| Effect of Thermomechanical Processing on Mechanical Properties of Hot Rolled Multiphase Steel |
| LI Zhuang1,2,WU Di2,L�� Hui��sheng3 |
| 1. Department of Material Engineering, Shenyang Institute of Aeronautical Engineering, Shenyang 110034, Liaoning, China;2. State Key Lab of Rolling and Automation, Northeastern University, Shenyang 110004, Liaoning, China;3. Department of Science and Technology Information, China Iron and Steel Research Institute Group, Beijing 100081, China |
|
|
|
|
Abstract The effect of thermomechanical processing (TMP) on the mechanical properties of hot rolled multiphase steel was investigated. TMP was conducted using a laboratory hot rolling mill, in which three different kinds of finish rolling deformation degrees and temperatures were applied. The results indicate that polygonal ferrite, granular bainite, and a considerable amount of stabilized retained austenite can be obtained by TMP. The stability of the retained austenite increases with decreasing finish rolling temperature and increasing finish rolling deformation degrees. Ultimate tensile strength (��b), total elongation (��), and the product of ultimate tensile strength by total elongation (��b����) for 50% reduction at finish rolling temperature of 700 �� reach maximum values [791 MPa, 36% and 28 476 (MPa��%), respectively].
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
Xiao-li Zhao,,Yong-jian Zhang,Cheng-wei Shao,Wei-jun Hui,Han Dong. Thermal stability of retained austenite and mechanical properties of medium-Mn steel during tempering treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 830-837. |
| [2] |
Hong-ru Ren,Jin-tao Gao,Zhe Wang,Chong Li,Fu-qiang Wang,Zhan-cheng Guo. Evolution of microstructure, mechanical and magnetic properties of electrodeposited 50%Ni-Fe alloy foil after thermal treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 844-851. |
| [3] |
Reng-chong Xu,,Yan-lin He,,Hu Jiang,,Hua Wang,,Na-qiong Zhu,,Xiao-gang Lu,, Lin Li,. Microstructures and mechanical properties of ferrite-based lightweight steel with different compositions[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 737-742. |
| [4] |
Yong-xing Jiao,Jian-sheng Liu*,Xing-wang Duan,Xiao-hua Zheng,Wen-wu He. Prediction of critical forging penetration efficiency for 06Cr19Ni9NbN steel by dynamic recrystallization[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 649-653. |
| [5] |
Ming-bo Zhou,Jing-lin Tang,*,Jie Yang,Cun-yu Wang. Tailored properties of a novelly-designed press-hardened 22MnMoB steel[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 508-512. |
| [6] |
Zhong-liang Tian,,Sen-bao Jiang,Zheng-zong Chen,Han-sheng Bao,Zheng-dong Liu,*. Microstructural evolution and mechanical properties of a new Ni-based heat-resistant alloy during aging at 750��C[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 513-519. |
|
|
|
|
2008, Vol. 15 