Selection of calcium treatment technology of LF #br#
refining for different steel |
XIAO Zunhu1,LIU Peng2,XU Gangjun2,ZHOU Junjun2,SUI Yafei2 |
(1. Company Office,Hunan Valin Lianyuan Iron and Steel Co.,Ltd.,Loudi 417000, Hunan, China;
2. Technology Center,Hunan Valin Lianyuan Iron and Steel Co.,Ltd.,Loudi 417000, Hunan, China) |
|
|
Abstract In order to optimize LF refining calcium treatment process for different steels,the evolution mechanism of inclusions in high strength structural steel,low carbon structural steel,welded cylinder steel,wear resistant steel and high carbon steel during LF refining and calcium treatment was investigated. The results show that the longer the slagsteel reaction time,the more thorough the inclusion modified before calcium treatment. Before calcium treatment,Al2O3 is the main inclusion of welded cylinder steel,MgOAl2O3CaO composite is the main inclusion of high strength structural steel and low carbon structural steel,and Al2O3CaO inclusion with low melting point is the main inclusion of high carbon steel and wearresistant steel. The amount and the size of inclusions in molten steel can be increased in the process of calcium treatment. The key to control Al2O3SiO2MnO composite inclusions is to avoid SiMn alloying in the middle and late stages of LF refining. Considering all factors,it is suggested that the current amount of feeding calcium wire should be increased for welded cylinder steel,light calcium treatment process should be used for high strength structural steel and low carbon structural steel,and calcium treatment process should be cancelled for high carbon steel and wear resistant steel.
|
|
|
|
|
[1] |
LI Si-jun, DU Jin-ke, PENG Yong-xiang, LI Ping, HU Bin. Numerical simulation study on single-point unequilibrium casting for beam blank in Laiwu Iron and Steel Company[J]. CONTINUOUS CASTING, 2020, 45(3): 1-9. |
[2] |
ZHENG Yuan-shou. High speed production technology of 160 mm× 160 mm continuous casting in Sangang[J]. CONTINUOUS CASTING, 2020, 45(3): 10-13. |
[3] |
WANG Bingxing,ZHU Fuxian,WANG Chao,LOU Haonan,. Application of oxide metallurgy in high heat input welding steels[J]. Iron and Steel, 2019, 54(9): 12-21. |
[4] |
WANG Chengyong, MEN Dongpo, CHEN Peng, LI Ziwen. Nonlinear prediction model for caking index based on coal petrology[J]. Iron and Steel, 2019, 54(9): 22-26. |
[5] |
NIU Lele,LIU Zhengjian,ZHANG Jianliang,ZHANG Zongwang, WANG Yaozu,DU Chengbo. Effect of mineral composition of iron ore on metallurgical properties of sinter[J]. Iron and Steel, 2019, 54(9): 27-32. |
[6] |
LU Yanan,WU Shengli,WANG Laixin,KOU Mingyin. Analysis of chemical compositions of slag affecting #br#
desulphurization in hot metal of COREX process[J]. Iron and Steel, 2019, 54(9): 33-38. |
|
|
|
|