CCT Curves of low carbon Mn-Si steels and development of water cooled bainitic steels |
XU Feng-yun, WANG Yong-wei |
|
|
Abstract CCT curves of Mn-Si steels with different Mn content or carbon content were tested and on this basis, water cooled baintic steels with non-expensive alloy element were developed. The results show that transformation of bainite can be separated from that of ferrite when Mn content approach certain content; relative length of incubation time of ferrite and bainite transformation can be controlled by changing carbon content in Mn-Si; granular bainite was obtained when ��300mm bar cooled by water, mix structure of fine widmanstatten ferrite, granular bainite and martensite was obtained as plate of 40mm thickness cooled by water; water cooled baintic steels developed with non-expensive alloy shows good combination of strength and toughness and tensile strength, yield strength and toughness (AKU -20 oC ) of ��300m bar after water cooled is higher than 850MPa, 620MPa, 65 J respectively, and tensile strength, yield strength and toughness (AKU -20 oC ) of plate of 40mm thickness after water cooled is higher than 1000 MPa, 800MPa, 50 J respectively
|
Received: 01 December 2008
|
Corresponding Authors:
XU Feng-Yun
|
|
|
|
[1] |
Zheng-yan ZHANG,,Qi-long YONG,Xin-jun SUN,Zhao-dong LI,Jun-yu KANG,Guo-dong WANG. Microstructure and Mechanical Properties of Precipitation Strengthened Fire Resistant Steel Containing High Nb and Low Mo[J]. Chinese Journal of Iron and Steel, 2015, 22(4): 337-343. |
[2] |
Lin-na DUAN,,Yu CHEN,Qing-you LIU,Shu-jun JIA,Cheng-chang JIA. Microstructures and Mechanical Properties of X100 Pipeline Steel Strip[J]. Chinese Journal of Iron and Steel, 2014, 21(2): 227-232. |
|
|
|
|