高氮不锈轴承钢碳化物分布与高温断裂机制

doi:10.13228/j.boyuan.issn0449-749x.20210796

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (6220 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract The high temperature fracture behavior of high nitrogen stainless bearing steel was studied by high temperature tensile test. The distribution characteristics of carbide in 170 ℃ and 470 ℃ tempered steel were investigated. The tensile fracture, microstructure evolution and carbide distribution law were analyzed. The results show that with the tempering temperature increasing from 170 ℃ to 470 ℃, the carbide larger than 0.8 μm in high nitrogen steel increases significantly, M₂₃C₆ strengthening increment increases by 2.59 MPa, and solution strengthening increment decreases by 118.82 MPa. The tensile strength of 470 ℃ tempering steel decreases at room temperature, and the tensile fracture behavior of the steel at room temperature is quasi-cleavage and a small amount of tear dimms. When the tensile temperature is increased to 300 ℃, the fracture surface of sample is equiaxed dimple, and the size of fracture source carbide of the 170 ℃ and 470 ℃ tempering samples is 2.8-3.6 μm and 5.5-6.7 μm, respectively. The tensile fracture at 450 ℃ is characterized by plastic-pore dimples, and the size of fracture source carbide at 170 ℃ and 470 ℃ is 2.7-3.4 μm and 5.8-6.4 μm, respectively. When the tensile temperature increases from 300 ℃ to 450 ℃, the effect of solution strengthening and dislocation strengthening is weakened, the interatomic bonding energy of metal decreases, the discontinuous stress distribution between carbide and matrix increases the deformation incompatibility, and the carbides bear higher stress then fracture occurs. Under the action of pure heat, the percentage of carbides of 0.5-0.8 μm increased. Under the action of thermodynamic coupling, dislocation proliferation caused by stress in steel provides channels for carbon diffusion, and 0.2-0.8 μm carbides are nucleated at grain boundaries and dislocation lines. The crack propagates rapidly along the maximum shear direction at angle of 45° with the tensile direction and then fractures. Finally, serrated fracture is formed. The increase of small carbides hinders dislocation slip and results in reduced plasticity. The large size carbides in steel distribute unevenly among the carbides to form large deformation plastic holes and increase the plasticity of steel.

Key words： high nitrogen stainless bearing steel high temperature fracture plastic high temperature hardness carbide

Received: 27 December 2021

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	CAO Fang
	YANG Mao-sheng
	YANG Shu-feng
	LI Jing-she
	LUO Zhi-qiang
	LIU Wei

Cite this article:

CAO Fang,YANG Mao-sheng,YANG Shu-feng等. Carbide distribution and high-temperature fracture mechanism of high nitrogen stainless bearing steel[J]. Iron and Steel, 2022, 57(6): 132-142.

URL:

http://www.chinamet.cn/Jweb_gt/EN/10.13228/j.boyuan.issn0449-749x.20210796 OR http://www.chinamet.cn/Jweb_gt/EN/Y2022/V57/I6/132

[1] 钟顺思,王昌生.轴承钢[M].北京:冶金工业出版社, 2000. (ZHONG Shun-Si, WANG Chang-sheng. Bearing Steel[M].Beijing:Metallurgical Industry Press, 2000.)
[2] Pfaffenberger E, Tarrantini P. High temperature corrosion resistant bearing steel development[C]//29th Joint Propulsion Conference and Exhibit. Monterey:American Institute of Aeronautics and Astronautics,1993.
[3] 王坤,胡锋,周雯,等.轴承钢研究现状及发展趋势[J].中国冶金,2020,30(9):119.(WANG Kun, HU Feng, ZHOU Wen, et al. Research status and development trend of bearing steel[J].China Metallurgy, 2020,30(9):119.)
[4] 徐林红, 罗海文. 广义帕累托分布在轴承钢夹杂物评价方面的应用[J]. 中国冶金, 2021, 31(6): 19.(XU Lin-hong, LUO Hai-wen. Application of generalized pareto distribution in evaluation of inclusions in bearing steels[J]. China Metallurgy, 2021, 31(6): 19.)
[5] 冯路路, 吴开明, 乔文玮,等. 轴承钢珠光体球化的研究现状及发展趋势[J]. 中国冶金, 2020, 30(9): 110. (FENG Lu-lu, WU Kai-ming, QIAO Wen-wei, et al. Research status and developing tendency of bearing steel spheroidization of pearlite[J]. China Metallurgy, 2020, 30(9): 110.)
[6] 尤蕾蕾, 王红伟, 侯俊, 等. G8Cr15轴承钢的工业化应用分析[J]. 中国冶金, 2020, 30(9): 91. (YOU Lei-lei, WANG Hong-wei, HOU Jun, et al. Analysis of industrial application of G8Cr15 bearing steel[J]. China Metallurgy, 2020, 30(9): 91.)
[7] 李永超, 卢彩玲, 左健成, 等. 轴承钢中间包首炉大型夹杂物分析及控制[J]. 连铸, 2021(3): 35. (LI Yong-chao, LU Cai-ling, ZUO Jian-cheng, et al. Analysis and control of macro-inclusion of bearing steel in tundish first heat[J]. Continuous Casting, 2021(3): 35.)
[8] 李权辉, 陶镳, 徐志祥, 等. 连铸保护渣对GCr15轴承钢铸坯渣沟缺陷的影响[J]. 连铸, 2021(1): 55. (LI Quan-hui, TAO Biao, XU Zhi-xiang, et al. Effect of mold slag on slag-scratch on continuous casting billet of GCr15 bearing steel[J]. Continuous Casting,2021(1): 55.)
[9] 肖微, 包燕平, 王敏, 等. 非铝脱氧GCr15轴承钢的夹杂物演变和控制[J]. 钢铁, 2021, 56(1): 37. (XIAO Wei, BAO Yan-ping, WANG Min, et al. Inclusions evolution and control of non-aluminum deoxidized GCr15 bearing steel[J]. Iron and Steel, 2021, 56(1): 37.)
[10] 刘吉刚, 许晓红. 以抗疲劳性能提升为目标的高碳轴承钢质量改善[J]. 中国冶金, 2020, 30(9): 75. (LIU Ji-gang, XU Xiao-hong. Quality improvements of high carbon bearing steel for increasing anti-fatigue performance[J]. China Metallurgy, 2020, 30(9): 75.)
[11] 杨延辉, 王琛, 范海东, 等. 100Cr6轴承钢的超高周疲劳性能研究[J]. 中国冶金, 2020, 30(9): 41. (YANG Yan-hui, WANG Chen, FANG Hai-dong, et al. Research of ultra-high cycle fatigue property of 100Cr6 bearing steel[J]. China Metallurgy, 2020, 30(9): 41.)
[12] 刘烨, 尹青, 李锋, 等. 超长疲劳寿命轴承钢的质量评价[J]. 中国冶金, 2020, 30(9): 37. (LIU Ye, YIN Qing, LI Feng, et al. Assessment on quality of bearing steel with ultra-long fatigue life[J]. China Metallurgy, 2020, 30(9):37.)
[13] 吕皓天, 杨亮, 陈浩, 等. 轴承钢的滚动接触疲劳与寿命预测模型[J]. 中国冶金, 2020, 30(9): 24. (LÜ Hao-tian, YANG Liang, CHEN Hao, et al. Rolling contact fatigue and life prediction model of bearing steel[J]. China Metallurgy, 2020, 30(9): 24.)
[14] 付悍巍, 崔一南, 张弛,等. 轴承钢滚动接触疲劳研究进展[J]. 中国冶金, 2020, 30(9): 11.(FU Han-wei, CUI Yi-nan, ZHANG Chi, et al. Research progress of rolling contact fatigue of bearing steels[J]. China Metallurgy, 2020, 30(9): 11.)
[15] Vogt J B. Fatigue properties of high nitrogen steels[J]. Journal of Materials Processing Technology, 2001, 117(3):364.
[16] Simmons J W. Overview: High-nitrogen alloying of stainless steels[J]. Materials Science and Engineering A, 1996, 207(2):159.
[17] 贾钰泽. 高氮马氏体不锈轴承钢的碳氮化物演变与强韧性能的研究[D]. 昆明:昆明理工大学,2015.(JIA Yu-ze. Study on Carbonitride Evolution and Strength and Toughness of High Nitrogen Martensitic Stainless Bearing Steel[D]. Kunming:Kunming University of Science and Technology, 2015)
[18] 郝宏伟,杨卯生,孙世清,等.高氮不锈轴承钢的微动磨损性能[J].钢铁研究学报,2016,28(7):61.(HAO Hong-wei, YANG Mao-sheng, SUN Shi-qing, et al.Friction and wear performance of high nitrogen stainless bearing steel[J].Journal of Iron and Steel Research,2016,28(7):61.)
[19] 张志慧. 高氮轴承钢组织演变与疲劳行为的研究[D].石家庄:河北科技大学,2018.(ZHANG Zhi-hui. Study on Microstructure Evolution and Fatigue Behavior of High Nitrogen Bearing Steel[D].Shijiazhaung: Hebei University of Science and Technology,2018.)
[20] 吝欢,杨卯生,舒佰坡,等.高氮不锈轴承钢高温旋弯疲劳性能及损伤机制[J].钢铁研究学报,2019,31(5):475.(LIN Huan, YANG Mao-sheng, SHU Bai-po, et al. High temperature rotating bending fatigue behavior and damage mechanism of high nitrogen stainless bearing steel[J].Journal of Iron and Steel Research,2019,31(5):475.)
[21] HUAN Lin, YANG Mao-sheng, SHU Bai-po, et al. Fretting wear behaviour of high-nitrogen stainless bearing steel under lubrication condition[J]. Journal of Iron and Steel Research International, 2020, 27(7):18.
[22] 宋超伟, 田勇, 王昊杰, 等. 预氮化对Cr-Co-Mo-Ni轴承钢渗碳层组织和性能的影响[J]. 中国冶金, 2020, 30(9): 83.(SONG Chao-wei, TIAN Yong, WANG Hao-jie, et al. Effect of preliminary nitriding treatment on microstructure and mechanical properties of carburized layer of Cr-Co-Mo-Ni bearing steel[J]. China Metallurgy, 2020, 30(9): 83.)
[23] Merchant H D, Murty G S, Bahadur S N, et al. Hardness-temperature relationships in metals[J]. Journal of Materials Science, 1973, 8(3):437.
[24] 杨晨星,吴志伟,杨卯生,等.镍铬轴承合金固溶时效态组织特征与力学性能[J].钢铁研究学报,2020,32(3):242.(YANG Chen-xin, WU Zhi-wei, YANG Mao-sheng, et al. Microstructure and mechanical properties of Ni-Cr bearing alloy in solution aging treatmen[J].Journal of Iron and Steel Research,2020,32(3):242.)
[25] 贾钰泽, 杨卯生, 周晓龙,等. 回火温度对高氮轴承钢碳化物演变及硬度的影响[J]. 钢铁,2015, 50(6):81.(JIA Yu-ze, YANG Mao-sheng, ZHOU Xiao-long, et al. Effect of tempering temperature on the evolution of carbide and hardness of high-nitrogen bearing steel[J].Iron and Steel,2015, 50(6):81.)
[26] 刘庆冬,刘文庆,王泽民,等.回火马氏体中合金碳化物的3D原子探针表征Ⅰ.形核[J].金属学报,2009,45(11):1281.(LIU Qing-dong, LIU Wen-qing, WANG Ze-min, et al.3D atom probe characterization of alloy carbides in tempering martenite Ⅰ. Nucleation[J].Acta Metallurgica Sinica,2009,45(11):1281.)
[27] 刘庆冬,彭剑超,刘文庆,等.回火马氏体中合金碳化物的3D原子探针表征 Ⅱ.长大[J].金属学报,2009,45(11):1288.(LIU Qing-dong, PENG JIan-chao, LIU Wen-qing, et al.3D atom probe characterization of alloy carbides in tempering martenite Ⅱ.Growth[J].Acta Metallurgica Sinica,2009,45(11):1288.)
[28] 刘庆冬,褚于良,彭剑超,等.回火马氏体中合金碳化物的3D原子探针表征 Ⅲ.粗化[J].金属学报,2009,45(11):1297.(LIU Qing-dong, CHU Yu-liang, PENG Jian-chao, et al. 3D atom probe characterization of alloy carbides in tempering martenite Ⅲ.Coarsening[J].Acta Metallurgica Sinica,2009,45(11):1297.)
[29] 雍岐龙. 钢铁材料中的第二相[M]. 北京: 冶金工业出版社, 2006.(YONG Qi-long. Second Phase in Iron and Steel[M].Beijing: Metallurgical Industry Press,2006.)
[30] WANG C, WANG M, JIE S, et al. Effect of microstructure refinement on the strength and toughness of low alloy martensitic steel[J]. Journal of Materials Science and Technology, 2007, 23(5):659.