Evolution and control of inclusions in aluminumcontaining on #br# oriented electrical steel through CSP process |
XIAO Zunhu1,SUI Yafei2,LIU Peng2,XU Gangjun2,LI Ciying2 |
(1. Company Office, Hunan Valin Lianyuan Iron and Steel Co., Ltd., Loudi 417000, Hunan, China;
2. Technology Center, Hunan Valin Lianyuan Iron and Steel Co., Ltd., Loudi 417000, Hunan, China) |
|
|
Abstract In order to control inclusions in electrical steel under CSP process better,the evolution mechanism of inclusions in the aluminumcontaining electrical steel during the RH refiningcontinuous castinghot rolling in the CSP line of Lianyuan Steel Company were investigated. The inclusions in the liquid steel are mainly Al2O3, Al2O3SiO2 and Al2O3CaOCaS after the RH alloying. The inclusions in the liquid steel are composed of most of Al2O3CaOCaS and a small amount of Al2O3 and CaS at RH outgoing and in tundish. The main measure to reduce inclusions in the molten steel is to reduce the oxidation of the top slag before the RH outlet. The main inclusions in hot rolled coil are AlN and MnS. The total amount of inclusions is positively correlated with the content of nitrogen and sulfur, and the effect of nitrogen is the most significant.
|
|
|
|
|
[1] |
HOU Xin-mei, LIU Yun-song, WANG En-hui. Effect of ladle-lining refractory on non-metallic inclusions in steel[J]. Iron and Steel, 2020, 55(6): 15-24. |
[2] |
YU Hui-xiang, PAN Ming, YANG De-xin. Behavior of inclusions in ultra-low carbon IF steel during deoxidation and alloying process[J]. Iron and Steel, 2020, 55(6): 46-53. |
[3] |
NIU Kai-jun, YANG Wen, ZHANG Li-feng, CHU Yan-ping, ZHANG Hong-qi, GUO Zi-qiang. Thermodynamics and industrial practice of formation of inclusions during solidification of tire cord steels[J]. Iron and Steel, 2020, 55(6): 61-67. |
[4] |
LI Lan-xin1,WANG Min1,JUAN Rong-fei1,BAO Yan-ping1,YANG Jin2. Distribution characteristics of oxides and sulfide inclusions in key areas of gear steel forgings[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 370-376. |
[5] |
QIN Zheng-feng, XUE Zheng-liang, LI Jin-bo, LI Bo-si. Origin of large spherical or bar-shaped inclusions in calcium treated steel[J]. Iron and Steel, 2020, 55(5): 31-38. |
[6] |
WANG Yi, ZHANG Li-feng, REN Ying, REN Qiang. Mechanism of inclusion evolution during refining process of 37Mn5 steel production[J]. Iron and Steel, 2020, 55(5): 39-44. |
|
|
|
|