Behavior of MgO.Al2O3 Based Inclusions in Alloy Steel During Refining Process |
YANG Shu-Feng LI Jing-feng,ZHANG Li-feng, et al |
|
|
Abstract The transformation of MgO8226;Al2O3 based inclusions in alloy steel during refining has been studied by industrial trials. Besides Factsage software is applied to study the formation and modification of spinel inclusions in alloy steel using calcium treatment during refining process. The results show the transformation sequence of inclusions is: MgO8226;Al2O3 �� CaO�CAl2O3�CMgO complex inclusions �� MgO8226;Al2O3; In order to avoid forming MgO61655;Al2O3 inclusions, the content of dissolved Ca in the molten steel has to reach 1ppm.
|
Received: 13 August 2009
|
Corresponding Authors:
YANG Shu-Feng
|
|
|
|
[1] |
Hong-bo Pan,,*,Meng-jiao Zhang,Wei-ming Liu,,Jun Yan,,Hui-ting Wang,Chang-sheng Xie,Zhan Guo. Effects of micro-alloying and production process on precipitation behaviors and mechanical properties of HRB600[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 536-543. |
[2] |
Jin-liang Gao,*,Yan Qi,Ya-qin Li,Hong-wei Shang,Dong-liang Zhao,Yang-huan Zhang. Hydrogen storage thermodynamic and kinetic characteristics of PrMg12-type alloys synthesized by mechanical milling[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 198-205. |
[3] |
Xuan-wei Lei,Ji-hua Huang*,Shu-hai Chen,Xing-ke Zhao. New bainite kinetics of high strength low alloy steel in fast cooling process[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 229-233. |
[4] |
Yin-tao GUO, Qian WANG, Gu-jun CHEN, Sheng-ping HE. Castability of Aluminum- and Sulfur-bearing Free-cutting Steel[J]. Chinese Journal of Iron and Steel, 2015, 22(Supplement 1): 87-92. |
[5] |
Jae-gil JUNG,Seok-jae LEE. Prediction of Nitrogen Diffusivity in ��-ferrite Based on Thermodynamics[J]. Chinese Journal of Iron and Steel, 2015, 22(8): 743-745. |
[6] |
Guo-cheng WANG,,,Sheng-li LI,,Xin-gang AI,,Chong-min ZHANG,,Chao-bin LAI. Characterization and Thermodynamics of Al2O3-MnO-SiO2(-MnS) Inclusion Formation in Carbon Steel Billet[J]. Chinese Journal of Iron and Steel, 2015, 22(7): 566-572. |
|
|
|
|