氮化物对齿条钢强度及冲击韧性的影响

doi:10.13228/j.boyuan.issn0449-749x.20230303

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (0 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract When smelting rack steel with steel ingots,due to the absorption of N during the casting process,the N content in the steel is relatively high,which affects the solid solution B content in the steel,reduces the hardenability of the steel plate,and affects the performance of the center the steel plate. In order to improve the strength and toughness matching of the steel ingot rolling gear steel,the addition of Al or Ti elements to reaction with N in the steel ensures sufficient solid solution B in the steel plate,improves the hardenability of the steel plate,and increases the proportion of tempered sorbite in the center of the steel plate. By comparing the properties and microstructure of steel plates,it was found that both adding Al and Ti can improve the hardenability and strength of the steel plate. The steel plate with Ti has better hardenability and higher strength,but its low-temperature impact absorption energy decreases. Analyzing the impact fracture surface of the steel plate,it was found that there are large particles of TiN inclusions in the steel plate. Cracks exist between the inclusions and the matrix or between the inclusions themselves,which become the source of cracks in the impact test and reduce the toughness of the steel plate. Comparison of steel plates with Al and Ti added Statistical analysis of inclusions above 2 μm shows that there are a large number of large particle TiN inclusions in Ti steel,with a maximum inclusion size exceeding 15 μm. There are still a small amount of TiN inclusions in the Al added steel plate,but the number and size of TiN inclusions have decreased,and AlN has not significantly increased. In situ analysis and comparison were conducted between the Al element in the Al steel plate and the Ti element in the Ti steel plate. It was found that the Al element is negatively segregated at the center and has a lower degree of segregation. The Ti element is positively segregated at the center and has poorer uniformity,with local segregation. Thermodynamic calculations indicate that when titanium is used for nitrogen fixation,TiN will precipitate at the solidification front,resulting in a higher precipitation temperature;when using aluminum nitrogen fixation,if the mass fraction of aluminum is not less than 0.08%,AlN precipitates in the solid state at a temperature higher than BN,which can ensure the solid solution boron content in the steel plate,ensure the hardenability of the steel plate,and control the size of TiN precipitates in the steel.

Key words： rack steel AlN TiN impact property in situ analysis

Received: 05 June 2023

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	FENG Zan
	GAO Hailiang
	TUO Chende
	WANG Zhen

Cite this article:

FENG Zan,GAO Hailiang,TUO Chende等. Effect of nitride on strength and impact property of rack steel[J]. Iron and Steel, 2024, 59(1): 124-131.

URL:

http://www.chinamet.cn/Jweb_gt/EN/10.13228/j.boyuan.issn0449-749x.20230303 OR http://www.chinamet.cn/Jweb_gt/EN/Y2024/V59/I1/124

[1] 杜伟,李鹤林. 海洋石油平台用钢的现状与发展趋势(四)[J]. 石油管材与仪器,2016,2(6):11.(DU W,LI H L. Status and development trends of offshore platform steels(Ⅳ)[J]. Petroleum Tubular Goods and Instruments,2016,2(6):11.)
[2] 张娟,曲锦波,张宽. wTi/w_N和wAl对含B钢淬透性及力学性能的影响[J]. 钢铁研究学报,2016,28(2):57.(ZHANG J,QU J B,ZHANG K. The effect of wTi/w_N and wAl on the hardenability and mechanical properties of B-containing steel [J]. Journal of Iron and Steel Research,2016,28(2):57.)
[3] 郭跃华,刘明,邓通武,等. Ti对含硼履带钢淬透性的影响[J]. 钢铁钒钛,2016,37(6):142.(GUO Y H,LIU M,DENG T W,et al. The effect of Ti on the hardenability of boron containing track steel[J]. Iron Steel Vanadium Titanium,2016,37(6):142.)
[4] 郭晓波,戚淑芳,赵成林. 低碳含硼钢氮化物析出特点研究[J]. 鞍钢技术,2013(6):27. (GUO X B,QI S F,ZHAO C L. Research on the characteristics of nitride precipitation in low carbon boric steel[J]. Ansteel Technology,2013(6):27.)
[5] 潘涛,王小勇,苏航. 合金元素Al对微B处理特厚钢板淬透性及力学性能的影响[J]. 金属学报,2014,50(4):431.(PAN T,WANG X Y,SU H. The effect of alloy element Al on the hardenability and mechanical properties of micro B treated extra thick steel plates[J]. Acta Metallurgica Sinica,2014,50(4):431.)
[6] 王帅,胡锋,李德发,等. TiN对高强度耐磨钢韧性的影响及其机制分析[J]. 中国冶金,2021,31(7):38.(WANG S,HU F,LI D F,et al. The effect of TiN on the toughness of high strength wear resistant steel and its mechanism analysis[J]. China Metallurgy,2021,31(7):38.)
[7] 杨跃标,李宗强,邓深,等. 热轧钛微合金化高强钢低温冲击韧性的控制[J]. 钢铁,2021,56(3):41.(YANG Y B,LI Z Q,DENG S,et al. Control of low-temperature impact toughness of hot-rolled titanium microalloyed high-strength steel[J]. Iron and Steel,2021,56(3):41.)
[8] 刘帅,王福明,李永亮. 微合金元素Nb和Ti对高强工程结构钢低温冲击性能的影响[J]. 工程科学学报,2018,40(s1):41.(LIU S,WANG F M,LI Y L. The effect of microalloying elements Nb and Ti on the low-temperature impact performance of high-strength engineering structural steel[J]. Chinese Journal of Engineering,2018,40(s1):41.)
[9] 周建川,李红俊,李静,等. 夹杂物对高强钢冲击性能影响及优化分析[J]. 四川冶金,2022,44(2):52.(ZHOU J C,LI H J,LI J,et al. Influence of inclusions on the impact performance of high-strength steel and optimization analysis[J]. Sichuan Metallurgy,2022,44(2):52.)
[10] 刘洪波,刘建华,沈少波. 铝含量对TWIP钢中夹杂物特征及AlN析出行为的影响[J]. 工程科学学报,2017,39(7):1008.(LIU H B,LIU J H,SHEN S B. The effect of aluminum content on the characteristics of inclusions and AlN precipitation behavior in TWIP steel[J]. Chinese Journal of Engineering,2017,39(7):1008.)
[11] 李莉,贾志伟,宋清阳,等. 酸溶铝含量对取向硅钢常化抑制剂析出的影响[J]. 电工钢,2021,3(4):5.(LI L,JIA Z W,SONG Q Y,et al. The effect of acid soluble aluminum content on the precipitation of normalization inhibitors in oriented silicon steel[J]. Electrical Steel,2021,3(4):5.)
[12] 吴德润,左康林. 超低碳铝硅镇静钢中的夹杂物析出在线观察[C]//第十九届(2016年)全国炼钢学术会议大会报告及论文摘要集.长沙:中国金属学会,2016:157.(WU D R,ZUO K L. Online observation of inclusion precipitation in ultra low carbon aluminum silicon killed steel[C]//Report and Abstract Collection of the 19th (2016) National Steelmaking Academic Conference. Changsha:The Chinese Society for Metals,2016:157.)
[13] 乔士宾,何西扣,刘正东. SA508Gr.4 N钢奥氏体晶粒长大行为研究[J]. 材料科学与工艺,2021,29(4):8.(QIAO S B,HE X K,LIU Z D. Study on austenite grain growth behavior of SA508Gr.4 N steel[J]. Materials Science and Technology,2021,29(4):8.)
[14] 魏民,李海洋,董延楠,等. 连铸高铝氮积齿轮钢第三脆性区形成机制与控制[J]. 中国冶金,2022,32(9):64.(WEI M,LI H Y,DONG Y N,et al. Formation mechanism and control of the third brittle zone in continuous casting high aluminum nitrogen accumulation gear steel[J]. China Metallurgy,2022,32(9):64.)
[15] 顾铁. 渗碳齿轮钢AlN固溶行为的研究[J]. 工程技术研究,2021,3(9):161.(GU T. A study on the solid solution behavior of AlN in carburized gear steel[J]. Engineering Technology Research,2021,3(9):161.)
[16] 倪玲玲,付锡彬,张可,等. 均热温度对Ti-V复合微合金钢组织演变和硬度的影响[J]. 金属热处理,2021,46(3):146.(NI L L,FU X B,ZHANG K,et al. The effect of soaking temperature on the microstructure evolution and hardness of Ti-V composite microalloyed steel[J]. Heat Treatment of Metals,2021,46(3):146.)
[17] 陈波涛,张泽峰,邢立东,等. 含钛微合金钢凝固过程中TiN的析出行为分析[J]. 连铸,2021(3):28.(CHEN B T,ZHANG Z F,XING L D,et al. Analysis of TiN precipitation behavior during solidification of titanium containing microalloyed steel[J]. Continuous Casting,2021(3):28.)
[18] 李永超,杨玉丹,吴豪明,等. 低钛轴承钢中TiN的尺寸分析和工艺研究[J]. 河北冶金,2022(4):19.(LI Y C,YANG Y D,WU H M,et al. Dimensional analysis and process study of TiN in low titanium bearing steel[J]. Hebei Metallurgy,2022(4):19.)
[19] 沈中芳,段豪剑,张立峰. 超纯铁素体不锈钢B439M 200 mm×1 260 mm连铸板坯中TiN夹杂物的分布[J]. 特殊钢,2016,37(3):46.(SHEN Z F,DUAN H J,ZHANG L F. Ultra pure ferritic stainless steel B439M 200 mm×1 260 mm distribution of TiN inclusions in continuous casting slab[J]. Special Steel,2016,37(3):46.)
[20] 夏明生,李秀景,王占国,等. Ti-IF钢中TiN的连铸析出分析[C]//2014年全国炼钢—连铸生产技术会论文集. 唐山:中国金属学会,2014:438.(XIA M S,LI X J,WANG Z G,et al. Analysis of TiN continuous casting precipitation in Ti-IF steel[C]//Proceedings of the 2014 National Steelmaking Continuous Casting Production Technology Conference. Tangshan:The Chinese Society for Metals,2014:438.)
[21] 王金永,刘建华,刘建飞,等. Ti-IF钢凝固过程中TiN的析出机理和规律[J]. 北京科技大学学报,2014,36(8):1025.(WANG J Y,LIU J H,LIU J F,et al. The precipitation mechanism and law of TiN during the solidification process of Ti IF steel[J]. Journal of University of Science and Technology Beijing,2014,36(8):1025.)
[22] 张肖遥,彭军,彭继华. 氮含量对稀土钢中夹杂析出热力学的探究[J]. 稀土,2022,43(6):1.(ZHANG X Y,PENG J,PENG J H. Research on the thermodynamics of inclusion precipitation in rare earth steel with nitrogen content[J]. Rare Earth,2022,43(6):1.)
[23] 陈民涛,吴杏格,李超越,等. 1Cr17Ni2钢锭锻造开裂失效分析[J]. 金属加工(热加工),2022(7):7.(CHEN M T,WU X G,LI C Y,et al. 1Cr17Ni2 ingot forging crack failure analysis[J]. Metal Working,2022(7):7.)
[24] 王妍,尹治力,杜进英. 特大型支承辊断裂原因分析[J]. 大型铸锻件,2023(1):36.(WANG Y,YIN Z L,DU J Y. Analysis of the causes of fracture of extra large support rolls[J]. Large Castings and Forgings,2023(1):36.)
[25] 俞占扬,张慧,干勇,等. 钢锭铸造过程中宏观偏析的研究进展[J]. 中国冶金,2021,31(5):6.(YU Z Y,ZHANG H,GAN Y,et al. Research progress of macrosegregation in steel ingot casting[J]. China Metallurgy,2021,31(5):6.)
[26] 荣文杰,李林敏,李宝宽. 大型钢锭凝固过程流动及组分传输研究[C]//第八届全国能源与热工学术年会论文集.大连:中国金属学会,2015:446.(RONG W J,LI L M,LI B K. Research on flow and component transport during the solidification process of large steel ingots[C]//Proceedings of the 8th National Energy and Thermal Engineering Academic Annual Conference. Dalian:The Chinese Society for Metals,2015:446.)
[27] 张涛,成国光,侯雨阳. 过热度对GCr15SiMn轴承钢钢锭宏观偏析的影响[J]. 中国冶金,2020,30(9):60.(ZHANG T,CHENG G G,HOU Y Y. The effect of superheat on macroscopic segregation of GCr15SiMn bearing steel ingots[J]. China Metallurgy,2020,30(9):60.)
[28] 涂武涛. 大型钢锭宏观偏析多元多相建模与仿真[D]. 北京:清华大学,2016.(TU W T Multivariate and Multiphase Modeling and Simulation of Macrosegregation in Large Steel Ingots[D]. Beijing:Tsinghua University,2016.)
[29] 蔡端星. 大型铸锭宏观偏析与夹杂物耦合模拟研究[D]. 上海:上海交通大学,2021.(CAI D X. Study on Coupling Simulation of Macrosegregation and Inclusions in Large Ingot Casting[D]. Shanghai:Shanghai Jiao Tong University,2021.)
[30] 陈林恒,桑晨,童志,等. 高强耐火钢中合金元素在焊接热循环作用下的偏聚行为[J]. 上海金属,2021,43(2):27.(CHEN L H,SANG C,TONG Z,et al. Segregation behavior of alloy elements in high-strength refractory steel under welding thermal cycling[J]. Shanghai Metals,2021,43(2):27.)
[31] 卡恩. 材料科学与技术[M]. 师昌绪, 译. 北京:科学出版社,1996.(CAHN R W. Materials Science and Technology[M]. SHI C X, Translated. Beijing:Science Press,1996.)
[32] GAO N,BAKER T N. Austenite grain growth behavior of microalloyed Al-V-N and Al-V-Ti-N steels[J]. ISIJ International,1998,38(7):744.
[33] TURKDOGAN E T. Causes and effects of nitride and carbonitride precipitation in HSLA steel in relation to continuous casting[C]//Kennedy W Steel Making Conference Proceedings. New York:AIME,1987:399.
[34] 黄希祜.钢铁冶金原理[M]. 北京:冶金工业出版社,2005.(HUANG X K. Principle of Ferrous Metallurgy[M]. Beijing:Metallurgical Industry Press,2005.)
[35] 陈家祥. 炼钢常用图标数据手册[M]. 北京:冶金工业出版社,1984. (CHEN J X. Manual of Chart and Data in Common Use of Steel Making[M]. Beijing:Metallurgical Industry Press,1984.)
[36] 郑万,寇锦荣,李烈军,等. 微钛固氮降低含铌钢皮下裂纹敏感性的机理[J]. 钢铁,2022,57(8):94.(ZHENG W,KOU J R,LI L J,et al. Mechanism of reducing subcutaneous crack sensitivity of niobium containing steel by nitrogen fixation with micro titanium[J]. Iron and Steel,2022,57(8):94.)