低温取向硅钢硅酸镁底层形成过程

doi:10.13228/j.boyuan.issn0449-749x.20220120

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (9142 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract The forsterite film of oriented silicon steel is an important part of product structure. The control of forsterite film is not only a process difficulty, but also a bottleneck of improvement of product performance. However,there are few previous studies on the formation of forsterite film, and there is a lack of theoretical support for the development and quality improvement of thin standardized high-performance products of high magnetic induction oriented silicon steel. Therefore, the formation process of forsterite film in grain-oriented silicon steel manufactured by the acquired inhibitor method was simulated by a high temperature annealing interruption experiment, and the microstructure and composition evolution of forsterite film during annealing were analyzed. The reaction formation process of forsterite film during high temperature annealing was clarified. The Mg₂SiO₄ particles nucleate on the surface of the steel at about 900 ℃ and grow up as the increase of annealing temperature. Up to 1 050 ℃, the Mg₂SiO₄ particles begin to become compact, and the densification process finishes at about 1 100 ℃. The key temperature for the formation of forsterite film is 900-1 100 ℃. In addition, the Al₂O₃·MgO spinel is formed under the forsterite film that can make a "pinning effect" on the forsterites film. During the formation of forsterite film, the Mg²⁺ of MgO diffuses from the surface to the oxide film and reacts with SiO₂. At the same time, SiO₂ in the oxide film matures. The content of Al released by AlN decomposition in the substrate above 1 000 ℃ reacts with Mg₂SiO₄ to form spinel. The excellent forsterite film structure is formed by the original decarburization annealing oxide film surface layer 1 μm to form dense Mg₂SiO₄ and the rest 2-3 μm thickness into a certain amount of ellipsoidal Al₂O₃· MgO spinel for "pinning" bonding layer. Its main control directions are, improving the activity of oxide film, selecting high activity MgO, adding low melting point reaction additives, etc.

Key words： grain-oriented silicon steel forsterite film oxide film high-temperature annealing spinel

Received: 21 February 2022

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WANG Xian-hui
	LIU Zhao-yue
	LI Rui-feng
	GAO Qian
	TENG Ren-hao

Cite this article:

WANG Xian-hui,LIU Zhao-yue,LI Rui-feng等. Formation process of forsterite film in grain-oriented silicon steel manufactured by acquired inhibitor method[J]. Iron and Steel, 2022, 57(6): 150-158.

URL:

http://www.chinamet.cn/Jweb_gt/EN/10.13228/j.boyuan.issn0449-749x.20220120 OR http://www.chinamet.cn/Jweb_gt/EN/Y2022/V57/I6/150

[1] 何忠治,赵宇,罗海文. 电工钢[M]. 北京: 冶金工业出版社, 2012. (HE Zhong-zhi. Electrical Steel[M]. Beijing: Metallurgical Industry Press, 2012.)
[2] 熊野知二,山崎幸司. 日本公开特许公报,1996-平8-143961.
[3] 户田宏郎,渡边誠. 日本公开特许公报,2002–129235.
[4] Konno T, Suga Y, Nozawa T, et al. The effects of glass film on total loss of grain-oriented 3% silicon iron[J]. Journal of Applied Physics, 1985, 57(1): 4124.
[5] 黎先浩孟小涛,赵鹏飞,等. 高磁感取向硅钢研发现状与展望[J]. 中国冶金, 2019, 29(1): 1.(LI Xian-hao,MENG Xiao-tao,ZHAO Peng-fei,et al. Present status and future prospect of high permeability grain-oriented silicon steel[J]. China Metallurgy, 2019, 29(1): 1.)
[6] 张波, 孟利, 张宁, 等. 超薄取向硅钢的研究进展[J]. 钢铁, 2020, 55(10): 96.(ZHANG Bo, MENG Li, ZHANG Ning, et al. Research progress of ultra-thin grain-oriented silicon steel[J]. Iron and Steel, 2020, 55(10): 96.)
[7] Hammer B, Riediger C, Hastenrath M, et al. Interactions between the inhibitor phases, secondary grain growth and glass-film formation in HGO electrical steel[J]. Journal of Magnetism and Magnetic Materials, 1992, 112(1/3):162.
[8] Puzhevich R B, Dukhnov A G, Samsikov E A, et al. Effect of the ground layer on the magnetic properties of highly permeable silicon steel[J]. Metal Science and Heat Treatment, 1986, 28(6): 435.
[9] Fujii H, Yamazaki S, Nagashima T, et al. Glass film structure of grain-oriented silicon steel using aluminum nitride as an inhibitor[J]. Journal of Materials Engineering and Performance, 1994, 3(2): 214.
[10] FU Y J, JIANG Q W, WANG B C, et al. Morphologies and influential factors of forsterite film in grain-oriented silicon steel[J]. Journal of Iron and Steel Research International, 2013, 20(11): 105.
[11] Cunha M A, Cesar M G. Forsterite film formation and grain growth in 3% Si steel[J]. IEEE Transactions on Magnetics, 1994, 30(6): 4890.
[12] 刘小飞, 黎先浩, 赵松山, 等. Sn和冷轧板厚度对取向硅钢初次再结晶组织和织构影响[J]. 中国冶金, 2021, 31(10): 34.(LIU Xiao-fei, LI Xian-hao, ZHAO Song-shan, et al. Effect of Sn and sheet thickness on primary recrystallized microstructure and texture in cold-rolled grain-oriented silicon steel[J]. China Metallurgy, 2021, 31(10): 34.)
[13] 张波, 孟利, 张宁, 等. 退火温度对超薄取向硅钢织构及磁性能的影响[J]. 钢铁, 2021, 56(3): 29. (ZHANG Bo, MENG Li, ZHANG Ning, et al. Effect of recrystallization annealing temperature on texture and magnetic properties of ultra-thin oriented-silicon steel[J]. Iron and Steel, 2021, 56(3): 29.)
[14] Sehoon J, Min S K, Park J, et al. A TEM study of oxide layers formed during decarburization annealing of electrical steel[J]. ISIJ International, 2011, 51(7): 1163.
[15] Masui H, Shiozaki M, Takahashi N, et al. Grain Oriented Silicon Steel Sheet Having Excellent Primary Film Properties: USA, US5565272 A[P]. 1996-10-15.
[16] Davies M J, Moses A J, Snell D. Measurement of coatings and surface oxide layers on grain oriented electrical steel[J]. Ironmaking and Steelmaking, 1998, 25(2): 124.
[17] Toda H, Sato K, Komatsubara M. Characterization of interna oxide layers in 3%Si grain oriented steel by electrochemical methods[J]. Journal of Materials Engineering and Performance, 1997, 6(6): 722.
[18] Cesar M G, Mantel M J. Effect of the temperature and dew point of the decarburization process on the oxide subscale of a 3% silicon steel[J]. Journal of Magnetism and Magnetic Materials, 2003, 254/255: 338.
[19] Mitchell M, Jackson D, James P F. Preparation and characterisation of forsterite (Mg₂SiO₄) aerogels[J]. Journal of Non-Crystalline Solids, 1998, 225(1): 125.
[20] 常正昇, 张乔英, 杨克枝, 等. 板坯连铸工艺参数对取向硅钢铸坯中心等轴晶率的影响[J].中国冶金, 2020, 30(1): 58.(CHANG Zheng-sheng, ZHANG Qiao-ying, YANG Ke-zhi,et al. Effects of continuous casting process parameters on central equiaxed crystal ratio of oriented silicon steel slab[J]. China Metallurgy, 2020, 30(1): 58.)
[21] 钱宇伟,储双杰,杨勇杰, 等. 硅钢级氧化镁反应行为研究[J]. 宝钢技术, 2004(3):40. (QIAN Wei-yu, CHU Shuang-jie, YANG Yong-jie, et al. Research of reaction behavior of silicon-steel grade magnesium oxide[J]. Bao Steel Technology, 2004(3):40.)
[22] 司华青.低温取向硅钢底层质量的研究[D]. 沈阳: 东北大学, 2013. (SI Hua-qing, Study on Quality of Coating Layer of Low Temperature Grain-Oriented Silicon Steel[D]. Shenyang: Northeastern University, 2013.)
[23] 陈勇, 袁磊, 刘涛, 等. 镁橄榄石合成反应动力学研究[J]. 东北大学学报(自然科学版), 2013, 34(1): 111. (CHEN Yong,YUAN Lei,LIU Tao,et al. Study on the reaction kinetics of forsterite synthesis[J]. Journal of Northeastern University(Natural Science), 2013, 34(1): 111.)
[24] 程灵,孟利,郭大为,等. 取向硅钢服役过程中绝缘涂层劣化规律与评价[J].钢铁,2019,54(1):79.(CHENG Ling, MENG Li, GUO Da-wei, et al. Deterioration law and evaluation of insulation coating of grain oriented silicon steel in service[J]. Iron and Steel, 2019,54(1):79.)
[25] 刘吉辉, 李静, 汪琦. 铁尾矿合成镁橄榄石质耐火材料的反应机理[J]. 辽宁科技大学学报, 2009, 32(1): 6. (LIU Ji-hui, LI Jing, WANG Qi. Reaction mechanism of synthesizing magnesia peridotite refractories from iron tailings[J]. Journal of University of Science and Technology Liaoning, 2009, 32(1): 6.)
[26] 卫晓辉,孙加林,孙庚辰. 莫来石的低温合成[J]. 耐火材料, 2008, 42(3): 229. (WEI Xiao-hui, SUN Jia-lin, SUN Geng-chen. Low temperature synthesis of mullite[J]. Refractory, 2008, 42(3): 229.)
[27] 王黎光,王书桓,段阳会,等.铌对低温取向硅钢初次再结晶行为的影响[J],钢铁,2022,57(1):119.(WANG Li-guang, WANG Shu-huan, DUAN Yang-hui, et al. Effect of Nb on primary recrystallization behavior of low temperature grain-oriented silicon steel[J]. Iron and Steel, 2022, 57(1): 119.)