Influence factors of fluidity characteristic number of iron ore powder |
FU Zhong-wang1,MO Chao-xing2,CHEN Xiao-min1,ZHAO Yong1,3,YUCHI He-peng1,WU Keng1 |
(1. State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China 2. Guangxi Liuzhou Iron and Steel Group Co., Ltd., Liuzhou 545002, Guangxi, China 3. Technology Institute of Shougang Group Co., Ltd., Beijing 100041, China) |
|
|
Abstract In order to determine the rule of liquid phase fluidity of iron ore fines, the fluidity characteristic number was used to characterize the fluidity of the liquid sintering phase. The characteristic number consists of kinds of important process information, including the actual temperature of the sintering production. Consequently, the characteristic number can be used to distinguish the fluidities among different iron ore powders objectively and accurately. By changing the chemical composition of the iron ore powder, the influence of the non-iron containing oxide on the fluidity characteristic number was investigated. The results show that with the increasing of the mass percent of SiO2, Al2O3 and MgO in iron ore powders, the flow temperature of the liquid increases gradually, the flow rate decreases gradually, and the fluidity characteristics number decreases in different levels. Therefore, the mass percent of the three compositions, SiO2, Al2O3 and MgO, should be controlled within a certain range. The effect of carbon on the fluidity characteristic number of iron ore on the type of the iron oxide in ore powder.
|
Received: 12 April 2018
Published: 24 December 2018
|
|
|
|
|
[1] |
WANG Chang,,YU Yang,,WANG Lin,,GUO Zi- feng,,L Bao- feng,WU Nai. Influence of chemical composition on surface quality of thin hot rolled pickled sheet[J]. , 2019, 31(1): 83-88. |
[2] |
BAO Wen-quan,XU Qiang,HAN Feng-jun,NIU Wei,MA Jun-jie. Reason analysis and improvement on the unqualified property of precipitation hardening steel 0Cr17Ni7Al[J]. Chinese Journal of Iron and Steel, 2017, 35(1): 14-16. |
[3] |
ZHU Li,,WU Keng,SHEN Wei,DU Rui- ling,YU Ying- chang,ZHAO Yong,. A new characterization method for the liquid phase fluidity of iron ore powder during sintering[J]. Chinese Journal of Iron and Steel, 2016, 28(6): 13-18. |
[4] |
SONG Li- na,,LAN Peng,,LIU Chun- xiu,,DU Chen- wei,,ZHANG Jia- quan,. Research situation of medium manganese steel for 3rd generation automobile sheet[J]. Chinese Journal of Iron and Steel, 2015, 27(7): 1-8. |
[5] |
JIA Shu-jun,GAO Hong-gang,LIU Ming-hui,LIU Qing-you. Composition Optimization of Cold-Rolled TRIP590 Steel[J]. Iron and Steel, 2013, 48(4): 64-69. |
[6] |
LI Meng,MA Jun-tao. Experimental Study of Producing As-Cast High Strength and Toughness Ductile Iron With Low-Mg-Nodulizer[J]. Chinese Journal of Iron and Steel, 2013, 25(11): 19-22. |
|
|
|
|