A new process for manufacturing organically compounded bentonite was developed successfully based on the organic intercalation and layered structure of bentonite. The main steps in the proposed process included wet sodium activation of bentonite ore, organic compounding and high-pressure roll grinding. The optimum procedure is recommended as follows: 5 mass% of sodium carbonate powder and 30 wt.% water are added to activate the bentonite ore for 24 h to prepare activated bentonite; 0.5 wt.% of organic molecules are added into the activated bentonite for organic compounding for 12 h; then, the high-pressure roll grinding is followed to treat the organically compounded bentonite; and finally, drying and fine grinding are performed for preparing the final organically compounded bentonite product with 10 wt.% moisture and 98% passing 0.074 mm. The obtained organically compounded bentonite was characterized using an X-ray diffractometer, a scanning electron microscope and an X-ray photoelectron spectrometer. To confirm the effect of organically compounded bentonite on green balls, the pelletizing tests were carried out. The results showed that high-pressure roll grinding can not only enhance the ability of the crystal layer to hold the combined water, but also strengthen the intercalation compounding of the organic additive, which is beneficial for the formation of a fiber-interlaced structure of the organically compounded bentonite and improves the quality index of the bentonite itself. Also, the organically compounded bentonite is helpful to improve the indexes of green balls.
A new process for manufacturing organically compounded bentonite was developed successfully based on the organic intercalation and layered structure of bentonite. The main steps in the proposed process included wet sodium activation of bentonite ore, organic compounding and high-pressure roll grinding. The optimum procedure is recommended as follows: 5 mass% of sodium carbonate powder and 30 wt.% water are added to activate the bentonite ore for 24 h to prepare activated bentonite; 0.5 wt.% of organic molecules are added into the activated bentonite for organic compounding for 12 h; then, the high-pressure roll grinding is followed to treat the organically compounded bentonite; and finally, drying and fine grinding are performed for preparing the final organically compounded bentonite product with 10 wt.% moisture and 98% passing 0.074 mm. The obtained organically compounded bentonite was characterized using an X-ray diffractometer, a scanning electron microscope and an X-ray photoelectron spectrometer. To confirm the effect of organically compounded bentonite on green balls, the pelletizing tests were carried out. The results showed that high-pressure roll grinding can not only enhance the ability of the crystal layer to hold the combined water, but also strengthen the intercalation compounding of the organic additive, which is beneficial for the formation of a fiber-interlaced structure of the organically compounded bentonite and improves the quality index of the bentonite itself. Also, the organically compounded bentonite is helpful to improve the indexes of green balls.
Si‑wei Li,Jian Pan,De‑qing Zhu, et al. Synthesis, characterization and properties of organic compound bentonite by molecular intercalation process[J]. Journal of Iron and Steel Research International, 2020, 27(10): 1127-1136.
2020, Vol. 27 