Development of comprehensive treatment technology for strip C-shaped warp defect in galvanizing unit |
QIAN Sheng1,2, GU Qing1, LI Xue-tong1,3, BAI Zhen-hua1,3 |
1. National Cold Rolling Strip Equipment and Process Engineering Technology Research Center, Yanshan University, Qinhuangdao 066004, Hebei, China; 2. College of Mechanical and Electrical Engineering, Huangshan University, Huangshan 245041, Anhui, China; 3. State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, Hebei, China |
|
|
Abstract In order to study the serious problem with uneven coating of hot-dip galvanizing strip steel products caused by C-shaped defects, continuous annealing process of hot-dip galvanizing units is optimized, and the comprehensive treatment technology of C-shaped defects of strip are developed. Firstly, the equipment and process characteristics of the continuous annealing process of hot dip galvanizing was considered, the formation mechanism of C-shaped warping was analyzed. The influencing factors such as the state of open burner, the state of the radiation tube, the state of the cooling fan, the gravity of the strip, and the genetic shape of the upstream process section were analyzed, which made the larger temperature difference on the surface of the strip, resulting in the uniform distribution of transverse residual plastic deformation of the strip in its thickness direction. When it exceeded its critical instability condition, C-shaped warping occurred. And then, from the perspective of systematics, the system function of continuous annealing furnace with the influencing factors of C-shaped warping defect was established. The multivariable coupling and complex nonlinear characteristics of continuous annealing furnace were considered, the continuous annealing process was divided into subsystems in the unit of process section, and the minimum warping of each process section was taken as the optimal goal. Based on C-shaped warping prediction model of the strip, the temperature optimization objective function of heating section, the temperature optimization objective function of soaking section and the optimization objective function of cooling fan state in cooling section were established respectively, and the system function was established in the form of the objective functions of each process section superposing. The comprehensive optimization method of process parameters in each process section of continuous annealing process was obtained, and the optimization process was formulated. The key technologies such as temperature optimization setting technology in heating section, temperature optimization setting technology in soaking section and optimization setting technology of cooling fan state in cooling section were formed. Finally, the comprehensive treatment technology was applied to a domestic iron and steel company and good results were achieved. The results show that the maximum warpage of the typical specification strip decreases from 17.0 mm to 5.9 mm, the warping of strip are compared before and after the process parameters optimizating. The production statistics of coating thickness of this type strip show that the average coating thickness on the upper and lower surfaces of the strip is reduced to the range required by the user after the C-shaped warping of the strip is improved.
|
Received: 14 April 2021
|
|
|
|
[1] 李新创. 新时代钢铁工业高质量发展之路[J]. 钢铁,2019,54(1):1.(LI Xin-chuang. Road map to high-quality development of iron and steel industry in new age[J]. Iron and Steel,2019,54(1):1.) [2] 孙永旭,钱胜,白振华. 热镀铝锌连退过程中带钢横向拉窄量预报及其影响因素[J]. 轧钢,2021,38(1):41.(SUN Yong-xu, QIAN Sheng, BAI Zhen-hua. Investigation on prediction of transverse narrowing of strip and its influence factors in continuous annealing process of galvalume unit[J].Steel Rolling,2021,38(1):41.) [3] 昝现亮,王凤琴,刘子英,等. 热轧带钢残余应力相关板形缺陷机理分析及攻关措施[J]. 中国冶金,2020,30(5):35.(ZAN Xian-liang,WANG Feng-qin,LIU Zi-ying,et al. Mechanism analysis and research measures of residual stress-related plate shape defects in hot rolled strip[J]. China Metallurgy,2020,30(5):35.) [4] 昝现亮,孙翼洲,王凤琴,等. 热轧平整带钢C翘机理分析及措施[J]. 轧钢,2020,37(5):21.(ZAN Xian-liang,SUN Yi-zhou,WANG Feng-qin,et al. Mechanism analysis of C warp defects of hot rolled strip in temper and its countermeasures[J]. Steel Rolling,2020,37(5):21.) [5] 丁美良,杨丽琴,关建辉,等. 薄规格酸洗板轧制稳定性研究[J]. 上海金属,2019,41(2):105. (DING Mei-liang,YANG Li-qin,GUAN Jian-hui,et al. Research on rolling stability for pickled thin-gauge sheet[J]. Shanghai Metals,2019,41(2):105.) [6] 张清东,卢兴福,戴杰涛,等. 冷轧带钢板形翘曲变形过程及规律的解析[J]. 北京科技大学学报,2014,36(3):378.(ZHANG Qing-dong,LU Xing-fu,DAI Jie-tao,et al. Analysis of warping deformation for cold-rolled strips[J]. Journal of University of Science and Technology Beijing,2014,36(3):378.) [7] 曹强. 冷轧高强钢板带热处理过程板形变化规律研究[D]. 北京:北京科技大学,2015.(CAO Qiang. Research on Flatness Evolution of Cold-Rolled High Strength Steel Strip During Heat Treatment[D]. Beijing:University of Science and Technology Beijing,2015.) [8] 戴杰涛,李烈军,张祖江. 基于辛弹性力学方法的中厚板板形翘曲行为分析[J]. 固体力学学报,2015,36(3):215.(DAI Jie-tao,LI Lie-jun,ZHANG Zu-jiang. Warping analysis of medium plate based on symplectic elasticity method[J]. Chinese Journal of Solid Mechanics,2015,36(3):215.) [9] 唐伟,杜凤山,文杰,等. 镀锡板翘曲控制策略研究与应用[J]. 钢铁,2019,54(12):55. (TANG Wei,DU Feng-shan,WEN Jie,et al. Research and application of warping control strategy on tinplate[J]. Iron and Steel,2019,54(12):55.) [10] 何建锋. 宝钢镀锡板翘曲原因分析与对策[J]. 宝钢技术,2004(1):36.(HE Jian-feng. Cause Analysis of tinplate warp and our countermeasures[J]. Baosteel Technology,2004(1):36.) [11] 张宝平,周莲莲. 连续退火生产线带材翘曲治理方案的研究[J]. 中国冶金,2007,6(17):55.(ZHANG Bao-ping,ZHOU Lian-lian. Research on control buckle of strip in continuous annealing[J].China Metallurgy,2007,6(17):55.) [12] 王章岭,付宝胜,夏银锋,等. 先进高强钢尾部翘曲行为的工艺优化[J]. 轧钢,2019,36(4):78.(WANG Zhang-ling,FU Bao-sheng,XIA Yin-feng,et al. Process optimization of tail warping behavior of advanced high strength steel strip[J]. Steel Rolling,2019,36(4):78.) [13] 杜国强,袁文振,张宝平,等. 连续退火机组带钢板形翘曲控制[J]. 中国冶金,2016,26(12):44.(DU Guo-qiang,YUAN Wen-zhen,ZHANG Bao-ping,et al. Buckling control for strip steel in continuous annealing line[J]. China Metallurgy,2016,26(12):44.) [14] 杨世铭,陶文铨. 传热学 [M]. 四版. 北京:高等教育出版社,2006.(YANG Shi-ming,TAO Wen-quan. Heat Transfer Theory [M]. 4th ed. Beijing:Higher Education Press,2006.) |
[1] |
BAI Zhen-hua, LIN Wei, WANG Wei, ZHANG Wen-jun, LI Xue-tong. Development of optimization technology for disc shear process parameters of hot-dip galvanizing line[J]. Iron and Steel, 2022, 57(1): 159-166. |
[2] |
QIAN Sheng, ZHANG Wen-jun, LIN Wei, GU Qing, BAI Zhen-hua. Formation mechanism and prediction model for C-warping defect of strip steel in continuous annealing process of hot galvalume unit[J]. Iron and Steel, 2021, 56(9): 88-95. |
[3] |
DUAN Xiao-xi, MA Xing-jiang, LU Yang-ze, HAN Zhi-gang, LI Zhen, NING Yuan-yuan. Formation mechanism and improvement measures of color difference defect on surface of hot-dip galvanized strip steel[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(6): 37-. |
[4] |
QIN Da-wei, LIU Hong-min, ZHANG Dong, WANG Jun-sheng. Prediction models of coating mass per unit area for hot-dip galvanized strip based on artificial neural network[J]. Iron and Steel, 2020, 55(5): 68-72. |
[5] |
CAO Guang- ming,LI Zhi- feng,WANG Hao,LIU Zhen- yu. Progress of pickling- free reductive annealing hot- dip galvanization on hot- rolled steel[J]. , 2019, 31(2): 159-167. |
[6] |
KE Jiang-jun,HU Hai-jiang,XU Guang,YUAN Qing. Analysis of the mechanism of sliver-type embossment defect on the surface of cold rolled hot galvanized sheet[J]. , 2019, 37(1): 32-35. |
|
|
|
|