1 College of Mechanical Engineering, Taiyuan University of Technology, Taiyuan 030024, Shanxi, China 2 Shanxi Provincial Key Laboratory of Metallurgical Equipment Design and Technology, Taiyuan University of Science and Technology, Taiyuan 030024, Shanxi, China 3 Heavy Machinery Engineering Research Center of the Ministry Education, Taiyuan University of Science and Technology, Taiyuan 030024, Shanxi, China
Characterization of hot deformation behavior of wear-resistant steel BTW1 using processing maps and constitutive equations
1 College of Mechanical Engineering, Taiyuan University of Technology, Taiyuan 030024, Shanxi, China 2 Shanxi Provincial Key Laboratory of Metallurgical Equipment Design and Technology, Taiyuan University of Science and Technology, Taiyuan 030024, Shanxi, China 3 Heavy Machinery Engineering Research Center of the Ministry Education, Taiyuan University of Science and Technology, Taiyuan 030024, Shanxi, China
ժҪ In order to predict flow instability of wear-resistant steel BTW1, the hot compressions of wear-resistant steel BTW1 were firstly performed at the temperature of 900�C1150 C and at the strain rate of 0.05�C15 s-1. Then, the constitutive relation was established based on Arrhenius-type hyperbolic sine equation. The results demonstrated that the flow stress depended on the deformation temperature and strain rate. When the deformation temperature kept constant, the flow stress increased as the strain rate increased. When the strain rate remained constant, the flow stress decreased as the temperature increased. The flow stresses calculated by constitutive equations were in a good agreement with experimental results. The apparent activation energy for deformation in the above processing region was estimated to be 369 kJ mol-1. A processing map could be obtained by the superimposition of an instability map on a power dissipation map. Based on the analysis of processing map and the microstructures, the rheological instability regimes of strain rate and temperature for hot deformation of wear-resistant steel BTW1 had been identified.
Abstract��In order to predict flow instability of wear-resistant steel BTW1, the hot compressions of wear-resistant steel BTW1 were firstly performed at the temperature of 900�C1150 C and at the strain rate of 0.05�C15 s-1. Then, the constitutive relation was established based on Arrhenius-type hyperbolic sine equation. The results demonstrated that the flow stress depended on the deformation temperature and strain rate. When the deformation temperature kept constant, the flow stress increased as the strain rate increased. When the strain rate remained constant, the flow stress decreased as the temperature increased. The flow stresses calculated by constitutive equations were in a good agreement with experimental results. The apparent activation energy for deformation in the above processing region was estimated to be 369 kJ mol-1. A processing map could be obtained by the superimposition of an instability map on a power dissipation map. Based on the analysis of processing map and the microstructures, the rheological instability regimes of strain rate and temperature for hot deformation of wear-resistant steel BTW1 had been identified.
Peng-tao Liu,, ? Qing-xue Huang,, ? Li-feng Ma, ? Tao Wang. Characterization of hot deformation behavior of wear-resistant steel BTW1 using processing maps and constitutive equations[J].Journal of Iron and Steel Research International, 2018, 25(10): 1054-1061.
Peng-tao Liu,, ? Qing-xue Huang,, ? Li-feng Ma, ? Tao Wang. Characterization of hot deformation behavior of wear-resistant steel BTW1 using processing maps and constitutive equations. , 2018, 25(10): 1054-1061.
Niko Ojala, Kati Valtonen, Atte Antikainen, Anu Kemppainen, Jussi Minkkinen, Olli Oja, Veli-Tapani Kuokkala.Wear performance of quenched wear resistant steels in abrasive slurry erosion[J].Wear, 2016, 354-355(15 May):21-31
[2]
M.Lindroos,MApostol,V.T.Kuokkala,A.Laukkanen,K.Valtonen,K.Holmberg,O.Oja.The effect of impact conditions on the wear and deformation behavior of wear resistant steels[J].INT J IMPACT ENG, 2015, 328-329(15 April):197-205
[3]
Y.K.Singla,RChhibber,H.Bansal,A.Kalra.Wear Behavior of Aluminum Alloy 6061-Based Composites Reinforced with SiC,Al2O3,and Red Mud: A Comparative Study[J].JOM, 2015, 67(9):2160-2169
[4]
P.Da?i?,FFranek,E.Assenova,M.Radovanovi?.International standardization and organizations in the field of tribology[J].INT J IMPACT ENG, 2003, 55(6):287-291
[5]
H.P.JostTribology: How a word was coined 40 years ago[J].TRIBOL LUBR TECHNOL, 2006, 62(3):24-28
[6]
B.B.Bartha,JZawadzki,S.Chandrasekar,T.N.Farris.Wear of hard-turned AISI 52100 steel[J].METALL MATER TRANS A, 2005, 36(6):1417-1425
[7]
Y.QWeng,CF.Yang,C.J.Shang.The State-of-Art and Development Trends of HSLA Steels in China[J].J IRON STEEL RES INT, 2011, 46(s1):1-13
[8]
Y.CAO,ZD.Wang,J.Kang,D.Wu,G.D.Wang.Effects of Tempering Temperature and MoNi on Microstructures and Properties of Lath Martensitic Wear-Resistant Steels[J].J IRON STEEL RES INT, 2013, 20(4):70-75
[9]
Y.Zhang,YSun,J.Zhao,S.Guan.Effects of Al on Microstructure and High-Temperature Wear Properties of Austenitic Heat-Resistant Steel[J].J IRON STEEL RES INT, 2012, 19(3):62-66
[10]
G.Liu,JGao,J.Wang,H.Yue.Study on Friction and Wear Properties between Medium Manganese Steel BTW and Hardox500[J].Coal Mine Machinery, 2016, 37(1):69-70
[11]
D.Sui,TWang,L.Zhu,L.Gao,Z.Cui.Mathematical Modeling of High-Temperature Constitutive Equations and Hot Processing Maps for As-Cast SA508-3 Steel[J].JOM, 2016, 68(11):2944-2951
[12]
Y.V.R.K.Prasad, K.P.Rao, S.Sasidhara.Hot Working Guide: Compendium of Processing Maps[M].Compendium of Processing Maps, 2015
[13]
D.He,YLin,M.Chen,J.Chen,D.Wen,X.Chen.Effect of pre-treatment on hot deformation behavior and processing map of an aged nickel-based superalloy[J].J ALLOY COMPD, 2015, 649(10):1075-1084
[14]
D.Xiao,XPeng,X.Liang,Y.Deng,G.Xu,Z.Yin.Study on Hot Workability of Al-5.87Zn-2.07Mg-2.28Cu Alloy Using Processing Map[J].JOM, 2017, 69(4):725-733
[15]
H.Ziegler,DE.Carlson.An Introduction to Thermomechanics[J].Journal of Applied Mechanics, 1978, 45(4):966-966
[16]
M.Masoumi,HL.F.Coelho,S.S.M Tavares,C.CSilva,H.F.G.D.Abreu.Effect of Grain Orientation and Boundary Distributions on Hydrogen-Induced Cracking in Low-Carbon-Content Steels[J].JOM, 2017, 69(8):1368-1374
[17]
F.Montheillet,JL.Coze.Influence of Purity on the Dynamic Recrystallization of Metals and Alloys[J].PHYS STATUS SOLIDI A, 2015, 189(1):51-58
[18]
D.Sui,TWang,L.Zhu,L.Gao,Z.Cui.Mathematical Modeling of High-Temperature Constitutive Equations and Hot Processing Maps for As-Cast SA508-3 Steel[J].JOM, 2016, 68(11):2944-2951
[19]
G.J.Richardson,CM.Sellars,W.J.Mctegart.Recrystallization during creep of nickel[J].ACTA METALL SIN, 1966, 14(10):1225-1236
[20]
T.Seshacharyulu,SC.Medeiros,W.G.Frazier,Y.V.R.K.Hot working of commercial Ti�C6Al�C4V with an equiaxed ���C�� microstructure: materials modeling considerations[J].MAT SCI ENG A-STRUCT, 2000, 284(1-2):184-194
[21]
X.Yang,WLi.Flow Behavior and Processing Maps of a Low-Carbon Steel During Hot Deformation[J].METALL MATER TRANS A, 2015, 46(12):6052-6064
[22]
N.M.Shkatulyak,OM.Tkachuk.A role played by the crystallographic texture in the process of corrosion of hot-rolled rods made of carbon steel[J].Materials Science, 2012, 48(2):153-161
[23]
T.Xi,CYang,M.B.Shahzad,K.Yang.Study of the processing map and hot deformation behavior of a Cu-bearing 317LN austenitic stainless steel[J].Materials Design, 2015, 87(15 December):303-312