1. Institute of Materials Science and Engineering, Jiangsu University of Science and Technology, Zhenjiang 212003,Jiangsu, China 2. CSC Jinling Shipyard, Nanjing 210015, Jiangsu, China 3. Jiangsu Kewei Welding IndustryCo. , Ltd. , Jiangyin 214400, Jiangsu, China
Comparative Study on Processing Property Between CWW CO2 Gas Shielded Welding and SAW
1. Institute of Materials Science and Engineering, Jiangsu University of Science and Technology, Zhenjiang 212003,Jiangsu, China 2. CSC Jinling Shipyard, Nanjing 210015, Jiangsu, China 3. Jiangsu Kewei Welding IndustryCo. , Ltd. , Jiangyin 214400, Jiangsu, China
ժҪ Cable welding wire (CWW) CO2 gas shielded welding is an innovative process arc welding with high efficiency, high quality and low consumption, in which cable wire is used as consumable electrode. CWW CO2 gas shielded welding and submerged arc welding (SAW) are used for contrast studies on processing property of high strength steel A36 used in ship structure. The results show that the shapes of weld seam, using CWW CO2 gas shielded welding and SAW, are good and no weld defect such as air hole, flaw, slag inclusion, incomplete fusion, lack of penetration and so on are found in the weld seam. Because the rotating of arc during CWW CO2 gas shielded welding process has a strong stirring effect on molten pool, the grain in the heat affected zone (HAZ) of the joints, using CWW CO2 gas shielded welding, is small. Tensile failure positions of joints by CWW CO2 gas shielded welding and SAW are all in the base metal, but tensile strength of CWW CO2 gas shielded welding joint is higher than that of SAW joint by an average of 2. 3%. The average impact energy of HAZ, using CWW CO2 gas shielded welding and SAW, is almost equal, but the average impact energy of the weld seam using CWW CO2 gas shielded welding is increased by 6%, and the average impact energy of the fusion line is increased by 7%. The 180�� bending tests for the joints of CWW CO2 gas shielded welding and SAW are all qualified, and the joints hardness is all less than HV 355, but hardness of CWW CO2 gas shielded welding wire welding joint near the fusion line is obviously lower. It can be concluded that the properties of CWW CO2 gas shielded welding are better than those of the SAW joint, and CWW CO2 gas shielded welding is suitable for welding high strength steel A36 used in ship structure.
Abstract��Cable welding wire (CWW) CO2 gas shielded welding is an innovative process arc welding with high efficiency, high quality and low consumption, in which cable wire is used as consumable electrode. CWW CO2 gas shielded welding and submerged arc welding (SAW) are used for contrast studies on processing property of high strength steel A36 used in ship structure. The results show that the shapes of weld seam, using CWW CO2 gas shielded welding and SAW, are good and no weld defect such as air hole, flaw, slag inclusion, incomplete fusion, lack of penetration and so on are found in the weld seam. Because the rotating of arc during CWW CO2 gas shielded welding process has a strong stirring effect on molten pool, the grain in the heat affected zone (HAZ) of the joints, using CWW CO2 gas shielded welding, is small. Tensile failure positions of joints by CWW CO2 gas shielded welding and SAW are all in the base metal, but tensile strength of CWW CO2 gas shielded welding joint is higher than that of SAW joint by an average of 2. 3%. The average impact energy of HAZ, using CWW CO2 gas shielded welding and SAW, is almost equal, but the average impact energy of the weld seam using CWW CO2 gas shielded welding is increased by 6%, and the average impact energy of the fusion line is increased by 7%. The 180�� bending tests for the joints of CWW CO2 gas shielded welding and SAW are all qualified, and the joints hardness is all less than HV 355, but hardness of CWW CO2 gas shielded welding wire welding joint near the fusion line is obviously lower. It can be concluded that the properties of CWW CO2 gas shielded welding are better than those of the SAW joint, and CWW CO2 gas shielded welding is suitable for welding high strength steel A36 used in ship structure.
FANG Chen-fu,HE Bin,ZHAO Zhong-chao,HU Xiao-guang,JIANG Jia-zhong,SHI Zhen. Comparative Study on Processing Property Between CWW CO2 Gas Shielded Welding and SAW[J]. �й������ڿ���, 2013, 20(4): 81-86.
FANG Chen-fu,HE Bin,ZHAO Zhong-chao,HU Xiao-guang,JIANG Jia-zhong,SHI Zhen. Comparative Study on Processing Property Between CWW CO2 Gas Shielded Welding and SAW. Chinese Journal of Iron and Steel, 2013, 20(4): 81-86.
2013, Vol. 20 