Effect of isothermal time on microstructures and mechanical properties in hot rolled TRIP steels with low Si and more Al |
WANG Xiao-hui, KANG Jian, LI Zhen-lei, LI Yun-jie, YUAN Guo, WANG Guo-dong |
(State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, Liaoning, China) |
|
|
Abstract In order to achieve the industrial application of hot rolled TRIP steels with low Si and more Al,hot rolled TRIP steels with low Si and more Al were set as studied object using scanning electron microscopy,transmission electron microscopy,tensile test and X-ray diffraction to study the effect of different isothermal time on microstructures and mechanical properties of experimental steels. The results show that the microstructures of experimental steels consist of polygonal ferrite,bainite ferrite and retained austenite. With isothermal time increasing,the volume percent of laminar bainite increases,while the volume percent of granular bainite decreases. When isothermal time is 20 min,the comprehensive mechanical properties of experimental steels reach the best,and the tensile strength,the total elongation and the strength ductility balance is 732.25 MPa,36% and 26.36 GPa·%,respectively. The volume percent and carbon concentration of retained austenite initially increases and then decreases,and the experimental steels exhibit excellent work hardening behaviour with isothermal time 20 min.
|
Received: 25 September 2018
Published: 09 May 2019
|
|
|
|
[1] |
WEI Tong-yu, ZOU De-ning, ZHANG Ying-bo, CHEN Wan-wan. Effect of aluminum on microstructure and properties of high alumina ferritic heat resistant steel[J]. Iron and Steel, 2020, 55(6): 80-83. |
[2] |
ZHAO Yun-peng, YU Chao, XIAO Hong, WU Zong-he, XU Peng-peng, XIE Hong-biao. Effect of pure iron interlayer on mechanical properties of hot rolled stainless steel clad plate[J]. Iron and Steel, 2020, 55(5): 73-79. |
[3] |
SHAO Cheng-wei, WANG Jun-tao, ZHAO Xiao-li, HUI Wei-jun. Microstructure and mechanical properties of intercritically annealed Al-contain medium Mn steel[J]. Iron and Steel, 2020, 55(5): 87-93. |
[4] |
CAO Jing-hua1,PAN Hong-bo2,3,ZHANG Jing1,ZHANG Teng-fei2,LI Xu-dong2,LIU Wei-ming2,3. Continuous cooling transformation of NbTi microcarbon deep drawing dualphase steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 322-328. |
[5] |
WANG Ji-hong, ZHANG Li-na, CHEN De-li, QI Yue, CAO Li-hong. Discussion about heat treatment process of X20Cr13 blade steel for gas turbine[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 18-. |
[6] |
XING Xian-qiang, CAO Wen-quan, WANG Cun-yu. Bond structure of 55SiCr steel used for coil springs of automotive suspension system[J]. Iron and Steel, 2020, 55(3): 68-73. |
|
|
|
|