| Analysis of Thermal Behavior for Beam Blank Continuous Casting Mold |
| XU Hai��lun, WEN Guang��hua, SUN Wei, et al |
|
|
|
|
Abstract Finite element models of steady heat conduction in the meniscus region of beam blank mold were developed by using ABAQUS software. The effect of mold grinding thickness, cooling water velocity, diameter of restrictor rods and water channel design on hot face temperature was analyzed in detail. Attention was focus on the peak temperature and temperature uniformity along hot face. The results showed that the peak temperature of existing mold, about 337.2 oC, is located in the fillet, and two valleys of hot face temperature are found in flange corner and junction of wide face and narrow face, respectively. Decreasing mold thickness, increasing cooling water velocity and increasing diameter of restrictor rods can all reduce peak temperature and improve temperature uniformity along hot race at the expense of lower overall temperature. Redesigning the water channel can decrease peak temperature and thermal gradient of mold without lowering overall temperature of hot face. In particular, the small hole design can improve temperature uniformity across hot face to the best advantage.
|
|
Received: 17 November 2009
|
|
Corresponding Authors:
Hai-lun XU
|
|
|
|
| [1] |
LI Jun��ZHANG Ling-ling��ZHAO Gui-zhou��CANG Da-qiang. Pilot practice of direct modification of molten blast furnace slag and preparation of mineral wool fiber[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 99-103. |
| [2] |
XU Ren-ze��ZHANG Jian-liang��ZHANG He-shun��LIU Chang-jiang�� FAN Xiao-yue��WANG Zhi-yu. Influence of TiO2 on properties of Jingtang blast furnace slag and thermodynamic analysis[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 104-108. |
| [3] |
JIANG Zhou-hua��ZHANG Xin-fa��LIU Fu-bin��GONG Wei. Harmful impurities control of raw material used in Ni-based superalloy production[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 1-10. |
| [4] |
SONG Guang-yi��YANG Quan��WANG Xiao-chen��ZHANG Xi-bang�� WANG Feng-mei��WANG Qiu-na. Work roll wear law for hot strip temper mill[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 54-59. |
| [5] |
WANG Bing-xing��XIONG Lei��ZHANG Tian��WANG Zhao-dong��WANG Guo-dong. Influence on deformation permeability of plate by controlled rolling process with inter-pass water cooling technology[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 60-65. |
| [6] |
YU Hui��ZHAI Jian-wei��ZHANG Chao-fan��LIU Shuai-shuai��LIU Li-gang. Microstructures and properties of nuclear carbon manganese steels P280GH after accelerated aging[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 66-72. |
|
|
|
|
2010, Vol. 17 