Effect of Prestrain on Microstructures and Properties of Si-Al-Mn TRIP Steel Sheet with Niobium |
TANG Zheng-you |
|
|
Abstract Paint baking treatment was carried out in a silicon oil bath at 170�� for 20 min for Si-Al-Mn TRIP Steel sheet with different pre-strains, effect of pre-strain on microstructures and properties was studied before and after baking. The results is shown that with the increasing of pre-strain amount during pre-straining and baking, the volume fraction of retained austenite decreases, the volume fraction of martensite and bainite increases, as well as yield strength enhances; as pre-strain ranges from 0 to 4%, the bake-hardening(BH) value increases; while from 4 to 16%, the BH value decreases; when the pre-strain amount is 4%, the highest BH value is about 70MPa in Si-Al-Mn TRIP Steel sheet with niobium, which displays excellent bake-hardening behavior.
|
Received: 06 January 2009
|
Corresponding Authors:
Zheng-you TANG
|
|
|
|
[1] |
Xiao-li Zhao,,Yong-jian Zhang,Cheng-wei Shao,Wei-jun Hui,Han Dong. Thermal stability of retained austenite and mechanical properties of medium-Mn steel during tempering treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 830-837. |
[2] |
Hui Guo,Peng Zhou,*,Ai-min Zhao,,Chao Zhi,Ran Ding,Jia-xing Wang. Effects of Mn and Cr contents on microstructures and mechanical properties of low temperature bainitic steel[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 290-295. |
[3] |
Ji-bo Peng,,Hu Jiang,,Gong-ting Zhang,Li-ben Chen,,Na-qiong Zhu,,Yan-lin He,,*, Xiao-gang Lu,,Lin Li,. In-situ analysis of retained austenite transformation in high-performance micro-alloyed TRIP steel[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 313-320. |
[4] |
Shi-meng ZHOU,,Xing-wang CHENG,,You-jing ZHANG,,Meng WANG,,Wen JIANG,,Hong-nian CAI,. Factors Affecting the Mechanical Properties of Ultra-high-strength Bainitic Steel Containing W and 0.33 mass% C[J]. Chinese Journal of Iron and Steel, 2016, 23(3): 289-296. |
[5] |
Cun-yu WANG,,Ying CHANG,Jie YANG,Wen-quan CAO,Han DONG,Yi-de WANG. Work Hardening Behavior and Stability of Retained Austenite for Quenched and Partitioned Steels[J]. Chinese Journal of Iron and Steel, 2016, 23(2): 130-137. |
[6] |
De-chao XU,Yan-dong LIU,Jun LI,,Qing-ge MENG,Pei LI. Microstructure Characterization and Mechanical Properties of TRIP-aided Steel under Rapid Heating for Different Holding Time[J]. Chinese Journal of Iron and Steel, 2016, 23(2): 138-144. |
|
|
|
|