1. College of Materials Science and Engineering, Fuzhou University, Fuzhou 350108, Fujian, China 2. Chengdu Aircraft Industrial Group Co��, Ltd��, AVIC, Chengdu 610092, Sichuan, China 3. Fujian San Ming Iron and Steel Group Co��, Ltd��, Sanming 365000, Fujian, China 4. College of Materials Science and Engineering,Fujian University of Technology, Fuzhou 350108, Fujian, China
Effect of Carbon Content on Stacking Fault Energy of Fe-20Mn-3Cu TWIP Steel
1. College of Materials Science and Engineering, Fuzhou University, Fuzhou 350108, Fujian, China 2. Chengdu Aircraft Industrial Group Co��, Ltd��, AVIC, Chengdu 610092, Sichuan, China 3. Fujian San Ming Iron and Steel Group Co��, Ltd��, Sanming 365000, Fujian, China 4. College of Materials Science and Engineering,Fujian University of Technology, Fuzhou 350108, Fujian, China
ժҪ A The influence of carbon content on the stacking fault energy (SFE) of Fe-20Mn-3Cu twinning-induced plasticity (TWIP) steel was investigated by means of X-ray diffraction peak-shift method and thermodynamic modeling. The experimental result indicated that the stacking fault probability decreases with increasing carbon addition, the SFE increases linearly when the carbon content in mass percent is between 0��23% and 1��41%. The thermodynamic calculation results showed that the SFE varied from 22��40 to 29��64 mJ��m-2 when the carbon content in mass percent changes from 0��23% to 1��41%. The XRD analysis revealed that all steels were fully austenitic before and after deformation, which suggested that TWIP effect is the predominant mechanism during the tensile deformation process of Fe-20Mn-3Cu-XC steels.
Abstract��A The influence of carbon content on the stacking fault energy (SFE) of Fe-20Mn-3Cu twinning-induced plasticity (TWIP) steel was investigated by means of X-ray diffraction peak-shift method and thermodynamic modeling. The experimental result indicated that the stacking fault probability decreases with increasing carbon addition, the SFE increases linearly when the carbon content in mass percent is between 0��23% and 1��41%. The thermodynamic calculation results showed that the SFE varied from 22��40 to 29��64 mJ��m-2 when the carbon content in mass percent changes from 0��23% to 1��41%. The XRD analysis revealed that all steels were fully austenitic before and after deformation, which suggested that TWIP effect is the predominant mechanism during the tensile deformation process of Fe-20Mn-3Cu-XC steels.
Xian PENG,,Ding-yi ZHU,Zhen-ming HU,Ming-jie WANG,,Long-long LIU,Hai-jun LIU. Effect of Carbon Content on Stacking Fault Energy of Fe-20Mn-3Cu TWIP Steel[J]. �й������ڿ���, 2014, 21(1): 116-120.
Xian PENG,,Ding-yi ZHU,Zhen-ming HU,Ming-jie WANG,,Long-long LIU,Hai-jun LIU. Effect of Carbon Content on Stacking Fault Energy of Fe-20Mn-3Cu TWIP Steel. Chinese Journal of Iron and Steel, 2014, 21(1): 116-120.
2014, Vol. 21 