| Effect of graphite nodules on fracture of ductile cast iron #br#
under low temperature impact loading |
| ZHANG Xinning |
| (School of Mechanical Engineering， Liaoning Shihua University， Fushun 113001， Liaoning， China) |
|
|
|
|
Abstract In order to clarify the microscopic fracture mechanism of ductile cast iron used under low temperatures，the effect of graphite nodules on fracture evolution process under low temperature impact loading was studied，which was proposed to provide further development of low temperature ductile iron material and failure assessment. The impact fracture morphology was analysised by using SEM and confocal laser scanning microscope. The results of quantitative fractography indicate that both Sa and Rc/R0are decreased with temperature during the impact fracture process. The cracks initiate from the interface between nodular graphite and the matrix. Therefore，in the spheroidization process，attention should be paid to improving the microstructure of the interface between the graphite and the matrix.
|
|
|
|
|
|
| [1] |
LI Si-jun， DU Jin-ke， PENG Yong-xiang， LI Ping， HU Bin. Numerical simulation study on single-point unequilibrium casting for beam blank in Laiwu Iron and Steel Company[J]. CONTINUOUS CASTING, 2020, 45(3): 1-9. |
| [2] |
ZHENG Yuan-shou. High speed production technology of 160 mm× 160 mm continuous casting in Sangang[J]. CONTINUOUS CASTING, 2020, 45(3): 10-13. |
| [3] |
WANG Bingxing，ZHU Fuxian，WANG Chao，LOU Haonan，. Application of oxide metallurgy in high heat input welding steels[J]. Iron and Steel, 2019, 54(9): 12-21. |
| [4] |
WANG Chengyong, MEN Dongpo, CHEN Peng, LI Ziwen. Nonlinear prediction model for caking index based on coal petrology[J]. Iron and Steel, 2019, 54(9): 22-26. |
| [5] |
NIU Lele,LIU Zhengjian,ZHANG Jianliang,ZHANG Zongwang, WANG Yaozu,DU Chengbo. Effect of mineral composition of iron ore on metallurgical properties of sinter[J]. Iron and Steel, 2019, 54(9): 27-32. |
| [6] |
LU Yanan,WU Shengli,WANG Laixin,KOU Mingyin. Analysis of chemical compositions of slag affecting #br#
desulphurization in hot metal of COREX process[J]. Iron and Steel, 2019, 54(9): 33-38. |
|
|
|
|