Preparation, Structure and Mechanical Properties of Nickel Based Porous Spherical Superalloy
MI Guo��fa1,LI Hong��yu2,LIU Xiang��yu1,WANG Kuang��fei1
1. School of Materials Science and Engineering, Henan Polytechnic University, Jiaozuo 454000, Henan, China; 2. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, Heilongjiang, China
Preparation, Structure and Mechanical Properties of Nickel Based Porous Spherical Superalloy
MI Guo��fa1,LI Hong��yu2,LIU Xiang��yu1,WANG Kuang��fei1
1. School of Materials Science and Engineering, Henan Polytechnic University, Jiaozuo 454000, Henan, China; 2. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, Heilongjiang, China
ժҪ The porous superalloy materials with hollow spherical pores were fabricated by using metal powder sintering process. The scanning electron microscope (SEM) observation was applied to the test samples and it revealed that the pores of the porous material exhibited a uniform distribution and the apertures were of same size in principle. The sintering necks appeared between adjacent particles on metal skeleton after sintering. The mechanical properties of the test samples were analyzed and the result showed that this kind of materials possessed excellent energy absorption capability, and the compression resistance decreased with increasing the porosity and aperture.
Abstract��The porous superalloy materials with hollow spherical pores were fabricated by using metal powder sintering process. The scanning electron microscope (SEM) observation was applied to the test samples and it revealed that the pores of the porous material exhibited a uniform distribution and the apertures were of same size in principle. The sintering necks appeared between adjacent particles on metal skeleton after sintering. The mechanical properties of the test samples were analyzed and the result showed that this kind of materials possessed excellent energy absorption capability, and the compression resistance decreased with increasing the porosity and aperture.