镁改质对Y1Cr13易切削不锈钢中硫化物的影响

doi:10.13228/j.boyuan.issn0449-749x.20190296

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (2694 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to study the modification effect of magnesium on sulfides in Y1Cr13 free-cutting stainless steel,the distribution,morphology and precipitation conditions of sulfides in steel before and after adding magnesium are analyzed by metallographic microscope,Image-Pro Plus image analysis software,scanning electron microscope and FactSage thermodynamic software. The results showed that adding a finite amount of magnesium in the Y1Cr13 free-cutting stainless steel can change Al₂O₃ into fine dispersed Al₂O₃·MgO,and the typical sulfides MnS in steel will precipitate with it as the core at 1 448 ℃,those formed MnS-Al₂O₃·MgO composite inclusions have internal soft and external hard structure. This structure makes MnS not easy to deform during rolling,and keeps spherical or ellipsoid shape in rolled products,and with the mass percent of magnesium,the precipitation temperature range of Al₂O₃·MgO will be larger,the precipitation amount will be more,and the improvement of MnS morphology will be more obvious. The sulfide grade decreased from fine line 5.5 and coarse line 4.5 before modification to fine line 3.5 and coarse line 1.0 after modification,and with the increase of its mass percent,the grade further decreased to fine line 2.5 and coarse line 0.5,and the rolling yield increased from 70% to 90%. Therefore,appropriately increasing the amount of magnesium is beneficial to improve its modification effect.

Key words： magnesium modification Y1Cr13 free-cutting stainless steel sulfides

Received: 02 July 2019

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WU Xiang-yu
	HE Yu-dong
	WU Liang-ping
	SHEN Ping
	FU Jian-xun

Cite this article:

WU Xiang-yu,HE Yu-dong,WU Liang-ping等. Effect of magnesium modification on sulfides in Y1Cr13 free-cutting stainless steel[J]. Iron and Steel, 2020, 55(4): 68-74.

URL:

http://www.chinamet.cn/Jweb_gt/EN/10.13228/j.boyuan.issn0449-749x.20190296 OR http://www.chinamet.cn/Jweb_gt/EN/Y2020/V55/I4/68

[1] 林企曾,李成. 迅速发展的中国不锈钢工业[J]. 钢铁,2006,41(12):1. (LIN Qi-zeng,LI Cheng. Rapidly growing stainless steel industry in China[J]. Iron and Steel,2006,41(12):1.)
[2] WU H L,HUANG Y,HUANG Z,et al. Experimental research on the abrasive belt grinding turbine blades material 1Cr13 stainless steel[J]. Key Engineering Materials,2011,487(1):452.
[3] Cardoso P H S,Kwietniewski C,Porto J P,et al. The influence of delta ferrite in the AISI 416 stainless steel hot workability[J]. Materials Science and Engineering A,2003,351(1):1.
[4] 余音宏,潘涛,尹建成,等. S含量对高速车轮钢性能和夹杂物的影响[J]. 钢铁,2013,48(10):57.(YU Yin-hong,PAN Tao,YIN Jian-cheng,et al. Effect of sulfur contents on properties and inclusions in high speed wheel steels[J]. Iron and Steel,2013,48(10):57.)
[5] 申景霞,郑艳,张海霞,等. 含硫齿轮钢20CrMnTiH中硫化物对切削性能的影响[J]. 特殊钢,2012,33(3):47.(SHEN Jing-xia,ZHENG Yan,ZHANG Hai-xia,et al. Effect of sulfides on cutting characteristics of sulphur bearing gear steel 20CrMnTiH[J]. Special Steel,2012,33(3):47.)
[6] 段飞虎,朱荣,林腾昌,等. 氧含量对硫系易切削钢切削性能的影响[J]. 炼钢,2012,28(1):44.(DUAN Fei-hu,ZHU Rong,LIN Teng-chang,et al. Effect of oxygen content on cutting performance in sulfur free cutting steel[J]. Steelmaking,2012,28(1):44.)
[7] 张硕,杨树峰,李京社,等. 碲处理控制Y15易切削钢中MnS夹杂物形貌[J]. 钢铁,2017,52(9):27. (ZHANG Shuo,YANG Shu-feng,LI Jing-she,et al. Morphology of MnS inclusions in Y15 high sulfur free-cutting steel by tellurium treatment[J]. Iron and Steel,2017,52(9):27.)
[8] Domizzi G,Anteri G,Ovejero-Garcia J. Influence of sulphur content and inclusion distribution on the hydrogen induced blister cracking in pressure vessel and pipeline steels[J]. Corrosion Science,2001,43(2):325.
[9] 李艳梅,朱伏先,崔凤平,等. 中厚钢板分层缺陷的形成机制分析[J]. 东北大学学报:自然科学版,2007,28(7):1002.(LI Yan-mei,ZHU Fu-xian,CUI Feng-ping,et al. Analysis of forming mechanism of lamination defect of steel plate[J]. Journal of Northeastern University:Natural Science,2007,28(7):1002.)
[10] 李泰. 非调质钢F45MnVS热顶锻裂纹分析和改进工艺措施[J]. 特殊钢,2015,36(5):28.(LI Tai. Analysis on hot heading crack of non-quenched and tempered steel F45MnVS and improve measures of process[J]. Special Steel,2015,36(5):28.)
[11] 陈晓康,杨树峰,李京社. 含钇E36船板钢夹杂物改性[J]. 中国冶金,2019,29(12):25. (CHEN Xiao-kang,YANG Shu-feng,LI Jing-she. Inclusion modification of E36 shipbuilding steel containing yttrium[J]. China Metallurgy,2019,29(12):25.)
[12] 肖国华,董瀚,王毛球,等. 镁和镁钙处理对非调质钢中硫化物形态的影响[J]. 钢铁,2011,46(4):64.(XIAO Guo-hua,DONG Han,WANG Mao-qiu,et al. Effect of Mg/Ca-treatment on morphology of sulfide in non-quenched and tempered steel[J]. Iron and Steel,2011,46(4):64.)
[13] 田俊,王德永,屈天鹏,等. 钙、镁在含硫钢中硫化物变性过程中的作用[J]. 钢铁,2017,52(11):32.(TIAN Jun,WANG De-yong,QU Tian-peng,et al. Role and distinction of Ca and Mg to sulfide modification for sulfur steel[J]. Iron and Steel,2017,52(11):32.)
[14] 刘威,杨树峰,李京社,等. 钙镁复合处理20CrMnTi钢中硫化物夹杂[J]. 钢铁,2017,52(12):21.(LIU Wei,YANG Shu-feng,LI Jing-she,et al. Modification of sulphide inclusions in 20CrMnTi steel by calcium-magnesium treatment[J]. Iron and Steel,2017,52(12):21.)
[15] JIANG Z H,ZHUANG Y,LI Y,et al. Effect of modification treatment on inclusions in 430 stainless steel by Mg-Al alloys[J]. Journal of Iron and Steel Research,International,2013,20(5):6.
[16] ZHANG T,LIU C,JIANG M. Effect of Mg on behavior and particle size of inclusions in Al-Ti deoxidized molten steels[J]. Metallurgical and Materials Transactions B,2016,47(4):2253.
[17] ZHANG T S,WANG D Y,JIANG M F. Effect of magnesium on evolution of oxide and sulphide in liquid iron at 1 873 K[J]. Journal of Iron and Steel Research,International,2014,21(12):1073.
[18] 张学伟,杨才福,柴锋,等. 热力学分析MnS夹杂物析出与控制[J]. 钢铁,2019,54(12):27.(ZHANG Xue-wei,YANG Cai-fu,CHAI Feng,et al. Precipitation and control of MnS inclusions by thermodynamic analysis[J]. Iron and Steel,2019,54(12):27.)