Austenite Grain Growth Behavior of X80 Pipeline Steel in Heating Process |
DUAN Lin-na |
|
|
Abstract Through changing soaking temperature and soaking time, austenite grain growth behavior of X80 pipeline steel under different heating conditions was studied. Relationships of average grain size with soaking temperature and time were obtained respectively. The results show that the prior-austenite grains grow with the increase of soaking temperature and time. When soaking temperature is lower than 1180��, austenite grain size and growth rate are small; when it higher than 1200��, austenite grains grow rapidly and abnormal grain growth appears. Soaking at 1180��, austenite grain growth rate is initially high and then decreases when soaking time exceeds 1h.
|
Received: 17 November 2008
|
|
|
|
[1] |
Jian-guo Chen,Yong-chang Liu,Chen-xi Liu,Bi-yu Yan,Hui-jun Li. Effects of tantalum on austenitic transformation kinetics of RAFM steel[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 705-710. |
[2] |
Hai-feng Xu,,*,Feng Yu,Chang Wang,Wan-li Zhang,Jian Li,Wen-quan Cao. Comparison of microstructure and property of high chromium bearing steel with and without nitrogen addition[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 206-213. |
[3] |
Tao SUN,,Feng YUE,,Hua- jie WU,,Chun GUO,,Ying LI,Zhong- cun MA. Solidification Structure of Continuous Casting Large Round Billets under Mold Electromagnetic Stirring[J]. Chinese Journal of Iron and Steel, 2016, 23(4): 329-337. |
[4] |
Jiao LUO,Ying-gang LIU,Miao-quan LI. Three-dimensional Numerical Simulation and Experimental Analysis of Austenite Grain Growth Behavior in Hot Forging Processes of 300M Steel Large Components[J]. Chinese Journal of Iron and Steel, 2016, 23(10): 1012-1019. |
[5] |
Qi SUN,,Jian WANG,,Hua-bing LI,Yue LI,,Ya-di HU,,Jin-gang BAI,Pei-de HAN,. Chi Phase after Short-term Aging and Corrosion Behavior in 2205 Duplex Stainless Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(10): 1071-1079. |
[6] |
Yan CHONG,,Zheng-dong LIU,Andy GODFREY,Lu WANG,Wei LIU,Yu-qing WENG. Heat Treatment of a Candidate Material for 700 �� A-USC Power Plants[J]. Chinese Journal of Iron and Steel, 2015, 22(2): 150-156. |
|
|
|
|