QD08钢中Ds类夹杂物形成原因及控制

doi:10.13228/j.boyuan.issn0449-749x.20210327

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (3602 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract QD08 steel requires high fatigue resistance due to its special working environment, and Ds inclusions are the main reason for weakening the fatigue resistance of QD08 steel. In order to explore the reasons for the formation of Ds inclusions and control methods, and solve the problem of excessive Ds inclusions, the whole process of steelmaking, refining and continuous casting of this steel grade was sampled and analyzed. The analysis results show that the main component of Ds inclusions that affect the fatigue performance of QD08 steel is CaS-Al₂O₃-MgO-CaO, and its size fluctuates in the range of 15-30 μm, which mainly begin to appear after the LF refining calcium treatment operation. The Ds inclusions in QD08 steel are formed by using calcium magnesium aluminate as the core framework and wrapping CaS on the periphery. Combined with the composition distribution of inclusions, it is determined that the high calcium content in steel is not conducive to the control of Ds inclusions in QD08 steel. The modified inclusions have a low melting point, and the inclusions have strong wettability with molten steel, making inclusions difficult pass through the steel slag interface into the refined slag. In addition, the inclusions are easy to aggregate and grow in the molten steel, resulting in an increase in the size of the inclusions, which provides conditions for the formation of Ds-type inclusions. The optimization plan for the refining slag with high solubility of calcium oxide and micro-calcium treatment in the refining process was proposed, and industrial verification tests were carried out. The micro-calcium treatment ensures the necessary inclusion modification, prevents the nozzle nodules, cooperates with reducing the fluctuation of the tundish liquid level, controls the appropriate drawing speed, avoids the slag leaving from the ladle, and avoids the occurrence of slag entrapment. The process controls more inclusions to be distributed in the non-liquid zone, inhibits the collision and growth of inclusions, and reduces the level of Ds inclusions. The test results show that the Ds inclusions in QD08 steel that affect its fatigue performance have been controlled, and the initial inspection pass rate has been increased from 93.6% to 98.0%, which has brought direct economic benefits to the enterprise.

Key words： QD08 steel Ds inclusion cleanliness calcium treatment industrial test

Received: 28 May 2021

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	SONG Zhao-qi
	LIU Wei
	YANG Shu-feng
	LI Jing-she
	CHEN Yong-feng
	ZUO Xiao-tan

Cite this article:

SONG Zhao-qi,LIU Wei,YANG Shu-feng等. Formation reason and control of Ds inclusions in QD08 steel[J]. Iron and Steel, 2021, 56(12): 68-74.

URL:

http://www.chinamet.cn/Jweb_gt/EN/10.13228/j.boyuan.issn0449-749x.20210327 OR http://www.chinamet.cn/Jweb_gt/EN/Y2021/V56/I12/68

[1] 印传磊,翟万里,蒋栋初,等. 42CrMo钢大尺寸夹杂物的来源与控制[J].中国冶金,2021,31(1):36.(YIN Chuan-lei, ZHAI Wan-li, JIANG Dong-chu, et al. Source and control of large-size inclusions in 42CrMo steel[J]. China Metallurgy, 2021, 31(1): 36.)
[2] 谢世正,刘宁,梁亮,等. NM450钢板折弯开裂原因分析[J].中国冶金,2021,31(7):46. (XIE Shi-zheng, LIU Ning, LIANG Liang, et al. Analysis of the causes of bending and cracking of NM450 steel plate[J]. China Metallurgy, 2021, 31(7): 46.)
[3] 战东平, 杨永坤, 姜周华, 等. 加热过程钢中夹杂物演变的研究进展[J]. 钢铁, 2021, 56(10): 16. (ZHAN Dong-ping, YANG Yong-kun, JIANG Zhou-hua, et al. A review of research on inclusions evolution in steel during heating process[J]. Iron and Steel, 2021, 56(10): 16.)
[4] 李永超,卢彩玲,左健成,等. 轴承钢中间包首炉大型夹杂物分析及控制[J].连铸,2021,46(3):35.(LI Yong-chao, LU Cai-ling, ZUO Jian-cheng, et al. Analysis and control of large inclusions in the first furnace of bearing steel tundish[J].Continuous Casting, 2021,46(3):35.)
[5] 车晓健,杨卯生,唐海燕,等. 高性能GCr15轴承钢中夹杂物控制与疲劳性能[J]. 钢铁,2018,53(5):76.(CHE Xiao-jian,YANG Mao-sheng,TANG Hai-yan,et al. Inclusion control and fatigue property of high performance GCr15 bearing steel[J]. Iron and Steel,2018,53 (5):76.)
[6] Ho H S, Zhou W L, Li Y,et al. Low-cycle fatigue behavior of austenitic stainless steels with gradient structured surface layer[J]. International Journal of Fatigue,2020,134:105481.
[7] 杨俊,杜江,陈波涛,等. 超低氧精炼时钙处理对氧化物夹杂的影响[J]. 钢铁,2015,50(1):19.(YANG Jun,DU Jiang,CHEN Bo-tao,et al. The effect of calcium treatment on oxide inclusions during ultra-low oxygen refining[J]. Iron and Steel,2015,50(1):19.)
[8] Hisashi Mori,Nobuyoshi Tanaka,Masazumi Hirai. Large inclusions in continuously cast carbon steel billets[J]. Transactions of the Iron and Steel Institute of Japan,2020,11(6):424.
[9] 张立峰,杨文,张学伟,等. 钢中夹杂物的系统分析技术[J]. 钢铁,2014,49(2):1.(ZHANG Li-feng,YANG Wen,ZHANG Xue-wei,et al. Systematic analysis technology of inclusions in steel[J]. Iron and Steel,2014,49(2):1.)
[10] Jiang Min, Wang Xin-hua, Pak Jong-jin,et al. In situ observation on behaviors of CaO-MgO-Al₂O₃ -SiO₂ complex inclusions at solid-liquid interface of low-oxygen special steel[J]. Metallurgical and Materials Transactions B,2014,45(5):94.
[11] 黄国俊. 含ZrO₂类Ds夹杂物的来源及控制分析[J]. 连铸,2020,45(1):36.(HUANG Guo-jun. Source and control analysis of Ds inclusions containing ZrO₂[J]. Continuous Casting,2020,45(1):36.)
[12] 任宏志. 稀土Ce元素对轴承钢中Ds类夹杂物的影响[D].包头:内蒙古科技大学,2019.(REN Hong-zhi. The Effect of Rare Earth Ce on Ds Inclusions in Bearing Steel[D]. Baotou:Inner Mongolia University of Science and Technology,2019.)
[13] 徐迎铁,陈兆平,杨宝权. 轴承钢Ds类大颗粒夹杂物研究[J]. 炼钢,2016,32(4):49.(XU Ying-tie,CHEN Zhao-ping,YANG Bao-quan. Research on Ds large particle inclusions in bearing steel[J]. Steelmaking,2016,32(4):49.)
[14] 缪新德,于春梅,石超民,等. 轴承钢中钙铝酸盐夹杂物的形成及控制[J]. 北京科技大学学报,2007,29(8):771.(MIAO Xin-de,YU Chun-mei,SHI Chao-min,et al. Formation and control of calcium aluminate inclusions in bearing steel[J]. Journal of University of Science and Technology Beijing,2007,29(8):771.)
[15] 张洪彪,李海,鲁东生,等. 低碳铝镇静钢QD08中Ds类夹杂物分析与控制[J]. 连铸,2017,42(5):50.(ZHANG Hong-biao,LI Hai,LU Dong-sheng,et al. Analysis and control of Ds inclusions in low carbon aluminum killed steel QD08[J]. Continuous Casting,2017,42(5):50.)
[16] 杨光维,陈兆平,柳向椿. 非钙处理对高等级齿轮钢夹杂物的影响[J]. 钢铁,2020,55(4):40.(YANG Guang-wei,CHEN Zhao-ping,LIU Xiang-chun. Effect of non-calcium treatment on inclusions in high-grade gear steel[J]. Iron and Steel,2020,55(4):40.)
[17] 缪新德,徐国庆,陈情华,等. GCr15钢中大颗粒夹杂(Ds类)的生成原因分析[J]. 炼钢,2007(2):21.(MIAO Xin-de,XU Guo-qing,CHEN Qing-hua,et al. Analysis on the formation of large particle inclusions (Ds type) in GCr15 steel[J]. Steelmaking,2007(2):21.)
[18] 姜敏,王昆鹏,侯泽旺,等. 低氧特殊钢中大尺寸Ds类夹杂物生成机理[J]. 工程科学学报,2016,38(6):780. (JIANG Min,WANG Kun-peng,HOU Ze-wang,et al. Formation mechanism of large-size Ds inclusions in low-oxygen special steel[J]. Chinese Journal of Engineering Science,2016,38(6):780.)
[19] 杨光维,陈兆平,柳向椿. 高等级齿轮钢夹杂物控制技术研究[J]. 炼钢,2019,35(1):61.(YANG Guang-wei,CHEN Zhao-ping,LIU Xiang-chun. Research on inclusion control technology of high-grade gear steel [J]. Steelmaking,2019,35 (1):61.)
[20] 刘珍童,杨文,任英,等. 铝脱氧钢钙处理效果影响因素分析[J]. 钢铁,2020,55(3):29.(LIU Zhen-tong,YANG Wen,REN Ying,et al. Analysis of influencing factors of calcium treatment effect of aluminum deoxidized steel[J]. Iron and Steel,2020,55(3):29.)
[21] Arai H,Matsumoto K,Shimasaki S I,et al. Model experiment on inclusion removal by bubble flotation accompanied by particle coagulation in turbulent flow[J]. ISIJ International,2009,49(7):965.
[22] 刘威. 钢中非金属夹杂物界面去除过程微观模型研究[D]. 北京:北京科技大学,2020.(LIU Wei. Research on the Microscopic Model of the Interface Removal Process of Non-Metallic Inclusions in Steel[D]. Beijing:University of Science and Technology Beijing,2020.)