ժҪ The microstructure characteristics and precipitation behavior of automobile beam steels produced by Compact Strip Production (CSP) were investigated by use of scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray energy dispersive spectroscopy. The result shows that the final microstructure is mainly of polygonal ferrite and small amount of pearlite, the average ferrite grain size is about 3��6��m. Small amount addition Ti to aluminium-killed steel can help to refine the microstructure and improve the mechanical properties. A large number of fine precipitates have been observed in automobile beam steels. The mean particle size is about 10��30nm. Remarkable strengthening and grain refinement can be obtained by these nano-particles.
Abstract��The microstructure characteristics and precipitation behavior of automobile beam steels produced by Compact Strip Production (CSP) were investigated by use of scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray energy dispersive spectroscopy. The result shows that the final microstructure is mainly of polygonal ferrite and small amount of pearlite, the average ferrite grain size is about 3��6��m. Small amount addition Ti to aluminium-killed steel can help to refine the microstructure and improve the mechanical properties. A large number of fine precipitates have been observed in automobile beam steels. The mean particle size is about 10��30nm. Remarkable strengthening and grain refinement can be obtained by these nano-particles.
ZHAO Zheng-zhi;LIU Jie. Analysis on Microstructure Characteristics and Precipitation Behavior of Automobile Beam Steels Produced by Compact Strip Production[J]. �й������ڿ���, 2010, 17(3): 56-56.
ZHAO Zheng-zhi;LIU Jie. Analysis on Microstructure Characteristics and Precipitation Behavior of Automobile Beam Steels Produced by Compact Strip Production. Chinese Journal of Iron and Steel, 2010, 17(3): 56-56.