| Development trend and challenge of advanced high strength automobile steels |
| WANG Cun-yu1， YANG Jie2， CHANG Ying3， CAO Wen-quan1， DONG Han1，4 |
| （1. Institute for Special Steels,Central Iron and Steel Research Institute,Beijing 100081,China;2. China Auto Lightweight Technology Innovation Strategic Alliance,Society of Automotive Engineers of China,Beijing 100055，China;3. School of Automotive Engineering,Dalian University of Technology,Dalian 116024,Liaoning,China;4. School of Material Science and Engineering， Shanghai University， Shanghai 200444， China） |
|
|
|
|
Abstract High strength steel is still the main material of automobiles，and has certain advantages and potentials in light weight，energy saving，emission reduction and cost for automobiles. The use ratio of high strength steel increases year by year and develops towards higher strength. Lower cost are important developing trend，the low cost production modes mainly reflected in hot rolling instead of cold rolling to produce sheet steel，and cold forming instead of hot stamping to produce ultra-high strength automobile parts，and so on. The third generation automobile steel，which relies on the metastable austenite enhancing strength and ductility，has become important development trends of advanced high strength steel. The development of advanced automobile steels bring new challenges to the material science，processing and equipment.
|
|
Received: 12 July 2018
Published: 15 February 2019
|
|
|
|
| [1]中国汽车工程学会，中国汽车轻量化技术创新战略联盟，中国第一汽车股份有限公司技术中心.中国汽车轻量化发展战略与途径[M]. 北京理工大学出版社2015年9月：140-166 [2]Stacy C.Davis, Susan E. Williams, Robert G. Boundy, et.al. 2016 VEHICLE TECHNOLOGIES MARKET REPORT[R].OAK Ridge National Laboratory, 2017 [3]Sruart Keeler, Sc.D, Menachem Kimchi, M. Sc. Advanced high-strength steels application guidelines version 5.0 [R]. world autosteel, 2014.5 [4]韩维建, 张瑞杰, 郑江.汽车材料及轻量化趋势[M], 机械工业出版社, 2017:27-28 [5]陈鹰.轻量化评估方法研究与高性能汽车钢冲压件技术开发[D]. 钢铁研究总院博士学位论文，2017，北京 [6].节能与新能源汽车技术路线图战略咨询委员会，中国汽车工程学会 编，节能与新能源汽车技术路线图[M]， 机械工业出版社，2016 [7]毛新平, 高吉祥, 柴毅忠.中国薄板坯连铸连轧技术的发展[J].钢铁, 2014, 49(7):49-60 [8]肖丽俊, 岳尔斌, 仇圣桃, 等.双辊薄带连铸生产取向硅钢的技术分析[J], [J].钢铁研究学报,, 2009, , 21((8)):1-4 [9]董瀚, 干勇, 翁宇庆, 等.高效率低能耗高质量的钢板温成形零件及其生产方法[P]. 中国: ZL 201110041545.3, 2012-11-14 [10]Cunyu Wang，Xiaodong Li，Shuo Han, et al.Warm stamping technology of the medium manganese steel[J],[J].steel research international, , :- [11]Kuvin B.Steelmaking and Steels, Getting Better and Better all the Time [J].[J].Metalforming, 2008, (2):7- [12]Matlock DK, Br?utigam VE, Speer JG.Application of the quenching and partitioning (Q&P) process to a medium-carbon,high-Si microalloyed bar steel[J].Mater. Sci. Forum, 2003, 426-432(2):1089-1094 [13]董瀚, 王毛球, 翁宇庆.高性能钢的组织调控理论与技术[J].钢铁, 2010, 45(7):1-7 [14]王存宇.30GPa%级超高强度马奥组织钢的研究[D]. 博士学位论文, 钢铁研究总院, 2010 [15]王存宇, 时捷, 曹文全, 等.工艺处理低碳钢马氏体的研究[J].金属学报, 2011, 47(6):720-726 [16]CY. Wang, J. Shi, W. Q. Cao, et al. .Microstructure Characterization of Low Alloy Martenstic Steel Processed by Quenching and Partitioning[J].[J]. Materials Science & Engineering A,, 2010, (527): :3442-3449 [17]WQ. Cao. C. Wang. J. Shi.et al..Microstructure and mechanical properties of Fe-0.2C-5Mn steel processed by ART-annealing[J]. [J].Materials Science and Engineering A, , 2011, (528):: 6661-6666 [18]Jie Shi, Xinjun Sun, Maoqiu Wang, et al.Enhanced work-hardening behavior and mechanical properties in ultrafine-grained steels with large-fractioned metastable austenite[J]. [J].Scripta Materialia, 2010, ((63)):815-818 [19]Cunyu Wang, Ying Chang, Jie Yang, et al.Work hardening behavior and stability of retained austenite for quenched and partitioned steels[J].Journal of iron and steel research, 2016, 23(2):130-137 [20]王存宇, 曹文全, 董瀚.中锰第三代汽车钢及其先进性[C]//第十一届中国钢铁年会论文集. 北京: 中国金属学会, 2017: 1648-1652 [21]董瀚.钢铁材料基础研究的评述[J].钢铁, 2008, 43(10):1-7 |
| [1] |
LIU Si-han, WANG Cun-yu, XU Hai-feng, CAO Wen-quan. Superplasticity and microstructure evaluation of cold rolled medium manganese steels[J]. Iron and Steel, 2020, 55(9): 97-103. |
| [2] |
LIU Zong-hui, QIN Feng-ting, REN Jian-zhong, ZHU Miao-yong. Effect of two-step slag making refining on sulfur and aluminum in C82DA steel[J]. Iron and Steel, 2020, 55(7): 78-84. |
| [3] |
CHEN Ming-xin1,YANG Xiao-jiang2,MENG Qing-yong2. Study on high temperature thermoplasticity of medium manganese steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 519-524. |
| [4] |
. [J]. , 2020, 45(6): 21-33. |
| [5] |
ZHAO Zhengzhi1,2,3,CHEN Weijian1,2,3,GAO Pengfei1,2,3,KANG Tao1,2,ZHAO Yan1,2,TANG Di1,3. Progress and perspective of advanced high strength automotive steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(12): 1059-1076. |
| [6] |
ZHOU Song-bo1,HU Feng1,WU Ya-jie1,WAN Xiang-liang1,WU Kai-ming1,XIE Xing2. Effect of austenite structure on cold bending properties of low carbon medium manganese steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(11): 990-999. |
|
|
|
|
2019, Vol. 54 