固态脱碳过程中锰钢微观组织演变及力学性能

doi:10.13228/j.boyuan.issn0449-749x.20230010

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (5811 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract High-strength and high-plasticity metal materials have broad application prospects. In order to obtain high-strength and high-plasticity metal materials at the same time,a process strategy of solid state decarburization to produce steel materials with gradient structure is proposed and 2.7%C-medium ferromanganese alloy plate with thickness of 1 mm was selected as the research object. Solid state decarbonization was carried out in H₂O-H₂ atmosphere,the average carbon content of medium manganese steel after decarburization was determined by carbon-sulfur meter,the microstructure and surface oxidation of decarburized medium manganese steel were observed by optical microscope. The simple hot rolling-tempering treatment of decarburized medium manganese steel was carried out,then the mechanical properties of medium manganese steel were measured by universal tensile testing machine. The results show that the amount of decarbonization increases gradually with the increase of decarbonization temperature and the thickness of oxide layer on the surface of medium manganese steel increases gradually with the extension of decarbonization time. The increase of temperature will increase the migration rate of solid solution carbon,so the growth of oxide layer thickness does not increase with the increase of temperature. Therefore,the control of oxidation layer in the process of decarbonization should reasonably adjust the decarbonization temperature,atmosphere conditions and decarbonization time according to the target carbon content. The carbon mass percent of medium manganese steel can be removed from 2.7% to less than 0.5% and the thickness of oxide layer can be controlled below 15 μm at 1 383 K temperature for 50 min. After solid state decarbonization,the structure of the medium manganese steel change gradually from the surface to the interior. The gradient layer gradually migrates to the center with the extension of decarbonization time. The evolution of gradient layer is caused by the migration of solid carbon to the surface of manganese steel during solid decarburization. This mechanism of using solid state decarbonization to create gradual changes in the internal structure of the steel material from surface to interior is conducive to additional strain hardening and high ductility. The strain-hardening ability of solid decarburized medium manganese steel was enhanced significantly after simple hot-rolling and tempering treatment,and the strength and plasticity matching were obtained,with the highest product of strength and ductility of 45.1 GPa·%. Solid state decarbonization method does not destroy the integrity of the material and creates a gradient structure with strong strain hardening effect,which does not exist in homogeneous materials under the same treatment conditions.

Key words： solid state decarbonization gradient structure medium manganese steel microscopic structure mechanical property

Received: 09 January 2023

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	HONG Lukuo
	AI Liqun
	SUN Caijiao
	MENG Fanjun
	WANG Xufeng
	TONG Shuai

Cite this article:

HONG Lukuo,AI Liqun,SUN Caijiao等. Microstructure evolution and mechanical properties of manganese steel during solid state decarburization[J]. Iron and Steel, 2023, 58(6): 118-125.

URL:

http://www.chinamet.cn/Jweb_gt/EN/10.13228/j.boyuan.issn0449-749x.20230010 OR http://www.chinamet.cn/Jweb_gt/EN/Y2023/V58/I6/118

[1] 陈永安,李大赵,闫志杰,等. Fe-Mn-Al-C系轻质高强钢研究现状及展望[J]. 钢铁,2021,56(4):83.(CHEN Y A,LI D Z,YAN Z J,et al. Research status and prospect of Fe-Mn-Al-C lightweight high strength steel[J]. Iron and Steel,2021,56(4):83.)
[2] 孙航,褚晓红,唐梦霞,等. 1 500 MPa级高伸长率双相钢的组织性能分析[J]. 中国冶金,2022,32(4):47.(SUN H,CHU X H,TANG M X,et al. Microstructure and properties analysis of 1 500 MPa grade high elongation dual phase steel[J]. China Metallurgy,2022,32(4):47.)
[3] 侯晓英,刘晓美,郝亮. 不同屈强比的冷轧DP780钢工艺调控技术分析[J]. 中国冶金,2019,29(2):29.(HOU X Y,LIU X M,HAO L. Analysis on process control technology of cold rolling DP780 steel with different yield ratios[J]. China Metallurgy,2019,29(2):29.)
[4] 李麟. 汽车用高强钢的发展与展望[J]. 上海金属,2022,44(3):1. (LI L. Development and prospect of high strength steel for automobile[J]. Shanghai Metals,2022,44(3):1.)
[5] 程丽群,宋凌鹏. 高强塑积汽车钢板的热处理工艺与力学性能研究[J]. 上海金属,2021,43(4):56.(CHENG L Q,SONG L P. Study on heat treatment process and properties of automobile steel plate with high product of strength and elongation[J]. Shanghai Metals,2021,43(4):56.)
[6] 翁宇庆. 中国钢铁材料发展现状及迈入新世纪的对策[J]. 钢铁,2001,36(10):1.(WENG Y Q. Present status and developing strategy of steels at the turn of new century in China[J]. Iron and Steel,2001,36(10):1.)
[7] LIU S L,HU B,LI W,et al. Refined heterogeneous phase unit enhances ductility in quenched ultra-high strength steels[J]. Scripta Materialia,2021,194:113636.
[8] GAO J H,JIANG S H,ZHANG H R,et al. Facile route to bulk ultrafine-grain steels for high strength and ductility[J]. Nature,2021,590:262.
[9] OJIMA M,INOUE J,NAMBU S,et al. Stress partitioning behavior of multilayered steels during tensile deformation measured by in situ neutron diffractio[J]. Scripta Materialia,2012,66(3/4):139.
[10] YANG Z N,JIANG F,WANG Y M,et al. Making composite steel higher strength and higher ductility via introducing carbon diffusion strategy[J]. Materials Research Letters,2021,9(9):391.
[11] KIM J G,BAEK S M,LEE H H,et al. Suppressed deformation instability in the twinning-induced plasticity steel cored three-layer steel sheet[J]. Acta Materialia,2018,147:304.
[12] BOUAZIZ O,MASSE J P,PETITGAND G,et al. A novel strong and ductile TWIP/martensite steel composite[J]. Advanced Engineering Materials,2016,18(1):56.
[13] 郭宇杰,刘廷光,白琴,等. 晶界工程对316L不锈钢晶界形貌影响的三维研究[J]. 上海金属,2022,44(4):36.(GUO Y J,LIU T G,BAI Q,et al. Three-dimensional study on effects of grain boundary engineering on morphology of grain boundaries in 316L stainless steel[J]. Shanghai Metals,2022,44(4):36.)
[14] WATANAB E T. Grain boundary engineering:Historical perspective and future prospects[J]. Journal of Materials Science,2011,46(12):4095.
[15] DING R,YAO Y J,SUN B H,et al. Chemical boundary engineering:A new route toward lean,ultrastrong yet ductile steels[J]. Science Advances,2020,6(13):eaay1430.
[16] HE B B,HU B,YEN H W,et al. High dislocation density induced large ductility in deformed and partitioned steels[J]. Science,2017,357:1092.
[17] 董瀚,王毛球,翁宇庆. 高性能钢的M³组织调控理论与技术[J]. 钢铁,2010,45(7):1.(DONG H,WANG M Q,WENG Y Q. Performance improvement of steels through M³ structure control[J]. Iron and Steel,2010,45(7):1.)
[18] CHEN J X,LI T,CHEN Y,et al. Ultra-strong heavy-drawn eutectic high entropy alloy wire[J]. Acta Materialia,2023,243:118515.
[19] WEI Y J,LI Y Q,ZHU L C,et al. Evading the strength-ductility trade-off dilemma in steel through gradient hierarchical nanotwins[J]. Nature Communications,2014,5:3580.
[20] FANG T H,LI W L,TAO N R,et al. Revealing extraordinary intrinsic tensile plasticity in gradient nano-grained copper[J]. Science,2011,331:1587.
[21] WANG H T,TAO N R,LU K. Architectured surface layer with a gradient nanotwined structure in a Fe-Mn austenitic steel[J]. Scripta Materialia,2013,68:22.
[22] 洪陆阔,艾立群,孙彩娇,等. 一种生产中高锰钢板带的工艺及装置:ZL 2020 1 1223612.9[P]. 2022-07-12.(HONG L K,AI L Q,SUN C J,et al. The Invention Relates to a Process and Device for Producing Medium and High Manganese Steel Plate Strip:ZL 2020 1 1223612.9[P]. 2022-07-12.)
[23] WU X L,JIANG P,CHEN L,et al. Extraordinary strain hardening by gradient structure[J]. Applied Physical Sciences,2014,111(20):7197.
[24] 李亚强,艾立群,李强,等. 1 mm铁碳合金薄带气-固反应脱碳试验[J]. 钢铁,2017,52(5):19.(LI Y Q,AI L Q,LI Q,et al. Experiment of gas-solid decarburization process of 1 mm Fe-C alloy ribbon[J]. Iron and Steel,2017,52(5):19.)
[25] 李亚强. 气氛条件对铁碳合金薄带气-固反应脱碳的影响[D]. 唐山:华北理工大学,2016.(LI Y Q. The Influence of Atmosphere Condition on Iron Sheet Gas-Solid Decarburization Process[D]. Tangshan:North China University of Science and Technology,2016.)
[26] 艾立群,侯耀斌,洪陆阔,等. H₂/H₂O气氛下Fe-C合金薄带气固脱碳反应动力学[J]. 工程科学学报,2021,43(6):816.(AI L Q,HOU Y B,HONG L K,et al. Gas-solid reaction kinetics of decarburization of Fe-C alloy strips in H₂/H₂O[J]. Chinese Journal of Engineering,2021,43(6):816.)
[27] 洪陆阔,艾立群,程荣,等. 铁碳合金薄带气固反应脱碳试验[J]. 钢铁,2016,51(3):27.(HONG L K,AI L Q,CHENG R,et al. Experimental of gas-solid decarburization of Fe-C alloy ribbon[J]. Iron and Steel,2016,51(3):27.)
[28] 侯耀斌,艾立群,洪陆阔,等. CO/CO₂气氛下Fe-C合金气固反应脱碳[J]. 钢铁,2020,55(11):133.(HOU Y B,AI L Q,HONG L K,et al. Gas-solid reaction decarburization of Fe-C alloy in CO/CO₂[J]. Iron and Steel,2020,55(11):133.)
[29] 孟凡峻,艾立群,洪陆阔,等. Ar-H₂O-H₂气氛下Fe-C-Mn薄带脱碳试验研究[J]. 钢铁钒钛,2021,42(5):132.(MENG F J,AI L Q,HONG L K,et al. Experimental study on decarbonization of Fe -C-Mn thin strips in Ar-H₂O-H₂ atmosphere[J]. Iron Steel Vanadium Titanium,2021,42(5):132.)
[30] 孙彩娇,艾立群,洪陆阔,等. H₂/H₂O气氛下Fe-C合金气固反应脱碳机理[J]. 材料导报,2020,34(10):20112.(SUN C J,AI L Q,HONG L K,et al. Mechanism of carbon diffusion in solid state steelmaking from the Fe-C alloy strip through gas-solid decarburization in H₂/H₂O[J]. Materials Reports,2020,34(10):20112.)