低碳微合金钢晶界铁素体三维形态及形成机理

doi:10.13228/j.boyuan.issn0449-749x.20210588

Abstract
Figure/Table
References
Related Citation (7)

Download: PDF (5219 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to better understand the three-dimensional morphology and formation mechanism of grain boundary ferrite in low carbon microalloyed steel, the 3D morphology of the different location was observed by focused ion beam scanning electron microscope equipped with electron back-scatter diffraction(EBSD), and the growth rate under test conditions was calculated by in-situ observation technology, finally the solute diffusion model was calculated by Matlab,from two aspects of test results and the theoretical data for the demonstration and analysis. The results show that the grain boundary surface ferrite does not grow along the austenite parent phase grain, but grows in a certain angle toward the grain. At the same time, it only grows near the austenite grain boundary and cannot grow too deep. Its three-dimensional morphology is flat on the front and thin strip on the side, accompanied with a large number of pits and defects. The grain boundary ribbed ferrite and austenite at the grain boundary have fixed interface on one side, and the other side is angular and grows into the grain. The three-dimensional morphology of ridged ferrite is like a triangular pyramid with a pointed tip. The adhesion surface is smooth, tidy, and the side has a deep gully. The findings were calculated using in situ observation techniques, the grain boundary ferrite precipitated at 725-775 ℃ has a faster growth rate, Locating between 100-250 μm/s, and the grain boundary ferrite precipitated at other temperatures has a lower growth rate. The distribution of grain boundary ferrite growth rate with temperature in local equilibrium/ para-equilibrium mode is obtained, the results find that the growth rate of grain boundary ferrite is mainly distributed in the para-equilibrium mode, and the growth rate of intragranular ferrite is only controlled by carbon diffusion.

Key words： grain boundary surface ferrite grain boundary ribbed ferrite three-dimensional morphology precipitation position solute diffusion model

Received: 23 September 2020

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	CAO Sheng-li
	WU Shao-wen
	ZHANG Cai-jun
	ZHANG Qing-jun

Cite this article:

CAO Sheng-li,WU Shao-wen,ZHANG Cai-jun等. Three-dimensional morphology and formation mechanism of grain boundary ferrite in low carbon microalloyed steel[J]. Iron and Steel, 2022, 57(3): 124-132.

URL:

http://www.chinamet.cn/Jweb_gt/EN/10.13228/j.boyuan.issn0449-749x.20210588 OR http://www.chinamet.cn/Jweb_gt/EN/Y2022/V57/I3/124

[1] 杨忠民, 王凯, 孙秀, 等.铌钛微合金钢铸坯晶界铁素体形貌与晶界裂纹[J].钢铁, 2018,53(11):70.(YANG Zhong-min, WANG Kai,SUN Xiu, et al. Grain boundary ferrite morphology and grain boundary crackin Nb/Ti microalloyed steel billets[J]. Iron and Steel, 2018,53(11):70.
[2] 师仲然, 赵和明, 杨海峰, 等. 轧制工艺对V-N-Ti钢焊接粗晶热影响区组织和韧性的影响[J]. 中国冶金, 2021, 31(3): 66. (SHI Zhong-ran, ZHAO He-ming, YANG Hai-feng, et al. Effect of rolling process on microstructure and toughness of coarse grain heat affected zone of V-N-Ti steel[J]. China Metallurgy, 2021, 31(3): 66.)
[3] 杜辰伟,兰鹏,汪春雷,等. 微合金钢连铸坯表面裂纹敏感性预测模型[J]. 中国冶金, 2019, 29(7): 23. (DU Chen-wei, LAN Peng,WANG Chun-lei,et al. Prediction model for surface cracking sensitivity of micro-alloyed steel continuous casting slab[J]. China Metallurgy, 2019, 29(7): 23.)
[4] 陈波涛, 张泽峰, 邢立东, 等. 含钛微合金钢凝固过程中TiN的析出行为分析[J]. 连铸, 2021 (3): 28. (CHEN Bo-tao, ZHANG Ze-feng, XING Li-dong, et al. Analysis of TiN precipitation during solidification of Ti-containing micro-alloy steel[J].Continuous Casting, 2021 (3): 28.)
[5] 程汉,陈万超,张恒华.微合金钢中Mo对α-Fe/NbC界面影响的第一性原理研究[J].上海金属,2020,42(5):94.(CHENG Han,CHEN Wan-chao,ZHANG Heng-hua. First-principle study on influence of Mo on α-Fe /NbC interface in micro-alloyed steel[J]. Shanghai Metals,2020,42(5):94.)
[6] 罗刚,梁祥祥,张剑桥,等.中断淬火的温度对淬火-配分低铬铁素体不锈钢组织和性能的影响[J].上海金属,2021,43(5):45.(LUO Gang, LIANG Xiang-xiang, ZHANG Jian-qiao. Effect of temperatures at the time of quenching interruption on microstructure and properties of a low-chromium ferritic stainless steel quenched and partitioned[J]. Shanghai Metals, 2021,43(5):45.)
[7] 姚浩, 张立峰, 任强, 等. 冷却速率对Ti-Zr处理钢针状铁素体转变的影响[J]. 钢铁, 2021, 56(11): 96. (YAO Hao, ZHANG Li-Feng, REN Qiang, et al. Effect of cooling rates on transformation of acicular ferrite in a Ti-Zr treated steel[J]. Iron and Steel, 2021, 56(11): 96.)
[8] 侯雨阳, 成国光. 铁素体不锈钢铸坯凝固特性及等轴晶率控制[J]. 连铸, 2021 (3): 7. (HOU Yu-yang, CHENG Guo-guang. Solidification characteristics and control measures of equiaxed zone ratio of ferritic stainless steel slab[J].Continuous Casting,2021 (3): 7.)
[9] 王晓东,高文刚,谭志福.铁素体轧制Ti-IF钢冲压成形条纹缺陷原因分析与改进措施[J].轧钢,2021,38(4):38.(WANG Xiao-dong,GAO Wen-gang,TAN Zhi-fu. Cause analysis of stripe defect generated on ferrite rolled Ti-IF steel strip after stamping and its countermeasures[J].Steel Rolling, 2021, 38(4): 38.)
[10] 杨浩, 邵伟, 曲锦波.微钛处理钢中的夹杂物特征及其对奥氏体晶粒尺寸和相变组织的影响[J]. 热加工工艺,2021, 50(7):48.(YANG Hao, SHAO Wei, QU Jin-bo. Inclusion characteristics and its effect on austenite grain size and transformed microstructure in Ti-treated steel[J]. Hot Working Technology, 2021,50(7):48.)
[11] 杨才福.钒微合金化钢的技术进展与应用[J].钢铁研究学报,2020,32(12):1029.(YANG Cai-fu. Recent development and applications of vanadium microalloying technology[J]. Journal of Iron and Steel Research, 2020,32(12):1029.)
[12] 张彩军, 武绍文, 吴哲, 等. 低碳钢铁素体相变析出行为[J].金属热处理,2019,44(6):51.(ZHANG Cai-jun, WU Shao-wen, WU Zhe, et al. Precipitation behavior of ferrite transformation of low carbon steel[J]. Heat Treatment of Metals, 2019,44(6):51.)
[13] Dube C A, Aaronson H I, Mehl R F. La formation de la ferrite proeutectoide dans les aciers au carbone[J]. Revue De Métallurgie, 1958, 55(3):201.
[14] 吴开明. 钢铁材料中铁素体的三维形态与分析[J]. 中国体视学与图像分析, 2017,22(2):119.(WU Kai-ming. Three-dimensional morphology and analysis of ferrite in steels[J]. Chinese Journal of Stereology and Image Analysis, 2017,22(2):119.)
[15] Spanos G, Wilson A W, Kral M V. New insights into the widmanstätten proeutectoid ferrite transformation: Integration of crystallographic and three-dimensional morphological observations[J]. Metallurgical and Materials Transactions A, 2005, 36(5):1209.
[16] Inkon B J, Mulvihill M, Mobus G.3D determination of grain shape in a FeAl-based Nanocomposite by 3D FIB tomography[J]. Scripta Materialia,2001, 45(7):753.
[17] Villinger C,Gregorius H,Kranz C,et al.FIB/SEM tomography with TEM-like resolution for 3D Imaging of high-pressure frozen cell[J]. Histochemistry and Cell Biology,2012,138:549.
[18] Uchic M D, Groeber M A, Dimiduk D M, et al. 3D micro structural characterization of nickel superalloys via serial-sectioning using a dual beam FIB-SEM[J].Scripta Materialia,2006,55(1):23.
[19] Zankel A, Wagner J,Poelt Peter. Serial sectioning methods for 3D investigations in materials science[J]. Micron, 2014,62:66.
[20] Groeber M A, Haley B K, Uchic M D. 3D Reconstruction and characterization of polycrystalline microstructures using a FIB-SEM system[J]. Materials Characterization, 2006, 57(4):259.
[21] Mingard K P, Jones H G, Gee M G. Metrological challenges for reconstruction of 3-D microstructures by focused ion beam tomography methods[J]. Journal of Microscopy, 2014, 253(2):93.
[22] Fan G H, Zhang Y B, Driver J H, et al. Oriented growth during recrystallization revisited in three dimensions[J]. Scripta Materialia, 2014, 72/73(2):9.
[23] 王会珍, 杨平, 毛卫民. 板条状马氏体形貌和惯习面的3D-EBSD分析[J]. 材料工程, 2013, 41(4):74.(WANG Hui-zhen, YANG Ping, MAO Wei-min. 3D EBSD analysis of morphology and habit plane for lath martensite[J]. Journal of Materials Engineering, 2013, 41(4):74.)
[24] Möbus G, Inkson B J. Three-dimensional reconstruction of buried nanoparticles by element-sensitive tomography based on inelastically scattered electrons[J]. Applied Physics Letters, 2001, 79(9):1369.
[25] 武绍文, 张彩军, 吴哲. 利用聚焦离子束技术构建铁素体三维形态[J].钢铁, 2019,54(1):85.(WU Shao-wen, ZHANG Cai-jun, WU Zhe. Construction of three-dimensional morphology of ferrite by focused ion beam technique[J]. Iron and Steel, 2019,54(1):85.)
[26] 成林.低碳微合金高强度钢中铁素体的形核、三维形态与长大动力学[D]. 武汉:武汉科技大学,2013.(CHENG Lin. The Nucleation, Three Dimensional Morphology and Growth Kinetics in Low Carbon High Strength Micro-alloyed Steels[D]. Wuhan:Wuhan University of Science and Technology,2013)
[27] Hillert M. Diffusion in growth of bainite[J]. Metallurgical and Materials Transactions A, 1994, 25(9):1957.
[28] Hillert M. Diffusion and interface control of reactions in alloys[J]. Metallurgical Transactions A, 1975, 6(1):5.
[29] Simonen E P, Aaronson H I, Trivedi R. Lengthening kinetics of ferrite and bainite sideplates[J]. Metallurgical Transactions, 1973, 4(5):1239.
[30] Trivedi R, Pound G M. Effect of concentration-dependent diffusion coefficient on the migration of interphase boundaries[J]. Journal of Applied Physics, 1967, 38(9):3569.
[31] Wells C, Batz W, Mehl R F. Diffusion coefficient of carbon in austenite[J]. Trans AIME, 1950,188:553.
[32] Ågren J.A revised expression for the diffusivity of carbon in binary Fe-C austenite[J]. Scr Metall, 1986,20:1507.
[33] 武绍文.晶内铁素体三维形貌分析与生长动力学研究[D].唐山:华北理工大学,2019.(WU Shao-wen. Three-dimensional Morphology Analysis and Growth Kinetics of Intragranular Ferrite[D]. Tangshan:North China University of Science and Technology,2019.)