Manganese sulfide inclusion control technology in medium and high sulfur steel |
XIE Xiao-yu1, GU Chao1, WANG Min1, BAO Yan-ping1, LUO Xiong-zhi2, PENG Guang-jian2 |
1. State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China; 2. Department of Technology and Quality, Hunan Valin Xiangtan Ironand Steel Co., Ltd., Xiangtan 411101, Hunan, China |
|
|
Abstract In recent years, with the continuous upgrading of manufacturing industry, the requirement of energy saving and environmental protection becomes higher and higher. For some steels used in the manufacture of complex parts, free-cutting elements (S, Te, Pb) are usually added to steel to improve its cutting performance in order to reduce energy consumption in the manufacturing process. Adding a certain amount of sulfur is the most commonly used improvement method at present. Sulfur mainly exists in the form of manganese sulfide in steel, and its morphology and distribution control level have important influence on the mechanical properties of steel. For medium and high sulphur steel, manganese sulfide is a plastic inclusion, which is easy to aggregate during precipitation and to deform along the rolling direction during rolling to form large-size strips. Such large-size manganese sulfide can seriously destroy the transverse properties of materials. To ensure the steel properties of medium and high sulphur steels, it is necessary to control the morphology and distribution of manganese sulphide inclusions in steel. The goal is to avoid the generation of large-size manganese sulphide and to obtain spindle-like manganese sulphide inclusions with fine and uniform distribution as possible. Manganese sulfide inclusion control is a systematic problem and must be carried out in conjunction with the entire process. The influence laws of some chemical compositions and process parameters on the inclusion precipitation of manganese sulfide were summarized. And the previous manganese sulfide inclusion control practices in the whole production process, including modification treatment of refining process, compound precipitation control, solidification process control and rolling and cooling control were reviewed. It is also pointed out that for the MnS control of non-quenched and tempered free cutting steel with medium and high sulfur content, how to implement the laboratory research results in industrial production is the direction of joint efforts for the majority of researchers in the future.
|
Received: 16 April 2021
|
|
|
|
[1] 陈蕴博,马鸣图,王国栋. 汽车用非调质钢的研究进展[J]. 中国工程科学,2014,16(2):4.(CHEN Yun-bo,MA Ming-tu,WANG Guo-dong. Resent progress of non-quenched and tempered steel for automotive sheet[J]. Strategic Study of CAE,2014,16(2):4.) [2] 袁武华,王峰. 国内外易切削钢的研究现状和前景[J]. 钢铁研究,2008(5):56.(YUAN Wu-hua,WANG Feng. Present research status and prospects on free cutting steel at home and abroad[J]. Research on Iron and Steel,2008(5):56.) [3] 陈蕴博,马炜,金康. 强韧微合金非调质钢的研究动向[J]. 机械工程材料,2001(3):1.(CHEN Yun-bo,MA Wei,JIN Kang. Development on improving the strength and toughness of microalloyed steels[J]. Materials for Mechanical Engineering,2001(3):1.) [4] 林腾昌, 门兵, 程雄, 等. 热处理对铸态钢中硫化锰夹杂物的影响[J].中国冶金, 2021, 31(4): 48.(LIN Teng-chang, MEN Bing, CHENG Xiong, et al. Influence of heat treatment on MnS inclusion in as-cast steel[J]. China Metallurgy, 2021, 31(4): 48.) [5] Hosseini S B,Temmel C,Karlsson B,et al. An in-situ scanning electron microscopy study of the bonding between MnS inclusions and the matrix during tensile deformation of hot-rolled steels[J]. Metallurgical and Materials Transactions A,2007,38(5):982. [6] MA M T,LI G Z,LI Z G,et al. The effect of morphology and distribution of sulfides on mechanical properties and fatigue life of non-quenched and tempered steel[J]. Advanced Materials Research,2008,51:11. [7] 艾克南,张盼盼,赵梦豪,等. 1215易切削钢拉拔表面裂纹形成机制分析[J]. 钢铁,2020,55(2):88.(AI Ke-nan,ZHANG Pan-pan,ZHANG Meng-hao,et al. Analysis of formation mechanism of surface crack of 1215 free-cutting steel during drawing[J]. Iron and Steel,2020,55(2):88.) [8] 车巨龙, 鲜奋强, 窦亚斌, 等. 非调质钢中MnS分布对轧材横向塑性的影响[J].中国冶金, 2020, 30(6): 48. (CHE Ju-long, XIAN Fen-qiang, DOU Ya-bin, et al. Effect of MnS distribution on transverse ductility of rolled non-quenched and tempered steel[J]. China Metallurgy, 2020, 30(6): 48.) [9] 常开地,赵焕春,张慧峰,等. 含硫非调质钢轧后硫化物夹杂形貌的观察[J]. 金属热处理,2006,31(9):60.(CHANG Kai-di,ZHAO Huan-chun,ZHANG Hui-feng,et al. Observation on sulphide inclusions morphology of sulphur-containing microalloyed steel after rolling[J]. Heat Treatment of Metals,2006,31(9):60.) [10] 许国方, 张雪良, 杨树峰, 等. 20CrMnTi齿轮钢冶炼全流程的夹杂物分析[J]. 中国冶金, 2020, 30(11): 23.(XU Guo-fang, ZHANG Xue-liang, YANG Shu-feng,et al. Inclusion characterization in whole smelting process of 20CrMnTi gear steel[J]. China Metallurgy, 2020, 30(11): 23.) [11] Sims C E. The nonmetallic constituents of steel[J]. Transaction AIME,1959,215. [12] Ito Y,Masumitsu N,Matsubara K. Formation of manganese sulfide in steel[J]. Transactions of the Iron and Steel Institute of Japan,1981,21(7):477. [13] Anmark N,Karasev A,Jonsson P G. The effect of different non-metallic inclusions on the machinability of steels[J]. Materials,2015,8(2):751. [14] 鲁金龙. 大规格曲轴用非调质钢中MnS形成机理及控制工艺研究[D]. 北京:北京科技大学,2020.(LU Jin-long. Research on Formation Mechanism and Control Process of MnS in Non-Quenched and Tempered Steel for Heavy Crankshaft [D]. Beijing:University of Science and Technology Beijing,2020.) [15] 吴华杰,陆鹏雁,岳峰,等. 钙处理对中硫含量钢中硫化物形态影响的试验研究[J]. 北京科技大学学报,2014,36(s1):230.(WU Hua-jie,LU Peng-yan,YUE Feng,et al. Effect of calcium treatment on sulfide inclusions in steel with medium sulphur content[J]. Chinese Journal of Engineering,2014,36(s1):230.) [16] 杨超云, 庄权, 刘航, 等. 稀土变质高洁净轴承钢中夹杂物的行为分析[J].中国冶金, 2020, 30(9): 45.(YANG Chao-yun, ZHUANG Quan, LIU Hang, et al. Analysis on modification behavior of rare earth to inclusions in highly clean bearing steel[J]. China Metallurgy, 2020, 30(9): 45.) [17] 赵麦群,王伟科,张颢,等. 稀土改性42CrMoS易切削钢中的硫化物夹杂分析[J]. 金属热处理,2004(11):20.(ZHAO Mai-qun,WANG Wei-ke,ZHANG Hao,et al. Analysis on sulphide inclusions in free-cutting 42CrMoS steel modified by rare earth elements[J]. Heat Treatment of Metals,2004(11):20.) [18] 董大西, 杨超云, 胡云生,等. 高洁净轴承钢中稀土变质夹杂物行为分析[J]. 中国冶金, 2020, 30(6): 30. (DONG Da-xi, YANG Chao-yun, HU Yun-sheng,et al. Analysis on modification behavior of rare earth to inclusions in high clean bearing steel[J]. China Metallurgy, 2020, 30(6): 30.) [19] REN Y,ZHANG L. Effect of Al2O3-SiO2-MnO inclusions on precipitation of MnS in Si-Mn-killed 304 stainless steels[J]. Ironmaking and Steelmaking,2019,46(6):558. [20] XIE J,ZHANG D,YANG Q,et al. Exploration of morphology evolution of the inclusions in Mg-treated 16MnCrS5 steel [J]. Ironmaking and Steelmaking,2019,46(6):564. [21] ZHANG Q,MIN Y,XU H,et al. Formation and evolution of inclusions in Si-killed resulfurized free-cutting steel[J]. ISIJ International,2018,58(7):1250. [22] 李代钟. 钢中硫化物夹杂物球化和对钢性能的影响[J]. 钢铁研究学报,1992,4(2):97.(LI Dai-zhong. Globularizing of sulfide inclusions and its influence on the properties of steel [J]. Journal of Iron and Steel Research,1992,4(2):97.) [23] 夏云进,王福明,王金龙,等. 氧含量对易切削钢中硫化物生成行为的影响[J]. 北京科技大学学报,2010,32(10):1271.(XIA Yun-jin,WANG Fu-ming,WANG Jin-long,et al. Effect of oxygen content on the formation behavior of sulfides in free-cutting steel[J]. Journal of University of Science and Technology Beijing,2010,32(10):1271.) [24] 段飞虎. 钢中氧含量对硫化物夹杂种类和形态的影响[J]. 钢铁研究,2016,44(4):20.(DUAN Fei-hu. Effect of oxygen content on the types and forms of sulfide inclusions in steel [J]. Research on Iron and Steel,2016,44(4):20.) [25] 张学伟,杨才福,柴锋,等. 热力学分析MnS夹杂物析出与控制[J]. 钢铁,2019,54(12):27.(ZHANG Xue-wei,YANG Cai-fu,CHAI Feng,et al. Precipitation and control of MnS inclusions by thermodynamic analysis[J]. Iron and Steel,2019,54(12):27.) [26] 张志刚, 任英, 成功, 等. 非调质钢中夹杂物生成热力学[J].中国冶金, 2020, 30(4): 23.(ZHANG Zhi-gang, REN Ying, CHENG Gong,et al. Thermodynamic of inclusion formation in non-tempered steel[J]. China Metallurgy, 2020, 30(4): 23.) [27] Wakoh M,Sawai T,Mizoguchi S. Effect of S content on the MnS precipitation in steel with oxide nuclei[J]. ISIJ International,1996,36(8):1014. [28] 吴华杰,岳峰,尤大利,等. Mn/S对含硫非调质钢中硫化物形态的影响[J]. 北京科技大学学报,2014,36(s1):77.(WU Hua-jie, YUE Feng,YOU Da-li,et al. Effect of Mn/S on sulfide inclusions in non-quenched and tempered steel containing sulfur[J]. Journal of University of Science and Technology Beijing,2014,36(s1):77.) [29] ZHAO F,WU M,JIANG B,et al. The effect of carbon contents on intragranular ferrite formed in the V-Ti-N microalloyed steel with a carbon content gradient prepared by controlling the surface decarburization[J]. Materials Characterization,2018,140:217. [30] Tsunekage N,Tsubakino H. Effects of sulfur content and sulfide-forming elements addition on impact properties of ferrite-pearlitic microalloyed steels[J].ISIJ International,2001,41(5):498. [31] Leung C,Van Vlack L H. Solution and precipitation hardening in(Ca, Mn) sulfides and selenides[J]. Metallurgical Transactions A,1981,12(6):987. [32] Blais C,L′Espérance G,Le Huy H,et al. Development of an integrated method for fully characterizing multiphase inclusions and its application to calcium-treated steels[J]. Materials Characterization,1997,38(1):25. [33] 陆鹏雁,吴华杰,岳峰,等. 钙处理对含硫非调质钢中夹杂物演变行为的影响[J]. 炼钢,2015,31(2):30.(LU Peng-yan,WU Hua-jie,YUE Feng,et al. Effect of calcium treatment on change behavior of inclusions in sulfur-containing non-quenched and tempered steel[J]. Steelmaking,2015,31(2):30.) [34] 杨利委. 钙处理非调质钢的夹杂物控制[J]. 中国金属通报,2020(1):166.(YANG Li-wei. Control of inclusions in calcium-treated non-quenched and tempered steel[J]. China Metal Bulletin,2020(1):166.) [35] 赵国伟,张生存,龚明健,等. 稀土元素在铸钢中的应用[J]. 中国铸造装备与技术,2019,54(5):12.(ZHAO Guo-wei,ZHANG Sheng-cun,GONG Ming-jian,et al. Application of rare earth elements in cast steel[J]. China Foundry Machinery and Technology,2019,54(5):12.) [36] 范磊,李晨,姜茂发. 稀土对高硫易切削钢中夹杂物的影响研究[J]. 钢铁钒钛,2020,41(6):119.(FAN Lei,LI Chen,JIANG Mao-fa. Experimental study on the effect of rare earth on inclusions in high-sulfur free-cutting steel[J]. Iron Steel Vanadium Titanium,2020,41(6):119.) [37] 吴春红,孙乐飞,赖朝彬,等. 钇基稀土处理对E36铸坯夹杂物的影响[J]. 钢铁钒钛,2016,37(5):139.(WU Chun-hong,SUN Le-fei,LAI Chao-bin, et al. Effect of rare earth treatment on inclusion of E36 slab for shipbuilding[J]. Iron Steel Vanadium Titanium,2016,37(5):139.) [38] SHEN P,YANG Q,ZHANG D,et al. The effect of tellurium on the formation of MnTe-MnS composite inclusions in non-quenched and tempered steel[J]. Metals,2018,8(8):639. [39] Zheng L,Malfliet A,Wollants P,et al. Effect of surfactant Te on the formation of MnS inclusions in steel[J]. Metallurgical and Materials Transactions B,2017,48(5):2447. [40] WANG F,GUO H,LIU W,et al. Control of MnS inclusions in high- and low-sulfur steel by tellurium treatment[J]. Materials,2019,12(7):1034. [41] Wakoh M,Sawai T,Mizoguchi S. Effect of oxide particles on MnS precipitation in low S steels[J]. Tetsu-to-Hagane,1992,78(11):1697. [42] Bramfitt B L. The effect of carbide and nitride additions on the heterogeneous nucleation behavior of liquid iron[J]. Metallurgical Transactions,1970,1(10):2958. [43] Turnbull D,Vonnegut B. Nucleation catalysis[J]. Industrial and Engineering Chemistry,1952,44(6):1292. [44] 李鹏,李光强,郑万. Al-Ti脱氧对非调质钢中MnS析出行为及组织的影响[J]. 钢铁研究学报,2013,25(11):49.(LI Peng,LI Guang-qiang,ZHENG Wan. Effect of Al-Ti deoxidation on MnS precipitation and the microstructure of non-quenched and tempered steel[J]. Journal of Iron and Steel Research,2013,25(11):49.) [45] Oikawa K,Ishida K,Nishizawa T. Effect of titanium addition on the formation and distribution of MnS inclusions in steel during solidification[J]. ISIJ International,1997,37(4):332. [46] SUN H,WU L,XIE J,et al. Inclusions modification and improvement of machinability in a non-quenched and tempered steel with Mg treatment[J]. Metallurgical Research and Technology,2020,117:208. [47] CHEN K,WANG D,HOU D,et al. Effect of interfacial properties on agglomeration of inclusions in molten steels[J]. ISIJ International,2019,59(10):1735. [48] 吴翔宇,何玉东,吴良平等. 镁改质对Y1Cr13易切削不锈钢中硫化物的影响[J]. 钢铁,2020,55(4):68.(WU Xiang-yu,HE Yu-dong,WU Liang-ping,et al. Effect of magnesium modification on sulfides in Y1Cr13 free-cutting stainless steel[J]. Iron and Steel,2020,55(4):68.) [49] 于哲,刘承军,闵义,等. 含硫易切削钢夹杂物控制试验研究[J]. 钢铁钒钛,2017,38(3):140.(YU Zhe,LIU Cheng-jun,MIN Yi,et al. Experimental study on inclusions control of resulfurized free cutting steel[J]. Iron Steel Vanadium Titanium,2017,38(3):140.) [50] 夏云进,郭鑫,李杰,等. 锆、铝脱氧对钢中硫化物生成行为的影响[J]. 钢铁,2016,51(2):38.(XIA Yun-jin,GUO Xin,LI Jie,et al. Effects of Zr, Al deoxidation on formation behavior of sulfides in steel[J]. Iron and Steel,2016,51(2):38.) [51] 郭沁怡,宋波,宋明明. Ti、Al、Zr脱氧对中硫非调质钢中硫化物形态的影响[J]. 材料热处理学报,2019,40(2):133.(GUO Qin-yi,SONG Bo,SONG Ming-ming. Effects of Ti, Al and Zr deoxidation on morphology of sulfides in medium-sulfur non-quenched and tempered steel[J]. Transactions of Materials and Heat Treatment,2019,40(2):133.) [52] Wakoh M,Sawai T,Mizoguchi S. Effect of Ti-Zr oxide particles on MnS precipitation in low S steels[J]. Tetsu-to-Hagane,1996,82(7):593. [53] LU J,CHENG G,CHEN L,et al. Distribution and morphology of MnS inclusions in resulfurized non-quenched and tempered steel with Zr addition[J]. ISIJ International,2018,58(7):1307. [54] Takada H,Bessho I,Ito T. Effect of sulfur content and solidification variables on morphology and distribution of sulfide in steel ingots[J]. Transactions of the Iron and Steel Institute of Japan,1978,18(9):564. [55] 夏云进,王福明,李长荣,等. 定向凝固研究易切削钢中硫化物的生成行为[J]. 北京科技大学学报,2012,34(2):118.(XIA Yun-jin,WANG Fu-ming,LI Chang-rong,et al. Study on the formation behavior of sulfides in free-cutting steel by unidirectional solidification[J]. Chinese Journal of Engineering,2012,34(2):118.) [56] Schwerdtfeger K. Influence of solidification rate on the microsegregation and interdendritic precipitation of manganesesulphide inclusions in a steel containing manganese and carbon[J]. Steel Research International,1970,41(9):923. [57] Takada H, Bessho I, Ito T. Effect of sulfur content and solidification variables on morphology and distribution of sulfide in steel ingots[J]. Tetsu-to-Hagané,1976,62(10):1319. [58] LIU H,HU D,FU J. Analysis of MnS inclusions formation in resulphurised steel via modeling and experiments[J]. Materials,2019,12(12):2028. [59] 娄德春,崔昆,吴晓春,等. 硫化锰夹杂物的热变形行为[J]. 钢铁研究学报,1996,8(6):11.(LOU De-chun,CUI Kun,WU Xiao-chun,et al. Behavior of MnS during hot deformation[J]. Journal of Iron and Steel Research,1996,8(6):11.) [60] 陈俊东,关晓光,汪云辉. 热变形工艺对低硫易切削钢中硫化锰形态演变的影响[J]. 金属热处理,2019,44(2):125.(CHEN Jun-dong,GUAN Xiao-guang,WANG Yun-hui. Influence of thermal deformation process on morphology evolution of MnS inclusion in low-sulphur free-cutting steel[J]. Heat Treatment of Metals,2019,44(2):125.) [61] 简龙,陈伟庆,孟金霞,等. 含硫非调质钢中硫化物形态的控制[J]. 钢铁,2006,41(10):74.(JIAN Long,CHEN Wei-qing,MENG Jin-xia,et al. Sulfide shape control in non quenched and tempered steel containing sulphur[J]. Iron and Steel,2006,41(10):74.) [62] SHAO X,WANG X,JIANG M,et al. Effect of heat treatment conditions on shape control of large-sized elongated MnS inclusions in resulfurized free-cutting steels[J]. ISIJ International,2011,51(12):1995. [63] 李兵,陈伟庆,郑宏光,等. 加热工艺对非调质钢49MnVS3中硫化物尺寸和形态的影响[J]. 金属热处理,2017,42(1):144.(LI Bing,CHEN Wei-qing,ZHENG Hong-guang,et al. Effect of heating process on size and morphology of sulfide inclusions in non-quenched and tempered 49MnVS3 steel[J]. Heat Treatment of Metals,2017,42(1):144.) |
[1] |
CHE Zhi-chao, LIU Wei, YANG Shu-feng, LI Jing-she, LIU Chao, YUAN Hao. Modification of sulfide inclusions in 15-5PH steel by tellurium treatment[J]. Iron and Steel, 2022, 57(3): 36-43. |
[2] |
JIANG Chang, WANG Zi-bo, WANG Yang, LU Heng-chang, MAN Ting-hui, ZHOU Lei. Continuous cooling transformation law of cold work hardening non-quenched and tempered steel[J]. Iron and Steel, 2022, 57(3): 91-96. |
[3] |
WANG Zhang-yin, JIANG Min, WANG Xin-hua. Formation and evolution of inclusions in Q345D steel during secondary refining process[J]. Iron and Steel, 2022, 57(2): 63-72. |
[4] |
WANG Kun-peng, WANG Ying, LIAO Jia-ming, XU Jian-fei, JIANG Min, WANG Xin-hua. Investigation on inclusions and breakages in ultra-deep drawing wire rod[J]. Iron and Steel, 2022, 57(2): 101-108. |
[5] |
WANG Yan, ZHU Li-guang, WU Yao-guang, WANG Chong-jun, LIU Zhi-yuan, HUO Jin-xia. Microstructure characteristics of welding heat affected zone in EH40 shipbuilding steel[J]. Iron and Steel, 2022, 57(2): 139-148. |
[6] |
ZHU Hang-yu, WANG Wei-sheng, ZHAO Ji-xuan, LI Jian-li, SONG Ming-ming, XUE Zheng-liang. Effect of manganese raw materials on non-metallic inclusions in low alloy TRIP steel[J]. Iron and Steel, 2022, 57(1): 66-73. |
|
|
|
|