Research on problem of "pseudo-bad flatness" at tail of hot rolling strip |
WANG Dong-cheng1,2, ZHANG Ya-lin1, XU Yang-huan1 |
1. National Engineering Research Center for Equipment and Technology of Cold Rolling Strip, Yanshan University,Qinhuangdao 066004, Hebei, China; 2. State Key Laboratory of Metastable Materials Science and Technology,Yanshan University, Qinhuangdao 066004, Hebei, China |
|
|
Abstract The head and tail of hot rolling strip are in the non-stationary rolling zone, which is prone to various size, shape and quality defects. In the process of rolling soft and thin strip, a kind of "pseudo-bad flatness" which have similar characteristics with middle wave often appears at the tail of strip, but its mechanism is completely different from that of bad flatness, so the conventional flatness control method cannot solve this problem. For this reason, the mechanism of the problem is analyzed firstly, and it is found that the reason of this phenomenon is the sudden shrinkage caused by the disappearance of tension in the moment of steel throwing. According to the above mechanism, the velocity matching relationship between F8 stand and coiler before steel throwing is optimized, which greatly improves the problem of "pseudo-bad flatness" at the tail of strip and avoids the scratch between strip surface and roller table.
|
Received: 17 June 2020
|
|
|
|
[1] 王国栋. 近年我国轧制技术的发展、现状和前景[J]. 轧钢,2017,34(1):1.(WANG Guo-dong. Development current situation and prospect of Chinese steel rolling technology in recent years[J]. Steel Rolling,2017,34(1):1.) [2] 陈百红,张红军,张成斌,等. 基于产品质量综合协调控制的热轧AGC系统优化[J]. 鞍钢技术,2019(3):32.(CHEN Bai-hong,ZHANG Hong-jun,ZHANG Cheng-bin,et al. Optimization of AGC system for hot rolling based on combined and coordinated control of product quality[J]. Angang Technology,2019(3):32.) [3] 王鹏. 热轧薄规格带钢生产能力提升实践[J]. 轧钢,2019,36(1):74.(WANG Peng. Productivity improvement practice for hot rolled thin gauge strip[J]. Steel Rolling,2019,36(1):74.) [4] 刘晓翠,张转转,李文远,等. 极限规格热轧高强耐候钢的开发[J]. 轧钢,2019,36(4):31.(LIU Xiao-cui,ZHANG Zhuan-zhuan,LI Wen-yuan,et al. Development of limit gauge of high strength atmospheric corrosion resisting steel strip[J]. Steel Rolling,2019,36(4):31.) [5] 王少飞,黄华贵,窦爱民,等. 高强DP钢的关键轧制技术开发与应用[J]. 中国冶金,2019,29(4):38.(WANG Shao-fei,HUANG Hua-gui,DOU Ai-min,et al. Development and application of key technology for DP high strength steel[J]. China Metallurgy,2019,29(4):38.) [6] 张健民,单旭沂. 热轧产线智能制造技术应用研究——宝钢1580热轧示范产线[J]. 中国机械工程,2020,31(2):246.(ZHANG Jian-min,SHAN Xu-yi. Application of intelligent manufacturing technology in hot rolling production line—Baosteel 1580 hot rolling demonstration production line[J]. China Mechanical Engineering,2020,31(2):246.) [7] 崔席勇,马涛,张伟,等. 带钢热轧智能窜辊策略的研究[J]. 重庆理工大学学报:自然科学,2019,33(11):95.(CUI Xi-yong,MA Tao,ZHANG Wei,et al. Research on intelligent shifting strategy for hot strip mill[J]. Journal of Chongqing University of Technology:Natural Science,2019,33(11):95.) [8] 胡伟东,李洪波,陈晨,等. 高速钢轧辊在2 250 mm热轧F5机架的应用[J]. 塑性工程学报,2019,26(1):292.(HU Wei-dong,LI Hong-bo,CHEN Chen,et al. Application of HSS roll at stand F5 in 2 250 mm hot strip mill[J]. Journal of Plasticity Engineering,2019,26(1):292.) [9] 董强,刘慧慧,张建水. 横向温度分布对无取向电工钢热轧板形的影响[J]. 中国冶金,2019,29(8):19.(DONG Qiang,LIU Hui-hui,ZHANG Jian-shui. Effects of transverse temperature distribution on strip shape of non-orientation electrical steel in hot rolling process[J]. China Metallurgy,2019, 29(8):19.) [10] 卢仲圩,邵健,何安瑞. 宽幅铝合金板带热连轧高精度板形控制系统[J]. 金属世界,2019(4):75.(LU Zhong-xu,SHAO Jian,HE An-rui. High precision shape control system for wide aluminum alloy in hot strip rolling[J]. Metal World,2019(4):75.) [11] 李伯群,范璇,李伟红,等. 板形设定模型参数优化与控制技术应用[J]. 钢铁,2019,54(2):47.(LI Bo-qun,FAN Xuan,LI Wei-hong,et al. Parameter optimization of shape setting model and application of control technology[J]. Iron and Steel, 2019, 54(2):47.) [12] 张明金,王洪彬,李新东. 热轧带钢头尾拉窄的原因分析与控制措施[J]. 轧钢,2009,26(4):60.(ZHANG Ming-jin,WANG Hong-bin,LI Xin-dong. Causes analysis of appearing narrow size of head and end of hot rolled strip and its control measures[J]. Steel Rolling,2009,26(4):60.) [13] 沈训良. 热轧带钢轧制过程的稳定性探讨[J]. 冶金丛刊,2001(5):13.(SHEN Xun-liang. Discussion on the stability during strip hot rolling process[J]. Metallurgical Collections,2001(5):13.) [14] 王章岭,付宝胜,夏银锋,等. 先进高强钢尾部翘曲行为的工艺优化[J]. 轧钢,2019,36(4):78.(WANG Zhang-ling,FU Bao-sheng,XIA Yin-feng,et al. Process optimization of tail warping behavior of advanced high strength steel strip[J]. Steel Rolling,2019,36(4):78.) [15] 韩久彦,罗晓阳,赵小龙,等. 热轧薄规格钢带折边缺陷分析及控制[J]. 甘肃冶金,2019,41(3):119.(HAN Jiu-yan,LUO Xiao-yang,ZHAO Xiao-long,et al. Analysis and control of edge folding defect on the hot rolled thin steel strip[J]. Gansu Metallurgy,2019,41(3):119.) [16] 于斌,杨旭,郭宝安,等. 一种热轧带钢头尾板形控制方法:中国,CN201210560491.6[P]. 2012-12-21.(YU Bin,YANG Xu,GUO Bao-an,et al. A Shape Control Method for Head and Tail of Hot Rolled Strip:China,CN201210560491.6[P]. 2012-12-21.) [17] 陈百红,史乃安,郝利国,等. 一种提高热轧带钢头部或尾部板形质量的方法:中国,CN201110296426.2[P]. 2011-09-30. (CHEN Bai-hong,SHI Nai-an,HAO Li-guo,et al. A Method to Improve the Shape Quality of the Head or Tail of Hot Rolled Strip:China,CN201110296426.2[P]. 2011-09-30.) |
[1] |
Zhi-ying Gao, Bo Tian, Yang Liu, Li-yuan Zhang, Mao-lin Liao. Dynamics-based optimization of rolling schedule aiming at dual goals of chatter suppression and speed increase for a 5-stand cold tandem rolling mill[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2021, 28(2): 168-180. |
[2] |
WEI Jun-you, ZHAO Wen-bo, CHEN Li, HU Peng, LIU Chong-lin, WAN Xiu-juan. Causes analysis of surface upwarping defects on hot rolled strip[J]. CONTINUOUS CASTING, 2020, 45(6): 48-56. |
[3] |
ZHOU Cong-rui, CHEN Xiao-long, ZHOU Ming-ke,FAN Lei, MEI Peng, BAO Si-qian. Cause analysis of surface blackening of SPHC hot rolled strip after pickling[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 41-. |
[4] |
WANG Dong-cheng, XU Yang-huan, DUAN Bo-wei, WANG Yong-mei, LIU Hong-min. Data-driven intelligent prediction model of edge seam defects for hot rolling strip[J]. Iron and Steel, 2020, 55(11): 82-90. |
[5] |
MA Wei1,LI Wei-gang1,2,ZHAO Yun-tao1,YAN Bao-kang1. Prediction of hot-rolled roll force based on deep learning[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(9): 805-815. |
[6] |
YANG Geng-wei,LU Jia-wei,SUN Hui,FANG Zi-wei,ZHOU Yi-liao,YAO Nan. Microstructure, mechanical properties and phase transformation behavior of TiV microalloyed highstrength hotstrip steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 726-732. |
|
|
|
|