Dynamic Soft Reduction Technology for Bloom Casting |
CHEN Yong, et al |
|
|
Abstract The dynamic soft reduction technology for 360mm��450mm bloom casting and its application results at PISCO (Panzhihua Iron & Steel Co.) were presented. In order to analyze the influence of the soft reduction on internal defects of bloom, such as center porosity and central segregation, experiment for contrasting process with or without soft reduction for bloom was investigated. The operation shows that after applying the soft reduction of bloom alloy steel, the ratio of center porosity whose defect level is below 1.0 increased from 66.67% to 85.71%, ratio of central segregation whose defect level is below 1.0 increased from 94.44% to 100%, ratio of central shrinkage cavity which is free increased from 88.89% to 96.42%, and central segregation index of carbon decreased from mean value of 1.15 to 1.05. These results have provided important technology supports for PISCO to optimize the steel product structure, and to improve the production of high quality, property, and value added products.
|
Received: 17 June 2009
|
|
|
|
[1] |
Xuan-wei Lei,Ji-hua Huang*,Shu-hai Chen,Xing-ke Zhao. New bainite kinetics of high strength low alloy steel in fast cooling process[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 229-233. |
[2] |
Gu-jun CHEN,Sheng-ping HE,Yin-tao GUO,Bo-yi SHEN,Shuo ZHAO,Qian WANG. Optimization of Calcium Addition to High-strength Low-alloy Steels[J]. Chinese Journal of Iron and Steel, 2015, 22(7): 590-597. |
[3] |
A-rong,Lin ZHAO,Chuan PAN,Zhi-ling TIAN. Influence of Ti on Weld Microstructure and Mechanical Properties in Large Heat Input Welding of High Strength Low Alloy Steels[J]. Chinese Journal of Iron and Steel, 2015, 22(5): 431-437. |
[4] |
Han YANG,Xi-xia WANG,Jin-bo QU. Effect of Boron on CGHAZ Microstructure and Toughness of High Strength Low Alloy Steels[J]. Chinese Journal of Iron and Steel, 2014, 21(8): 787-792. |
[5] |
Hui-bin WU,Jin-ming LIANG,Di TANG,Xiao-tong LIU,Peng-cheng ZHANG,Yuan-jie YUE. Influence of Inclusion on Corrosion Behavior of E36 Grade Low-alloy Steel in Cargo Oil Tank Bottom Plate Environment[J]. Chinese Journal of Iron and Steel, 2014, 21(11): 1016-1021. |
[6] |
G Subhash Chander,G Madhusudhan Reddy,A Venugopal Rao. Influence of Rotational Speed on Microstructure and Mechanical Properties of Dissimilar Metal AISI 304-AISI 4140 Continuous Drive Friction Welds[J]. Chinese Journal of Iron and Steel, 2012, 19(10): 64-73. |
|
|
|
|