ժҪ Microstructure, tensile and impact toughness properties and fracture location of friction stir welded AISI 1018 mild steel are revealed in this paper. The 5 mm thick AISI 1018 mild steel plates were friction stir welded with tool rotational speed of 1000 rpm and welding speed of 50 mm/min with tungsten base alloy tool. Tensile strength of stir zone is higher (8%) when compared to the base metal. This may be due to the formation of finer grains in the weld nugget region under the stirring action of the rotating tool. The ductility and impact toughness of the joints are decreased compared to the base metal and this is due to the inclusion of tungsten particles in the weld region.
Abstract��Microstructure, tensile and impact toughness properties and fracture location of friction stir welded AISI 1018 mild steel are revealed in this paper. The 5 mm thick AISI 1018 mild steel plates were friction stir welded with tool rotational speed of 1000 rpm and welding speed of 50 mm/min with tungsten base alloy tool. Tensile strength of stir zone is higher (8%) when compared to the base metal. This may be due to the formation of finer grains in the weld nugget region under the stirring action of the rotating tool. The ductility and impact toughness of the joints are decreased compared to the base metal and this is due to the inclusion of tungsten particles in the weld region.
A.K.Lakshminarayanan. Microstructure, Tensile and Impact Toughness Properties of Friction Stir Welded Mild Steel[J]. �й������ڿ���, 2010, 17(10): 68-74.
A.K.Lakshminarayanan. Microstructure, Tensile and Impact Toughness Properties of Friction Stir Welded Mild Steel. Chinese Journal of Iron and Steel, 2010, 17(10): 68-74.
2010, Vol. 17 