ժҪ Austenitic 316L stainless steel has good corrosion resistance; however, the relative softness often limits its application. Severe adhesive wear often occurs between the 316L stainless steel and the metal counterpart. Cu-10Sn alloy is often used to improve the wear resistance of powder metallurgy 316L stainless steel. The influence of Cu-10Sn on sintering behavior and wear resistance of powder metallurgy 316L stainless steel was investigated. The parameters investigated included sintering temperature and volume percent of Cu-10Sn. A maximum relative density of 97% was achieved with 25% (in volume percent) Cu-10Sn content at a sintering temperature of 1300 �� for 60 min. The irregular and sharp angles of 316L stainless steel particles become round, and the pores are removed completely as a result of large amount of liquid phase formed during sintering. The minimum friction mass loss was achieved with 25% Cu-10Sn content.
Abstract��Austenitic 316L stainless steel has good corrosion resistance; however, the relative softness often limits its application. Severe adhesive wear often occurs between the 316L stainless steel and the metal counterpart. Cu-10Sn alloy is often used to improve the wear resistance of powder metallurgy 316L stainless steel. The influence of Cu-10Sn on sintering behavior and wear resistance of powder metallurgy 316L stainless steel was investigated. The parameters investigated included sintering temperature and volume percent of Cu-10Sn. A maximum relative density of 97% was achieved with 25% (in volume percent) Cu-10Sn content at a sintering temperature of 1300 �� for 60 min. The irregular and sharp angles of 316L stainless steel particles become round, and the pores are removed completely as a result of large amount of liquid phase formed during sintering. The minimum friction mass loss was achieved with 25% Cu-10Sn content.
YANG Xia,BAI Ying-long,XU Meng,GUO Shi-ju. Effect of Additive Cu-10Sn on Sintering Behavior and Wear Resistance of 316L Stainless Steel[J]. �й������ڿ���, 2013, 20(7): 84-88.
YANG Xia,BAI Ying-long,XU Meng,GUO Shi-ju. Effect of Additive Cu-10Sn on Sintering Behavior and Wear Resistance of 316L Stainless Steel. Chinese Journal of Iron and Steel, 2013, 20(7): 84-88.
2013, Vol. 20 