High Efficient Technology of Steelmaking With Low Silicon Hot Metal on Large Converter
JIANG Xiao��fang1,WANG Ming��lin1,YANG Wen��yuan1, GAN Yong1,WANG Ying��jun2,YU Zu��da2
1. National Engineering Research Center of Continuous Casting, Central Iron and Steel Research Institute, Beijing 100081, China;2. Steelmaking Plant, Baoshan Iron and Steel Co, Shanghai 201900, China
High Efficient Technology of Steelmaking With Low Silicon Hot Metal on Large Converter
JIANG Xiao��fang1,WANG Ming��lin1,YANG Wen��yuan1, GAN Yong1,WANG Ying��jun2,YU Zu��da2
1. National Engineering Research Center of Continuous Casting, Central Iron and Steel Research Institute, Beijing 100081, China;2. Steelmaking Plant, Baoshan Iron and Steel Co, Shanghai 201900, China
ժҪ To resolve the difficulty in slag formation during steelmaking with low silicon hot metal and to increase productivity, a new 5��hole lance was developed by increasing oxygen flow from 50 000 m3/h to 60 000 m3/h. Synthetic slag was added to adjust the slag composition. The problems such as difficulty in dephosphorization and slag adhesion to oxygen lance and hood were settled. Steel production and metal yield were increased and the nozzle life was prolonged through these techniques.
Abstract��To resolve the difficulty in slag formation during steelmaking with low silicon hot metal and to increase productivity, a new 5��hole lance was developed by increasing oxygen flow from 50 000 m3/h to 60 000 m3/h. Synthetic slag was added to adjust the slag composition. The problems such as difficulty in dephosphorization and slag adhesion to oxygen lance and hood were settled. Steel production and metal yield were increased and the nozzle life was prolonged through these techniques.
JIANG Xiao��fang;WANG Ming��lin;YANG Wen��yuan;GAN Yong;WANG Ying��jun;YU Zu��da. High Efficient Technology of Steelmaking With Low Silicon Hot Metal on Large Converter[J]. �й������ڿ���, 2007, 14(6): 27-0.