Profile and Flatness Control Technology With a Long Shifting Stroke on Wide Non-Oriented Electrical Steel Sheets
YANG Guang-hui1,CAO Jian-guo1,ZHANG Jie1,SONG Ping2,YAN Tan-li2,RAO Ke-feng2
[1. School of Mechanical Engineering, University of Science and Technology Beijing, Beijing 100083, China 2. Hot Rolling Plant, Wuhan Iron and Steel Group Corporation, Wuhan 430083, Hubei, China]
Profile and Flatness Control Technology With a Long Shifting Stroke on Wide Non-Oriented Electrical Steel Sheets
YANG Guang-hui1,CAO Jian-guo1,ZHANG Jie1,SONG Ping2,YAN Tan-li2,RAO Ke-feng2
[1. School of Mechanical Engineering, University of Science and Technology Beijing, Beijing 100083, China 2. Hot Rolling Plant, Wuhan Iron and Steel Group Corporation, Wuhan 430083, Hubei, China]
ժҪ In order to solve the difficult profile and flatness control problem of wide non-oriented electrical steel sheets, the factors such as the relationship between strip crown control and strip width, the relationship between the maximum wearing value of work roll and the number of a rolling campaign and the wear contour change of work roll were analyzed on the basis of industrial test. Through analyzing the rolling process characteristics of non-oriented electrical steel sheets, the ASR (asymmetry self-compensating work rolls) shape control technology and its roll shifting strategy of the wider non-oriented electrical steel sheets was proposed and developed. When the technology was applied, the number of the wide non-oriented electrical steel (2��3 mm��1280 mm) in one rolling campaign rose from 40 coils of the trial production to 70 coils of the industrial production, the ratio of the measured strip crown less than 45 ��m was increased from 50��0% to 94��9%, and the ratio of the measured strip crown more than 60 ��m was decreased from 20��0% to 0��7%.
Abstract��In order to solve the difficult profile and flatness control problem of wide non-oriented electrical steel sheets, the factors such as the relationship between strip crown control and strip width, the relationship between the maximum wearing value of work roll and the number of a rolling campaign and the wear contour change of work roll were analyzed on the basis of industrial test. Through analyzing the rolling process characteristics of non-oriented electrical steel sheets, the ASR (asymmetry self-compensating work rolls) shape control technology and its roll shifting strategy of the wider non-oriented electrical steel sheets was proposed and developed. When the technology was applied, the number of the wide non-oriented electrical steel (2��3 mm��1280 mm) in one rolling campaign rose from 40 coils of the trial production to 70 coils of the industrial production, the ratio of the measured strip crown less than 45 ��m was increased from 50��0% to 94��9%, and the ratio of the measured strip crown more than 60 ��m was decreased from 20��0% to 0��7%.
YANG Guang-hui,CAO Jian-guo,ZHANG Jie,SONG Ping,YAN Tan-li,RAO Ke-feng. Profile and Flatness Control Technology With a Long Shifting Stroke on Wide Non-Oriented Electrical Steel Sheets[J]. �й������ڿ���, 2012, 19(1): 31-35.
YANG Guang-hui,CAO Jian-guo,ZHANG Jie,SONG Ping,YAN Tan-li,RAO Ke-feng. Profile and Flatness Control Technology With a Long Shifting Stroke on Wide Non-Oriented Electrical Steel Sheets. Chinese Journal of Iron and Steel, 2012, 19(1): 31-35.
2012, Vol. 19 