Volatilization mechanism of ESR slag with high #br# fluoride under hightemperature |
ZHAO Junxue,LU Liang,ZHAO Zhongyu,WANG Ze,CUI Yaru,LI Xiaoming |
(School of Metallurgical Engineering,Xi′an University of Architecture and Technology,
Xi′an 710055, Shaanxi, China) |
|
|
Abstract In order to explore the volatilization mechanism of the ESR slag component under hightemperatures,the hightemperature volatilization mechanism of slag is studied based on the CaF2CaOSiO2Al2O3MgO slag system for the Electroslag remelting (ESR) slag with a high fluoride. Using the calculation of FactSage software, thermogravimetric (TG) experiments and mass spectrometry (MS) analyses under a high temperature, combined with hightemperature roasting experiments, XRF analyses, SEM phase observations, the results have indicated: CaF2 reacts with SiO2 and MgO to form SiF4 and MgF2 gas between 550800 ℃; CaF2 reacts with MgO to form MgF2 gas and reacts with a small amount of Al2O3 to form AlF3 gas between 8001 200 ℃; the volatile is mainly CaF2 with a small amount of AlF3 in the range of 1 2001 500 ℃. The crystal is mainly calcium dialuminate and a small amount of cuspidine in the high temperature region (1 0001 400 ℃), and when the temperature is increased to 1 500 ℃, the crystal is mainly cuspidine. The purpose is to explore the volatilization mechanism of the ESR slag component under hightemperatures which has reference value of the optimization of the ESR slag preparation process.
|
|
|
|
|
[1] |
ZHAO Zhong-yu, ZHAO Jun-xue, TAN Ze-xin, LU Liang, CUI Ya-ru, LI Xiao-ming. Determination and analysis of CaF2-Al2O3 binary phase diagram based on volatilization effect[J]. Iron and Steel, 2020, 55(4): 34-39. |
[2] |
LIN Jie, YANG Cheng, WANG Yuanming, MOU Fenyun, HOU Dong, WANG Deyong. Deoxidation thermodynamics in electroslag remelting process[J]. Iron and Steel, 2019, 54(9): 44-49. |
[3] |
YIN Bin, LI Wan-ming, WU Shao-peng, ZANG Xi-min, YU Hao-cen. Thermodynamic analysis of Al and Ti element loss in electroslag remelting Inconel718 superalloy[J]. Iron and Steel, 2019, 54(5): 86-94. |
[4] |
ZHAO Jun-xue,SHANG Nan,ZHAO Zhong-yu,SHI Rui-meng,LU Liang, WANG Ze. Influence of slag preparation mode on melting point of ESR slag with medium fluoride content[J]. Iron and Steel, 2018, 53(8): 44-48. |
[5] |
XING Bao-fu,GUO Ren-hui,YANG Song,FENG Tao,ZHANG Xiao-lei. Control of Al and Ti content of electroslag remelting of GH4033 alloy in the protection atmosphere[J]. , 2018, 36(5): 57-61. |
[6] |
CHE Xiao-jian,,YANG Mao-sheng,TANG Hai-yan,LI Jian-xin, PANG Xue-dong,SUN Yong. Inclusion control and fatigue performance in high performance GCr15 bearing steel[J]. Iron and Steel, 2018, 53(5): 76-85. |
|
|
|
|