Flatness control analysis of tension levelling process based on finite element method |
JIN Hao-yue, SUN Jie, WEI Zhen, WANG Long-jun, HOU Fan, ZHANG Dian-hua |
State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, Liaoning, China |
|
|
Abstract Flatness is an important index to judge the quality of strip steel. The common flatness defects are edge wave,middle wave,quarter wave and so on,which is essentially the uneven distribution of residual stress in the bandwidth. Wave defects can be effectively eliminated by the joint action of tension roller, bending roller and straightening roller. In the straightening process,plastic elongation occurs on strip under the effect of tension which is below yield strength. The flatness and quality of strip can be significantly improved. However,in the design and application of the tension leveler,the adjustment of tension leveler parameters is mostly based on experience and lacks theoretical guidance. To quantitatively analyze the improvement effect of tension leveler with different process parameters on the straightening of wave defects and increase the straightening effect of tension leveler in actual production,the tension levelling process of strip steel in a 1 450 mm cold pickling-rolling line was analyzed by the finite element software ANSYS/LS-DYNA which based on the three-dimensional elastic-plastic finite element method. The influence of tension and roll-intermesh on the flatness of straightened strip with initial flatness defect was analyzed. The influences of intermesh and tension on the flatness of strip with initial edge wave or middle wave shape defects are consistent. The results shown that wave defects of strip steel can be significantly improved by tension levelling. The intermesh of straightening roll is the main influencing factor,with the increase of intermesh the type of strip defect changes from edge wave to straight,and with the further increase of intermesh for straightening roller,the edge wave defect appeared again. With the increase of inlet tension,the type of strip defect changes from edge wave to medium wave after tension levelling.
|
Received: 15 December 2021
|
|
|
|
[1] 陈梅,李胜祗,阎军,等. 薄带拉伸弯曲矫直技术研究进展[J]. 安徽工业大学学报(自然科学版),2004(1):11.(CHEN Mei,LI Sheng-zhi,YAN Jun,et al. Development of the thin strip tension-leveling[J]. Journal of Anhui University of Technology(Natural Science),2004(1):11.) [2] 王国栋,刘振宇,张殿华. RAL关于钢材热轧信息物理系统的研究进展[J]. 轧钢,2021,38(1):1.(WANG Guo-dong,LIU Zhen-yu,ZHANG Dian-hua. Research progress on the cyber-physical system of steel hot rolling in RAL[J]. Steel Rolling,2021,38(1):1) [3] 王国栋. 中国钢铁轧制技术的进步与发展趋势[J]. 钢铁,2014,49(7):23.(WANG Guo-dong. Progress and developing trends of steel rolling technology in China[J]. Iron and Steel,2014,49(7):23.) [4] 张清东,周岁,银家琛. 薄带材浪形缺陷生成与拉伸矫直过程数值仿真[J]. 工程科学学报,2015,37(6):789.(ZHANG Qing-dong,ZHOU Sui,YIN Jia-chen. Numerical simulation on the wave-shaped defect generation and tension straightening process of thin strips[J]. Chinese Journal of Engineering,2015,37(6):789.) [5] 李淑华,李同庆. 拉弯矫直理论和带材残余延伸率的计算[J]. 上海金属,2001,23(6):30.(LI Shu-hua,LI Tong-qing. Theory on stretch-bend straightening and calculation for the residual elongation of strip[J]. Shanghai Metals,2001,23(6):30.) [6] 陈兵,舒建华,郭瑞娟,等. 拉伸弯曲矫直理论及仿真研究综述[J]. 重型机械,2013(3):1.(CHEN Bing,SHU Jian-hua,GUO Rui-juan,et al. Theoretical research and simulation of stretch bending leveling mechanism[J]. Heavy Machinery,2013(3):1.) [7] Patula E J. The tension-roller-leveling process—Elongation and power loss[J]. Journal of Engineering for Industry,1979,101(3):269. [8] 肖林,苏逢荃,邹家祥. 金属带材拉伸弯曲矫直过程简化解析分析之二——理想弹塑性带材在1个弯曲辊上的拉弯过程分析[J]. 北京科技大学学报,2000,22(1):75.(XIAO Lin,SU Feng-quan,ZOU Jia-xiang. Theoretical investigation into continuous tension leveling process of metal strip(2)—Analysis on the tension leveling process of elastic-perfect plastic metal strip over the first bending roll[J]. Journal of University of Science and Technology Beijing,2000,22(1):75.) [9] Misaka Y,Masui T. Shape correction of steel strip by tension leveller[J]. Journal of Japan Society for Technology of Plasticity,1978,18(8):475. [10] Huh H,Lee H,Park S,et al. The parametric process design of tension levelling with an elasto-plastic finite element method[J]. Journal of Materials Processing Technology,2001,113(1):714. [11] Yoshida F,Urabe M. Computer-aided process design for the tension levelling of metallic strips[J]. Journal of Materials Processing Technology,1999,90:218. [12] Morris J W,Hardy S J,Thomas J T. Some fundamental considerations for the control of residual flatness in tension levelling[J]. Journal of Materials Processing Technology,2002,120(1/2/3):385. [13] Morris J W,Hardy S J,Thomas J T. Effects of tension levelling process parameters on cold rolled strip characteristics using a designed factorial analysis approach[J]. Ironmaking and Steelmaking,2005,32(5):443. [14] Morris J W,Hardy S J,Lees A W,et al. Formation of residual stresses owing to tension levelling of cold rolled strip[J]. Ironmaking and Steelmaking,2001,28(1):44. [15] 李生存,陈景辉,王浩宇. 拉矫机工作辊异常磨损和轴头烧损的对策[J]. 中国冶金,2018,28(10):51.(LI Sheng-cun,CHEN Jing-hui,WANG Hao-yu. Countermeasures for inordinate wearing and axle neck burning of work roll in tension leveler[J]. China Metallurgy,2018,28(10): 51.) [16] 张清东,周岁,张晓峰,等. 薄带钢拉矫机浪形矫平过程机理建模及有限元验证[J]. 机械工程学报,2015,51(2):49.(ZHANG Qing-dong,ZHOU Sui,ZHANG Xiao-feng,et al. Analytic modeling and corroborating by FEM of tension leveling process of thin buckled steel strip[J]. Journal of Mechanical Engineering,2015,51(2):49.) [17] 孙朝阳,张栋,张清东,等. 不锈钢带拉矫过程变形行为的数值模拟研究[J]. 钢铁,2010,45(8):51.(SUN Chao-yang,ZHANG Dong,ZHANG Qing-dong,et al. Numerical simulation on the deformation behavior of tension levelling process for stainless steel strip[J]. Iron and Steel,2010,45(8):51.) [18] 张清东,常铁柱,黄河,等. 全硬薄宽镀锌带钢的拉伸弯曲矫直工艺[J]. 钢铁,2007,42(6):47.(ZHANG Qing-dong,CHANG Tie-zhu,HUANG He,et al. Tension leveling for wide and thin galvanized full hard steel strip[J]. Iron and Steel,2007,42(6):47.) [19] 张亮,陈兵,付光,等. 冷轧拉伸弯曲矫直机工艺参数设定影响因素研究[J]. 轧钢,2014,31(6):5.(ZHANG Liang,CHEN Bing,FU Guang,et al. Research of influence factors on process parameters setting of cold rolling tension leveller[J]. Steel Rolling,2014,31(6):5.) [20] Mathieu N,Dimitriou R,Parrico A,et al. Flatness defects after bridle rolls:A numerical analysis of leveling[J]. International Journal of Material Forming,2013,6(2):255. [21] 刘东冶,何安瑞,邵健,等. 辊式矫直过程弯辊量对边浪影响的仿真分析[J]. 中国冶金,2021,31(10):81.(LIU Dong-ye,HE An-rui,SHAO Jian,et al. Simulation analysis for influence of roll bending on edge wave in roll straightening process[J]. China Metallurgy,2021,31(10):81.) [22] Mathieu N,Potier-Ferry M,Zahrouni H. Reduction of flatness defects in thin metal sheets by a pure tension leveler[J]. International Journal of Mechanical Sciences,2017,122:267. |
[1] |
JIN Fengwei,FENG Ying,CHEN Zhaoyu,SUN Wenquan,ZHANG Yongjun. Pre-alculation optimization of finishing delivery temperature of hot strip head based on data driven[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2022, 34(7): 655-663. |
[2] |
YU Meng, WANG Chun-hai, ZHANG Xiao-feng, WEN Jie, WANG Yong-qiang, ZHANG Qing-dong. Shape warping behavior of stainless steel/carbon steel clad plate during temper rolling[J]. Iron and Steel, 2022, 57(7): 106-114. |
[3] |
QIAO Li-zhu, ZHANG Wei-li, PENG Han-zhong, WU Sheng-li. Influence of desorption parameters on regeneration process and regeneration effect of activated coke[J]. Iron and Steel, 2022, 57(6): 159-166. |
[4] |
WU Hai-long, CEN Chuan-fu, CAO Yu, ZHONG Shan, LIU Ying, LU Hao-jian. Numerical simulation of temperature field of continuous casting billet during transporting to direct rolling[J]. CONTINUOUS CASTING, 2022, 41(5): 1-9. |
[5] |
WANG En-rui, CHEN Zi-gang, LIU Feng-lin, LIU Tian-wu, ZHANG Ming. Oxide scale structure of hot rolled structural steel and its effect on pickling quality[J]. Iron and Steel, 2022, 57(3): 71-78. |
[6] |
LI Wei-gang, XU Kang, LI Jin-ling, ZHAO Yun-tao. Research and application of surface defect recognition algorithm for hot rolled strip[J]. Iron and Steel, 2022, 57(10): 139-147. |
|
|
|
|