Corrosion Products and Formation Mechanism During Initial Stage of Atmospheric Corrosion of Carbon Steel
1. Beijing Key Laboratory for Corrosion, Erosion and Surface Technology, University of Science and Technology Beijing, Beijing 100083, China;2. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China
ժҪ The formation and development of corrosion products on carbon steel surface during the initial stage of atmospheric corrosion in a laboratory simulated environment have been studied by scanning electron microscopy (SEM) and Raman spectroscopy. The results showed that two different shapes of corrosion products, that is, ring and chain, were formed in the initial stage of corrosion. MnS clusters were found in the nuclei of corrosion products at the active local corrosion sites. The ring��shaped products were composed of lepidocrocite (�ê�FeOOH) and maghemite (�ê�Fe2O3) transformed from lepidocrocite. The chain��type products were goethite (����FeOOH). A formation mechanism of the corrosion products is proposed.
Abstract��The formation and development of corrosion products on carbon steel surface during the initial stage of atmospheric corrosion in a laboratory simulated environment have been studied by scanning electron microscopy (SEM) and Raman spectroscopy. The results showed that two different shapes of corrosion products, that is, ring and chain, were formed in the initial stage of corrosion. MnS clusters were found in the nuclei of corrosion products at the active local corrosion sites. The ring��shaped products were composed of lepidocrocite (�ê�FeOOH) and maghemite (�ê�Fe2O3) transformed from lepidocrocite. The chain��type products were goethite (����FeOOH). A formation mechanism of the corrosion products is proposed.
XIAO Kui;DONG Chao��fang;LI Xiao��gang;WANG Fu��ming. Corrosion Products and Formation Mechanism During Initial Stage of Atmospheric Corrosion of Carbon Steel[J]. �й������ڿ���, 2008, 15(5): 42-0.
XIAO Kui;DONG Chao��fang;LI Xiao��gang;WANG Fu��ming. Corrosion Products and Formation Mechanism During Initial Stage of Atmospheric Corrosion of Carbon Steel. Chinese Journal of Iron and Steel, 2008, 15(5): 42-0.
2008, Vol. 15 