Effect of secondary cold rolling reduction rate on microstructure and properties of tinplate |
FANG Yuan1,2, MO Zhi-ying3, SUN Chao-fan1, WU Zhi-guo1, LIU Wei3, SONG Hao1 |
1. Research Institute of Technology, Shougang Group Co., Ltd., Beijing 100043, China; 2. Beijing Key Laboratory of Green Recyclable Process for Iron and steel Production Technology, Beijing 100043, China; 3. Tinplate Department, Shougang Jingtang United Iron and Steel Co., Ltd., Tangshan 063200, Hebei, China) |
|
|
Abstract In order to develop secondary cold-rolled tinplate,effects of the secondary cold rolling reduction on the microstructure and properties of the tinplate were studied by the hardness tester,tensile tester,optical microscope,transmission electron microscope and X-ray diffractometer. The results showed that as the secondary cold rolling reduction rate increasing,the hardness and strength of the test steel increased,the anisotropy increases,and the elongation decreased. When the secondary cold rolling reduction rate was 20%,the higher hardness and elongation match could be reached. At the same time,the secondary cold rolling reduction had a significant influence on the texture. When the secondary cold rolling reduction rate was between 20% and 40%,the highest orientation density in the α-orientation line appeared between {223}〈110〉 and {445}〈110〉,which could reach 6.2. And with the secondary cold rolling reduction rate increasing,the {111}〈110〉 orientation density in the γ-oriented line gradually decreased from 3.1 to 2.7,and the {111}〈112〉 orientation density gradually increased from 4.9 to 5.3.
|
Received: 26 June 2018
Published: 15 February 2019
|
|
|
|
[1] |
周其良, 译.镀锡板指南[M].北京:冶金工业出版社,1989:4-7.
|
[1] |
周其良, 译.镀锡板指南[M].北京:冶金工业出版社,1989:4-7.
|
[2] |
MichaeI C.Tin PIate[J].PIating and Surface Finishing, 1998, 85(11):66-67
|
[2] |
MichaeI C.Tin PIate[J].PIating and Surface Finishing, 1998, 85(11):66-67
|
[3] |
郑菊华,胡忠举,龙东平.二次冷轧压下率对带钢力学性能与织构的影响[J].材料导报:研究篇, 2016, 30(8):95-99
|
[3] |
郑菊华,胡忠举,龙东平.二次冷轧压下率对带钢力学性能与织构的影响[J].材料导报:研究篇, 2016, 30(8):95-99
|
[4] |
张功庭,郑之旺,王敏莉.冷轧压下率对退火含铌钛钢性能及织构的影响[J].机械工程材料, 2014, 38(7):29-32
|
[4] |
张功庭,郑之旺,王敏莉.冷轧压下率对退火含铌钛钢性能及织构的影响[J].机械工程材料, 2014, 38(7):29-32
|
[5] |
董浩,赵宇,喻晓军,等.二次冷轧压下率对无取向电工钢薄带磁性能和织构的影响[J].钢铁, 2008, 43(5):80-83
|
[5] |
董浩,赵宇,喻晓军,等.二次冷轧压下率对无取向电工钢薄带磁性能和织构的影响[J].钢铁, 2008, 43(5):80-83
|
[6] |
方圆,吴志国,孙超凡,等.工艺参数对二次冷轧镀锡板组织性能的影响[C].第十一届中国钢铁年会论文集,2017:1042-1045.
|
[6] |
方圆,吴志国,孙超凡,等.工艺参数对二次冷轧镀锡板组织性能的影响[C].第十一届中国钢铁年会论文集,2017:1042-1045.
|
[7] |
Guan Xiaojun etal.A Study on Optimization Process-ing Parameters for Extra Low-Carbon Hihg Strength Steel Sheet with Bake-Hardenability[C].Proc. of the 4th ICTP,Beijing,China,1993:1861-1866.
|
[7] |
Guan Xiaojun etal.A Study on Optimization Process-ing Parameters for Extra Low-Carbon Hihg Strength Steel Sheet with Bake-Hardenability[C].Proc. of the 4th ICTP,Beijing,China,1993:1861-1866.
|
[8] |
王昭东,李自刚,何晓明,等.冷轧压下量对铁素体区热轧-钢冷轧板的再结晶织构特点和深冲性能的影响[J].金属学报, 2000, 36(6):613-617
|
[8] |
王昭东,李自刚,何晓明,等.冷轧压下量对铁素体区热轧-钢冷轧板的再结晶织构特点和深冲性能的影响[J].金属学报, 2000, 36(6):613-617
|
[9] |
李一鸣,任慧平,金自力,等.工艺不同冷轧压下率低碳钢板退火织构的演变[J].内蒙古科技大学学报, 2009, 28(1):72-75
|
[9] |
李一鸣,任慧平,金自力,等.工艺不同冷轧压下率低碳钢板退火织构的演变[J].内蒙古科技大学学报, 2009, 28(1):72-75
|
[10] |
关小军,王先进,凤佩华,等.超低碳高强度BH钢板的织构发展[J].钢铁研究, 1995, (5):22-25
|
[10] |
关小军,王先进,凤佩华,等.超低碳高强度BH钢板的织构发展[J].钢铁研究, 1995, (5):22-25
|
[1] |
DU Liang, HAN Xiu-li, ZHANG Quan-sheng, ZHOU Xiang, YANG Hong-da, WANG Ying. Quantitative relation between mineralogical structure and metallurgical properties of sinter of import iron ore[J]. Iron and Steel, 2020, 55(6): 38-45. |
[2] |
QIAN Cheng, ZHANG Jia-sheng, BAI Zhen-hua, CUI Ya-ya, HUA Chang-chun, CHEN Shu-zong. Oil film thickness model of roll surface and its influencing factors during double cold rolling[J]. Iron and Steel, 2020, 55(6): 68-74. |
[3] |
SUN Chao-fan, FANG Yuan, WANG Ya-qing, LIU Wei. Influence of temper rolling reduction rate on microstructure and mechanical properties of TS290 steel[J]. Iron and Steel, 2020, 55(6): 75-79. |
[4] |
WEI Tong-yu, ZOU De-ning, ZHANG Ying-bo, CHEN Wan-wan. Effect of aluminum on microstructure and properties of high alumina ferritic heat resistant steel[J]. Iron and Steel, 2020, 55(6): 80-83. |
[5] |
JIANG Yue-yue, WANG Zhao-dong, DENG Xiang-tao. Effect of trace rare earth Ce on martensitic transformation behavior of ultra-high strength low alloy steel[J]. Iron and Steel, 2020, 55(6): 84-90. |
[6] |
WU Zhi-guang, GONG Xue-ting, LI Xin, ZHAO Ji-qing, GONG Zhi-hua. Effect of heat treatment process on creep-rupture property of 20Cr1Mo1VTiB bolt steel[J]. Iron and Steel, 2020, 55(6): 101-106. |
|
|
|
|