:

TF711

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHANG Meng-Bo

Cite this article:

ZHANG Meng-Bo. Thermodynamics of dephosphorization capacity of containing TiO2 and Al2O3 of CaO-based semi-steel slag[J]. Iron and Steel, 2018, 53(3): 27-37.

URL:

http://www.chinamet.cn/Jweb_gt/EN/10.13228/j.boyuan.issn0449-749x.20170408 OR http://www.chinamet.cn/Jweb_gt/EN/Y2018/V53/I3/27

[1]	黄希祜．钢铁冶金原理(第三版) [D]．北京：冶金工业出版社，2004. (HUANG Xi-Hu. Principles of Steel Metallurgy.3th Ed [D]. Beijing: Metallurgical Industry Press, 2004.)
[1]	黄希祜．钢铁冶金原理(第三版) [D]．北京：冶金工业出版社，2004. (HUANG Xi-Hu. Principles of Steel Metallurgy.3th Ed [D]. Beijing: Metallurgical Industry Press, 2004.)
[2]	林路，包艳平，王敏，等．转炉冶炼BaO-SiO2-FeO渣系中磷的行为 [J]．北京科技大学学报，2013，35(6)：720. (LIN Lu, BAO Yan-ping, WANG Min, et al. Phosphorus behavior in CaO-SiO2-FeO slag during converter melting process [J]. Journal of University of Science and Technology Beijing, 2013, 35(6)：720.)
[2]	林路，包艳平，王敏，等．转炉冶炼BaO-SiO2-FeO渣系中磷的行为 [J]．北京科技大学学报，2013，35(6)：720. (LIN Lu, BAO Yan-ping, WANG Min, et al. Phosphorus behavior in CaO-SiO2-FeO slag during converter melting process [J]. Journal of University of Science and Technology Beijing, 2013, 35(6)：720.)
[3]	李鹏程，杨学民，张鉴．CaO-MgO-FeO-Fe2O3-SiO2炼钢渣系磷分配比的热力学模型 [J]．北京科技大学学报，2014，36(12)：1608. (LI Peng-cheng, YANG Xue-min, ZHANG Jian. Thermodynamic model of the phosphorus distribution ratio of CaO-MgO-FeO-Fe2O3-SiO2 steelmaking slags [J]. Journal of University of Science and Technology Beijing, 2014, 36(12):1608.)
[3]	李鹏程，杨学民，张鉴．CaO-MgO-FeO-Fe2O3-SiO2炼钢渣系磷分配比的热力学模型 [J]．北京科技大学学报，2014，36(12)：1608. (LI Peng-cheng, YANG Xue-min, ZHANG Jian. Thermodynamic model of the phosphorus distribution ratio of CaO-MgO-FeO-Fe2O3-SiO2 steelmaking slags [J]. Journal of University of Science and Technology Beijing, 2014, 36(12):1608.)
[4]	Ban-ya S．Mathematical expression of slag-metal reaction in steelmaking process by quadratic formalism based on the regular solution model [J]．ISIJ International，1993，33(1)：2.
[4]	Ban-ya S．Mathematical expression of slag-metal reaction in steelmaking process by quadratic formalism based on the regular solution model [J]．ISIJ International，1993，33(1)：2.
[5]	李风伟．GCr15轴承钢冶炼过程炉渣成分及夹杂物研究[D]．北京：北京科技大学，2014. (LI Feng-wei. Research on Slag Compositions and Inclusions of GCr15 Bearing Steel during Steelmaking Process [D]. Beijing: University of Science and Technology Beijing, 2014.)
[5]	李风伟．GCr15轴承钢冶炼过程炉渣成分及夹杂物研究[D]．北京：北京科技大学，2014. (LI Feng-wei. Research on Slag Compositions and Inclusions of GCr15 Bearing Steel during Steelmaking Process [D]. Beijing: University of Science and Technology Beijing, 2014.)
[6]	郭汉杰．冶金物理化学教程(第二版) [D]．北京：冶金工业出版社，2006. (GUO Han-jie. The Tutorials of Physical Chemistry of Metallurgy.2nd Ed [D]. Beijing: Metallurgical Industry Press, 2006.)
[6]	郭汉杰．冶金物理化学教程(第二版) [D]．北京：冶金工业出版社，2006. (GUO Han-jie. The Tutorials of Physical Chemistry of Metallurgy.2nd Ed [D]. Beijing: Metallurgical Industry Press, 2006.)
[7]	张鉴．冶金熔体和溶液的计算热力学 [D]．北京：冶金工业出版社，2007. (ZHANG Jian. Computational Thermodynamics of Metallurgical Melts and Solutions [D]. Beijing: Metallurgical Industry Press, 2007.)
[7]	张鉴．冶金熔体和溶液的计算热力学 [D]．北京：冶金工业出版社，2007. (ZHANG Jian. Computational Thermodynamics of Metallurgical Melts and Solutions [D]. Beijing: Metallurgical Industry Press, 2007.)
[8]	德国钢铁工程师协会编，王俭译．渣图集 [D]．北京：冶金工业出版社，1989. (German association of iron and steel engineers, WANG Jian (Translation). slags atlas [D]. Beijing: Metallurgical Industry Press, 1989.)
[8]	德国钢铁工程师协会编，王俭译．渣图集 [D]．北京：冶金工业出版社，1989. (German association of iron and steel engineers, WANG Jian (Translation). slags atlas [D]. Beijing: Metallurgical Industry Press, 1989.)
[9]	陈家祥．炼钢常用图表数据手册2版[D]．北京：冶金工业出版社，2010. (CHEN Jiang-xiang. Chart data in Steelmaking.2nd Ed [D]. Beijing: Metallurgical Industry Press, 2010.)
[9]	陈家祥．炼钢常用图表数据手册2版[D]．北京：冶金工业出版社，2010. (CHEN Jiang-xiang. Chart data in Steelmaking.2nd Ed [D]. Beijing: Metallurgical Industry Press, 2010.)
[10]	梁英教，车荫昌．无机物热力学数据手册．沈阳：东北大学出版社，1993. (LIANG Ying-jiao. CHE Yin-chang. Datasheet of inorganic thermodynamics [D]. Shenyang: Northeast university press, 1993.)
[10]	梁英教，车荫昌．无机物热力学数据手册．沈阳：东北大学出版社，1993. (LIANG Ying-jiao. CHE Yin-chang. Datasheet of inorganic thermodynamics [D]. Shenyang: Northeast university press, 1993.)
[11]	Ban-yS a，Hino M，Stao A, et al. O, P and S Distribution equilibria between Iron and CaO-Al2O3-FetO slag saturated with CaO[J]．Tetsu-to-Hagane，1991，77：361.
[11]	Ban-yS a，Hino M，Stao A, et al. O, P and S Distribution equilibria between Iron and CaO-Al2O3-FetO slag saturated with CaO[J]．Tetsu-to-Hagane，1991，77：361.
[12]	Wagner C．The concept of the basicity of slags [J]．Metallurgical and Materials Transactions B，1975，6(3)：405.
[12]	Wagner C．The concept of the basicity of slags [J]．Metallurgical and Materials Transactions B，1975，6(3)：405.
[13]	Young R W，Duffy J A，Hassall G J, et al．Use of the optical basicity concept for determining phosphorus and sulphur slag/metal Partitions [J]．Ironmaking and steelmaking，1992，19(3)：201.
[13]	Young R W，Duffy J A，Hassall G J, et al．Use of the optical basicity concept for determining phosphorus and sulphur slag/metal Partitions [J]．Ironmaking and steelmaking，1992，19(3)：201.
[14]	Yang X M，Liu T Z，Guo Z C，et al．Study on the correlation between phosphate capacity index and slag basicity [J]．Chinese Journal of Process Engineering，1995，16(3)：194.
[14]	Yang X M，Liu T Z，Guo Z C，et al．Study on the correlation between phosphate capacity index and slag basicity [J]．Chinese Journal of Process Engineering，1995，16(3)：194.
[15]	Yang X M，Guo Z C，Wang D G，et al．Investigation on the correlation between sulfide capacity and phosphate capacity of metallurgical slag [J]．Iron and Steel，1996，31(Suppl 1)：25.
[15]	Yang X M，Guo Z C，Wang D G，et al．Investigation on the correlation between sulfide capacity and phosphate capacity of metallurgical slag [J]．Iron and Steel，1996，31(Suppl 1)：25.
[16]	Yang X M，Shi C B，Zhang M，et al．A thermodynamic model of phosphate capacity for CaO-SiO2-MgO-FeO-Fe2O3 -MnO-Al2O3-P2O5 slags equilibrated with molten steel during a top-bottom combined blown converter steelmaking process based on the ion and molecule coexistence theory [J]．Metallurgical and Materials Transactions B，2011，42B(5)：951.
[16]	Yang X M，Shi C B，Zhang M，et al．A thermodynamic model of phosphate capacity for CaO-SiO2-MgO-FeO-Fe2O3 -MnO-Al2O3-P2O5 slags equilibrated with molten steel during a top-bottom combined blown converter steelmaking process based on the ion and molecule coexistence theory [J]．Metallurgical and Materials Transactions B，2011，42B(5)：951.
[17]	李晋岩，张盟，柴国明，等．CaO-FeO-Fe2O3-Al2O3-P2O5炉渣的磷酸盐容量预测模型．太原：第十七届（2013年）全国冶金反应工程学学术会议论文集(下册) [C]，2013，804. (LI Jin-yan, ZHANG Meng, CHAI Guo-ming, et al. Prediction model of phosphate capacity for CaO-FeO-Fe2O3-Al2O3-P2O5 slags // The 17th (2013) National Conference on Metallurgical Reaction Engineering (volume II) [C]. Taiyuan, 2013, 804.)
[17]	李晋岩，张盟，柴国明，等．CaO-FeO-Fe2O3-Al2O3-P2O5炉渣的磷酸盐容量预测模型．太原：第十七届（2013年）全国冶金反应工程学学术会议论文集(下册) [C]，2013，804. (LI Jin-yan, ZHANG Meng, CHAI Guo-ming, et al. Prediction model of phosphate capacity for CaO-FeO-Fe2O3-Al2O3-P2O5 slags // The 17th (2013) National Conference on Metallurgical Reaction Engineering (volume II) [C]. Taiyuan, 2013, 804.)
[18]	王新华．钢铁冶金学—炼钢学 [D]．北京：高等教育出版社，2007. (WANG Xin-hua. Ferrous Metallurgy-Steelmaking [D]. Beijing: Higher Education Press, 2007.)
[18]	王新华．钢铁冶金学—炼钢学 [D]．北京：高等教育出版社，2007. (WANG Xin-hua. Ferrous Metallurgy-Steelmaking [D]. Beijing: Higher Education Press, 2007.)
[19]	Farshid Pahlevani，Shin-ya Kitamur， Hiroyuki Shibata，et al．Distribution of P2O5 between solid solution of 2CaO·SiO2 -3CaO·P2O5 and liquid phase [J]．ISIJ International，2010，50 (6)：822
[19]	Farshid Pahlevani，Shin-ya Kitamur， Hiroyuki Shibata，et al．Distribution of P2O5 between solid solution of 2CaO·SiO2 -3CaO·P2O5 and liquid phase [J]．ISIJ International，2010，50 (6)：822
[20]	刁江．Al2O3和Na2O对高磷铁水脱磷的影响 [J]．钢铁研究学报，2013，25(2)：9. (DIAO Jiang. Effect of Al2O3 and Na2O on dephosphorization of high phosphorus hot metal [J]. Journal of Iron and Steel Research, 2013，25(2)：9.)
[20]	刁江．Al2O3和Na2O对高磷铁水脱磷的影响 [J]．钢铁研究学报，2013，25(2)：9. (DIAO Jiang. Effect of Al2O3 and Na2O on dephosphorization of high phosphorus hot metal [J]. Journal of Iron and Steel Research, 2013，25(2)：9.)
[21]	B Deo，J Halder，B Snoeijer，et al．Effect of MgO and Al2O3 variations in oxygen steelmaking (BOF) slag on slag morphology and phosphorus distribution [J]．Ironmaking and Steelmaking，2005，32(1)：54.
[21]	B Deo，J Halder，B Snoeijer，et al．Effect of MgO and Al2O3 variations in oxygen steelmaking (BOF) slag on slag morphology and phosphorus distribution [J]．Ironmaking and Steelmaking，2005，32(1)：54.
[22]	林路，包艳平，王敏，等．二氧化钛改质对含磷转炉渣中磷富集行为的影响 [J]．北京科技大学学报，2014，36(8)：1013. (LIN Lu, BAO Yan-ping, WANG Min, et al. Influence of titania modification on phosphorus enrichment in P-bearing steel-making slag [J]. Journal of University of Science and Technology Beijing, 2014，36(8)：1013.)
[22]	林路，包艳平，王敏，等．二氧化钛改质对含磷转炉渣中磷富集行为的影响 [J]．北京科技大学学报，2014，36(8)：1013. (LIN Lu, BAO Yan-ping, WANG Min, et al. Influence of titania modification on phosphorus enrichment in P-bearing steel-making slag [J]. Journal of University of Science and Technology Beijing, 2014，36(8)：1013.)
[23]	李显鹏，高金涛，张延玲，等．CaO-FeO-SiO2-Al2O3/Na2O/TiO2渣系与碳饱和铁水间磷分配行为．钢铁，2017，52(2)：18. （LI Xian-peng, GAO Jin-tao, ZHANG Yan-ling, et al. Distribution behavior of phosphorus between CaO-FeO-SiO2-Al2O3 /Na2O/TiO2 slags and carbon-saturated iron [J]. Iron and Steel, 2017，52(2)：18.）
[23]	李显鹏，高金涛，张延玲，等．CaO-FeO-SiO2-Al2O3/Na2O/TiO2渣系与碳饱和铁水间磷分配行为．钢铁，2017，52(2)：18. （LI Xian-peng, GAO Jin-tao, ZHANG Yan-ling, et al. Distribution behavior of phosphorus between CaO-FeO-SiO2-Al2O3 /Na2O/TiO2 slags and carbon-saturated iron [J]. Iron and Steel, 2017，52(2)：18.）
[24]	张淑会．CaO-SiO2-Al2O3-MgO-FeO 五元渣系热力学性能的研究[D]．唐山：河北理工大学，2003. (ZHANG Shu-hui. Study on thermodynamics poroperty of CaO-SiO2-Al2O3-MgO-FeO slags [D]. Tangshan: Hebei University of Technology, 2003.)
[24]	张淑会．CaO-SiO2-Al2O3-MgO-FeO 五元渣系热力学性能的研究[D]．唐山：河北理工大学，2003. (ZHANG Shu-hui. Study on thermodynamics poroperty of CaO-SiO2-Al2O3-MgO-FeO slags [D]. Tangshan: Hebei University of Technology, 2003.)
[25]	赵丽树．CaO-SiO2-Al2O3-MgO-FetO渣系热力学性能的研究[D]．沈阳：东北大学，2012. (Zhao L S. Study on Thermodynamic properties of CaO-SiO2-Al2O3-MgO-FetO slags [D]. Shenyang: Northeastern University, 2012.)
[25]	赵丽树．CaO-SiO2-Al2O3-MgO-FetO渣系热力学性能的研究[D]．沈阳：东北大学，2012. (Zhao L S. Study on Thermodynamic properties of CaO-SiO2-Al2O3-MgO-FetO slags [D]. Shenyang: Northeastern University, 2012.)
[26]	Lee C. M，Fruehan R. J．Phosphorus equilibrium between hot metal and slag [D]．Ironmaking and Steelmaking，2013，32(6)：503.
[26]	Lee C. M，Fruehan R. J．Phosphorus equilibrium between hot metal and slag [D]．Ironmaking and Steelmaking，2013，32(6)：503.