Effect of Y on inclusions characteristics and tensile #br# properties in EH36 shipbuilding steel |
ZHAO Mengjing1,2,WANG Feng1,2,XI Xiaojun1,2,YANG Shufeng1,2,LI Jingshe1,2 |
(1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing,
Beijing 100083, China;2. Beijing Key Laboratory of Special Melting and Preparation of
HighEnd Metal Materials, Beijing 100083, China) |
|
|
Abstract Adding rare earth Y into steel can modify inclusions effectively in steel,bringing the changes of tensile properties. In order to study the effect of different content of Y on inclusions modification and tensile properties in steel,EH36 shipbuilding steel was chosen to analyze the inclusions in origin steel and in test steel with different Y addition using scanning electron microscope (SEM) and energy dispersive spectroscope (EDS). Tensile properties were also explored and tested. The results showed that rare earth Y could modify effectively the inclusions. The origin strip of MnS inclusions or the composite manganese sulfide inclusions could be modified into the spherical inclusions which the core was YAlO and the outer ring was rare earth oxysulfide. For mechanical properties,the results showed that the tensile strength and yield strength of shipbuilding steel were improved significantly with the Y addition increasing. The sample with the Y addition of 0.055% had the best morphology of inclusions modification and better tensile strength and yield strength.
|
|
|
|
|
[1] |
HOU Xin-mei, LIU Yun-song, WANG En-hui. Effect of ladle-lining refractory on non-metallic inclusions in steel[J]. Iron and Steel, 2020, 55(6): 15-24. |
[2] |
YU Hui-xiang, PAN Ming, YANG De-xin. Behavior of inclusions in ultra-low carbon IF steel during deoxidation and alloying process[J]. Iron and Steel, 2020, 55(6): 46-53. |
[3] |
NIU Kai-jun, YANG Wen, ZHANG Li-feng, CHU Yan-ping, ZHANG Hong-qi, GUO Zi-qiang. Thermodynamics and industrial practice of formation of inclusions during solidification of tire cord steels[J]. Iron and Steel, 2020, 55(6): 61-67. |
[4] |
LI Lan-xin1,WANG Min1,JUAN Rong-fei1,BAO Yan-ping1,YANG Jin2. Distribution characteristics of oxides and sulfide inclusions in key areas of gear steel forgings[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 370-376. |
[5] |
QIN Zheng-feng, XUE Zheng-liang, LI Jin-bo, LI Bo-si. Origin of large spherical or bar-shaped inclusions in calcium treated steel[J]. Iron and Steel, 2020, 55(5): 31-38. |
[6] |
WANG Yi, ZHANG Li-feng, REN Ying, REN Qiang. Mechanism of inclusion evolution during refining process of 37Mn5 steel production[J]. Iron and Steel, 2020, 55(5): 39-44. |
|
|
|
|