Grain coarsening behavior of high temperature carburizing gear steels |
ZHANG Guo-qiang, HE Xiao-fei, YU Wen-chao, SHI Jie, WANG Mao-qiu |
(Institute of Special Steels, Central Iron and Steel Research Institute, Beijing 100081, China) |
|
|
Abstract In order to develop gear steel for carburizing at high temperature of 980 ℃,austenite grain coarsening of case hardening steel 18Cr2Ni2Mo with the addition of niobium in contents of 0,0.036%,0.060% and 0.100% was investigated by means of pseudo-carburizing at 930 and 980 ℃. Results show that the grain size of tested steel austenitizing at 930 and 980 ℃ can be significantly refined by niobium addition due to the pinning effect of NbC precipitates,and with the increase of niobium mass percent in steel,grain coarsening at high temperature of 980 ℃ can be evidently hindered. After austenitizing at 980 ℃ for 20 h,the average grain size of the 18Cr2Ni2Mo gear steel with 0.100% Nb addition is still about 26 μm,so the steel can be used for carburizing at high temperature of 980 ℃.
|
Received: 29 September 2018
Published: 09 May 2019
|
|
|
|
[1] |
CAO Yan-guang, LI Zhao-dong, DING Can-can, ZHANG Jin-wen, YONG Qi-long, GAO Jian-bing. Effect of niobium addition on hardenability of high-speed railway axle steel[J]. Iron and Steel, 2020, 55(6): 107-112. |
[2] |
LI Lan-xin1,WANG Min1,JUAN Rong-fei1,BAO Yan-ping1,YANG Jin2. Distribution characteristics of oxides and sulfide inclusions in key areas of gear steel forgings[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 370-376. |
[3] |
CAO Yun-fei, YU Wei, LIU Min, JIANG Rui, WANG Chun. Austenite grain growth model of 38MnSiVS bearing microalloyed forging steel[J]. Iron and Steel, 2020, 55(5): 103-108. |
[4] |
XIAO Da-heng, TANG Wei, LUO Deng, WANG Zhen, XIE Zhen-jia, SHANG Cheng-jia. Microstructure and properties of low temperature steel for ultra large liquefied petroleum gas carrier[J]. Iron and Steel, 2020, 55(4): 82-87. |
[5] |
. Study on NbC Precipitate of Nb Microalloying Mid-carbon Steel[J]. , 2020, 45(3): 0-0. |
[6] |
LIN Peng,ZHANG Hong-cai,LIU Ying,XU Zheng-zhou. Cause analysis of surface crack defects of gear steel 20CrNiMo rolled product[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(2): 40-. |
|
|
|
|